Fabrication of Cu2SnS3 solar cells by screen-printing and high-pressure sintering process

Cu-poor Cu2−xSnS3 (CTS) powders with x = 0.0–0.3 prepared by mixing the elemental powders and post-heating at 600 °C in N2 gas were analyzed by X-ray diffraction and ultraviolet–visible–near-infrared (UV–vis–NIR) spectroscopy. The area of the solid solution region in the Cu-poor side of CTS was quite small in the Cu2S–SnS2 pseudo-binary system. We deposited CTS films by a screen printing and high-pressure sintering (PHS) process and post-annealing at 575 °C for 10 min under a 1% H2S/N2 gas atmosphere. The solar cells were fabricated with a device structure of Ag/indium tin oxide (ITO)/i-ZnO/CdS/Cu2SnS3 (CTS)/Mo/soda-lime glass. The CTS solar cell with x = 0.1 showed maximum efficiency of 1.03%. Then, we prepared Cu1.9SnS3 powders by mixing the elemental powders and post-heating at various temperatures. The CTS solar cell with Cu1.9SnS3 powder prepared by post-heating at 300 °C showed an efficiency of 1.38% with Voc of 182 mV, Jsc of 21.7 mA/cm2, and FF of 0.350.

[1]  Kentaro Ito,et al.  Electrical and Optical Properties of Stannite-Type Quaternary Semiconductor Thin Films , 1988 .

[2]  T. Wada,et al.  Crystal structures and band-gap energies of Cu2Sn(S,Se)3 (0≤ x ≤1.0) solid solution , 2013 .

[3]  Tayfun Gokmen,et al.  Beyond 11% Efficiency: Characteristics of State‐of‐the‐Art Cu2ZnSn(S,Se)4 Solar Cells , 2013 .

[4]  P. K. Nair,et al.  Cu2SnS3 and Cu4SnS4 Thin Films via Chemical Deposition for Photovoltaic Application , 2010 .

[5]  S. Zhuang,et al.  Study and enhance the photovoltaic properties of narrow-bandgap Cu2SnS3 solar cell by p-n junction interface modification. , 2012, Journal of colloid and interface science.

[6]  S. Tajima,et al.  6% Efficiency Cu2ZnSnS4-based thin film solar cells using oxide precursors by open atmosphere type CVD , 2012 .

[7]  A. Pérez‐Rodríguez,et al.  Raman analysis of monoclinic Cu2SnS3 thin films , 2012 .

[8]  Photovoltaic characteristics of thin films of Cu2SnS3 , 1987 .

[9]  F. Gao,et al.  Structural and Optical Properties of In-Free Cu2ZnSn(S,Se)4 Solar Cell Materials , 2012 .

[10]  H. Katagiri,et al.  Fabrication of Cu2SnS3 thin films by sulfurization of evaporated Cu‐Sn precursors for solar cells , 2013 .

[11]  S. Eguchi,et al.  Preparation of Cu$_{2}$SnS$_{3}$ Thin Films by Sulfurization of Cu/Sn Stacked Precursors , 2012 .

[12]  David B Mitzi,et al.  High‐Efficiency Solar Cell with Earth‐Abundant Liquid‐Processed Absorber , 2010, Advanced materials.

[13]  H. Katagiri,et al.  Cu$_{2}$SnS$_{3}$ Thin-Film Solar Cells from Electroplated Precursors , 2012 .

[14]  A. D. Cunha,et al.  A study of ternary Cu2SnS3 and Cu3SnS4 thin films prepared by sulfurizing stacked metal precursors , 2010 .

[15]  D. Mitzi,et al.  Thermally evaporated Cu2ZnSnS4 solar cells , 2010 .

[16]  G. Schmidt,et al.  Phase relations and optical properties of semiconducting ternary sulfides in the system Cu–Sn–S , 2003 .

[17]  K. Boubaker,et al.  A new procedure to prepare semiconducting ternary compounds from binary buffer materials and vacuum-deposited copper for photovoltaic applications , 2010 .

[18]  M. Umehara,et al.  Cu2Sn1-xGexS3 (x = 0.17) Thin-Film Solar Cells with High Conversion Efficiency of 6.0% , 2013 .

[19]  T. Wada,et al.  A structural study of Cu–In–Se compounds by x-ray absorption fine structure , 2011 .

[20]  M. Amlouk,et al.  Structural and optical properties of Cu 2SnS 3 sprayed thin films , 2009 .

[21]  Tayfun Gokmen,et al.  Device characteristics of a 10.1% hydrazine‐processed Cu2ZnSn(Se,S)4 solar cell , 2012 .

[22]  S. Tajima,et al.  Enhancement of Conversion Efficiency of Cu2ZnSnS4 Thin Film Solar Cells by Improvement of Sulfurization Conditions , 2013 .

[23]  T. Minemoto,et al.  Sputtered (Zn,Mg)O buffer layer for band offset control in Cu2ZnSn(S,Se)4 solar cells , 2014 .

[24]  Tadashi Ito,et al.  Enhanced Conversion Efficiencies of Cu2ZnSnS4-Based Thin Film Solar Cells by Using Preferential Etching Technique , 2008 .

[25]  G. Zoppi,et al.  Thin film solar cells based on the ternary compound Cu2SnS3 , 2012 .