Spark Plasma Sintering of Alumina

A systematic study of various spark plasma sintering (SPS) parameters, namely temperature, holding time, heating rate, pressure, and pulse sequence, was conducted to investigate their effect on the densification, grain-growth kinetics, hardness, and fracture toughness of a commercially available submicrometer-sized Al 2 O 3 powder. The obtained experimental data clearly show that the SPS process enhances both densification and grain growth. Thus, Al 2 O 3 could be fully densified at a much lower temperature (1150°C), within a much shorter time (minutes), than in more conventional sintering processes. It is suggested that the densification is enhanced in the initial part of the sintering cycle by a local spark-discharge process in the vicinity of contacting particles, and that both grain-boundary diffusion and grain-boundary migration are enhanced by the electrical field originating from the pulsed direct current used for heating the sample. Both the diffusion and the migration that promote the grain growth were found to be strongly dependent on temperature, implying that it is possible to retain the original fine-grained structure in fully densified bodies by avoiding a too high sintering temperature. Hardness values in the range 21-22 GPa and fracture toughness values of 3.5 ± 0.5 MPa.m 1/2 were found for the compacts containing submicrometer-sized Al 2 O 3 grains.

[1]  A. Krell.  Load dependence of hardness in sintered submicrometer Al2O3 and ZrO2 , 1995 .

[2]  Brian R. Lawn,et al.  A Critical Evaluation of Indentation Techniques for Measuring Fracture Toughness: I , 1981 .

[3]  Andreas Krell,et al.  Grain Size Dependence of Hardness in Dense Submicrometer Alumina , 1995 .

[4]  F. Castro,et al.  Sinter-HIP of α-alumina powders with sub-micron grain sizes , 2002 .

[5]  T. Hirai,et al.  Densification of Al_2O_3 powder using spark plasma sintering , 2000 .

[6]  A. Krell.  Improved hardness and hierarchic influences on wear in submicron sintered alumina , 1996 .

[7]  T. Ohji,et al.  Strengthening of Porous Alumina by Pulse Electric Current Sintering and Nanocomposite Processing , 2004 .

[8]  Mel I. Mendelson,et al.  Average Grain Size in Polycrystalline Ceramics , 1969 .

[9]  A. Mukherjee,et al.  Electric pulse assisted rapid consolidation of ultrafine grained alumina matrix composites , 2000 .

[10]  Andreas Krell,et al.  The Influence of shaping method on the grain size dependence of strength in dense submicrometre alumina , 1996 .

[11]  Moon J. Kim,et al.  Retention of nanostructure in aluminum oxide by very rapid sintering at 1150 °C , 1995 .

[12]  Zeming He,et al.  Grain-growth rate constant of hot-pressed alumina ceramics , 2000 .

[13]  G. Messing,et al.  Enhanced Densification of Boehrmte Sol-Gels by α-Alumina Seeding , 1984 .

[14]  Y. Makino,et al.  Effect of Spark Plasma Sintering on Densification, Mechanichal Properties and Micro-structure of Alumina Ceramics , 1999 .

[15]  M. Sacks,et al.  Low‐Temperature Sintering of Aluminum Oxide , 1988 .

[16]  L. C. Jonghe,et al.  Initial Coarsening and Microstructural Evolution of Fast‐Fired and MgO‐Doped Al2O3 , 1997 .

[17]  F. Lange,et al.  Powder Processing Science and Technology for Increased Reliability , 1989 .

[18]  Lei Gao,et al.  Bending strength and microstructure of Al2O3 ceramics densified by spark plasma sintering , 2000 .

[19]  S. Risbud,et al.  Influence of initial crystal structure and electrical pulsing on densification of nanocrystalline alumina powder , 1998 .

[20]  M. Nygren,et al.  Superfast Densification of Oxide/Oxide Ceramic Composites , 1999 .

[21]  M. Tokita.  Trends in Advanced SPS Spark Plasma Sintering Systems and Technology , 1993 .