Spinodal decomposition of a nickel-titanium alloy

The decomposition of a supersaturated nickel-14% titanium solid solution has been investigated by field-ion microscopy. It was established that the formation of ordered γ′ (Ni3Ti) precipitates proceeded via a spinodal mechanism and that no distinct precipitate (e.g. Ni6Ti) was involved. The diffuse nature of the interface between ordered and disordered regions was clearly illustrated by a new technique for determining composition fluctuations over short distances. Considerable sharpening of the interface occurred on isothermal ageing. The spinodal temperature was estimated to be (880 ± 70) °C for this composition and a value of (0.6 ± 0.1) nm was obtained for the interaction parameter, Ψ. Im Feldionenmikroskop wird die Zersetzung einer ubersattigten Nickel-14%Titan-Legierung untersucht. Es wird gezeigt, das die Bildung von geordneten γ′ (Ni3 Ti)-Prezipitaten uber einen spinodalen Mechanismus vor sich geht und das keine davon verschiedenen Prezipitate (z. B. Ni6Ti) beteiligt sind. Die diffuse Natur der Grenzflache zwischen geordneten und ungeordneten Bereichen wird durch eine neue Technik zur Bestimmung der Fluktuationen der Zusammensetzung uber kurze Entfernungen klar illustriert. Eine betrachtliche Verscharfung der Grenzflache tritt nach isothermer Alterung auf. Die Spinodal-temperatur wird zu (880 ± 70) °C fur diese Zusammensetzung berechnet und es wird ein Wert von (0,6 ± 0,1) nm fur den Wechselwirkungsparameter Ψ erhalten.

[1]  R. Sinclair,et al.  On the determination of a local order parameter in a nickel-titanium alloy , 1973 .

[2]  T. Page,et al.  Field‐ion microscopy of interphase interfaces , 1973 .

[3]  R. Faulkner,et al.  Field-ion microscopy of the early stages of γ' precipitation in a nickel-aluminium alloy , 1972 .

[4]  B. Loberg.  Inelastic changes in specimens during operation of the field-ion microscope , 1971 .

[5]  B. Ralph,et al.  A versatile field‐ion microscope for metallographic studies , 1970 .

[6]  A. Ardell.  The growth of gamma prime precipitates in aged Ni−Ti alloys , 1970 .

[7]  B. Ralph,et al.  A field-ion study of carbide particle coarsening in an alloy steel , 1969 .

[8]  A. Ardell,et al.  On the modulated structure of aged Ni-Al alloys: with an Appendix On the elastic interaction between inclusions by J. D. Eshelby , 1966 .

[9]  M. Fine,et al.  Magnetic study of deformation in an age hardened Ni-Ti alloy☆ , 1964 .

[10]  M. Fine,et al.  Precipitation studies in Ni-10 at.% Ti☆ , 1963 .

[11]  John W. Cahn,et al.  On spinodal decomposition in cubic crystals , 1962 .

[12]  I. Lifshitz,et al.  The kinetics of precipitation from supersaturated solid solutions , 1961 .

[13]  J. Manenc,et al.  Quelques aspects de la précipitation dans un alliage nickel-titane , 1959 .

[14]  L. Goddard,et al.  Electron ray tracing through magnetic lenses , 1944 .

[15]  A. Ardell,et al.  The effect of volume fraction on particle coarsening: theoretical considerations , 1972 .

[16]  Kazuo Saito,et al.  Precipitation in Ni-12 at. % Ti Alloy , 1969 .

[17]  John W. Cahn,et al.  Phase Separation by Spinodal Decomposition in Isotropic Systems , 1965 .