P. Pichler

Defect initiation and accumulation kinetics in hard-coated WC-Co hardmetal under multi-axial loads at elevated temperature in a novel ball-in-cone test setup

C. Czettl, R. Ebner, T. Klünsner, 2022, International Journal of Refractory Metals and Hard Materials.

A physical reason for asymmetric creep deformation behaviour of WC-Co hardmetal under tension and compression loading at 700 °C and 800 °C

S. Marsoner, C. Czettl, R. Ebner, 2021 .

Creep behaviour of WC-12 wt% Co hardmetals with different WC grain sizes tested in uniaxial tensile and compression step-loading tests at 700 °C and 800 °C

S. Marsoner, C. Czettl, R. Ebner, 2021 .

Damage indicators for early fatigue damage assessment in WC-Co hardmetals under uniaxial cyclic loads at a stress ratio of R = −1 at elevated temperatures

S. Marsoner, C. Czettl, R. Ebner, 2021, International Journal of Refractory Metals and Hard Materials.

Evaluation of wood material models for the numerical assessment of cutting forces in chipping processes

M. Leitner, F. Grün, P. Pichler, 2017, Wood Science and Technology.

Strain ratcheting limit stresses as a function of microstructure of WC-Co hardmetals under uniaxial cyclic loads under a stress ratio of R = −∞ at elevated temperatures

S. Marsoner, C. Czettl, R. Ebner, 2022, International Journal of Refractory Metals and Hard Materials.

On the transition of failure control from material-intrinsic defects to defects forming during monotonically increasing and cyclic mechanical loading in WC-Co hard metal at elevated temperature

R. Pippan, S. Marsoner, C. Czettl, 2022, Acta Materialia.

Wear and fatigue resistance of mild steel components reinforced by arc welded hard layers

Martin Leitner, Philip Pichler, Florian Steinwender, 2017 .

Evaluation of wood material models for the numerical assessment of cutting forces in chipping processes

M. Leitner, F. Grün, P. Pichler, 2017, Wood Science and Technology.