An investigation to revitalize the separation performance of hollow fibers with a thin mixed matrix composite skin for gas separation

Hollow fibers with a thin zeolite beta-polysulfone mixed matrix selective layer and enhanced selectivity for He/N2 and O2/N2 separation have been developed in this study. It is believed that the heat treatment and the coating processes combine to bring out the separation properties of zeolite beta imbedded in the polymer matrix. The fibers were initially formed by using the dual-layer co-extrusion and dry-jet wet/wet spinning technology. Owing to the loose nature of the mixed matrix skin, the as-spun fibers show Knudsen diffusion even after silicone rubber coating. The effectiveness of heat treatment and surface coating in healing the hollow fiber has been investigated. SEM pictures show that heat treatment at above Tg can significantly densify the loose mixed matrix layer and produce hollow fibers with a thin mixed matrix selective layer of around 1.5–12m. However, heat treatment at above Tg does not necessarily produce defect-free hollow fiber membranes. Three types of silicone rubber coatings were applied and compared. It is found that, after a two-step coating, the ideal selectivity of mixed matrix fibers increases to surpass that of hollow fiber with a neat polysulfone outer layer. The sealing of the mixed matrix outer layer instead of the caulking of the inner layer is confirmed to be the cause for the selectivity increment. The reaction between the two chemicals in the two-step coating is contributive to the efficiency of this coating method. In addition, it is also observed that the thickness of the mixed matrix composite outer layer influences permeance and selectivity. The activation energies (Ep) for O2 and N2 calculated from the permeance or permeability at different temperatures indicate that the addition of zeolite beta in the polysulfone has reduced the energy barrier for O2 permeation. © 2005 Elsevier B.V. All rights reserved.

[1]  R. Mahajan,et al.  Challenges in forming successful mixed matrix membranes with rigid polymeric materials , 2002 .

[2]  William J. Koros,et al.  Tailoring mixed matrix composite membranes for gas separations , 1997 .

[3]  Tai‐Shung Chung,et al.  Formation of ultrathin high-performance polyethersulfone hollow-fiber membranes , 1997 .

[4]  L. Robeson,et al.  Correlation of separation factor versus permeability for polymeric membranes , 1991 .

[5]  Zhen Huang,et al.  Fundamental understanding of nano-sized zeolite distribution in the formation of the mixed matrix single- and dual-layer asymmetric hollow fiber membranes , 2005 .

[6]  Huanting Wang,et al.  Homogeneous polymer–zeolite nanocomposite membranes by incorporating dispersible template-removed zeolite nanocrystals , 2002 .

[7]  William J. Koros,et al.  High Pressure CO2/CH4 Separation Using Carbon Molecular Sieve Hollow Fiber Membranes , 2002 .

[8]  Tai‐Shung Chung,et al.  Fabrication and characterization of BTDA-TDI/MDI (P84) co-polyimide membranes for the pervaporation dehydration of isopropanol , 2005 .

[9]  Dongfei Li,et al.  Fabrication of fluoropolyimide/polyethersulfone (PES) dual-layer asymmetric hollow fiber membranes for gas separation , 2002 .

[10]  Xudong Hu,et al.  Effect of Air-Gap Distance on the Morphology and Thermal Properties of Polyethersulfone Hollow Fibers , 1997 .

[11]  Rajiv Mahajan,et al.  Mixed matrix membrane materials with glassy polymers. Part 2 , 2002 .

[12]  Takeshi Matsuura,et al.  Reverse osmosis and ultrafiltration , 1985 .

[13]  Y. Kang,et al.  Zeolite-filled polyimide membrane containing 2,4,6-triaminopyrimidine , 2001 .

[14]  C. A. Smolders,et al.  Preparation of zeolite filled glassy polymer membranes , 1994 .

[15]  S. Kulprathipanja,et al.  The effects of polymer chain rigidification, zeolite pore size and pore blockage on polyethersulfone (PES)-zeolite A mixed matrix membranes , 2005 .

[16]  Stephen J. Miller,et al.  Mixed matrix membranes using carbon molecular sieves: II. Modeling permeation behavior , 2003 .

[17]  C. A. Smolders,et al.  Adsorbent filled membranes for gas separation. Part 1. Improvement of the gas separation properties of polymeric membranes by incorporation of microporous adsorbents , 1993 .

[18]  R. Behling,et al.  Preparation and characterization of thin-film zeolite–PDMS composite membranes☆ , 1992 .

[19]  W. Guo,et al.  Study and characterization of the hysteresis behavior of polyimide membranes in the thermal cycle process of pervaporation separation , 2005 .

[20]  I. Pinnau,et al.  Surface fluorination of polysulfone asymmetric membranes and films , 1991 .

[21]  Chun Cao,et al.  Fabrication of Matrimid/polyethersulfone dual-layer hollow fiber membranes for gas separation , 2004 .

[22]  T. M. Gür.  Permselectivity of zeolite filled polysulfone gas separation membranes , 1994 .

[23]  W. Koros,et al.  Gas transport properties of biphenol polysulfones , 1992 .

[24]  Stephen J. Miller,et al.  Effect of condensable impurity in CO2/CH4 gas feeds on performance of mixed matrix membranes using carbon molecular sieves , 2003 .

[25]  I. Pinnau,et al.  Relationship between substructure resistance and gas separation properties of defect-free integrally skinned asymmetric membranes , 1991 .

[26]  I. Vankelecom,et al.  Silylation To Improve Incorporation of Zeolites in Polyimide Films , 1996 .

[27]  M. Tsapatsis,et al.  Preparation and characterization of a glassy fluorinated polyimide zeolite-mixed matrix membrane , 2002 .

[28]  L. Yılmaz,et al.  Gas permeation characteristics of polymer-zeolite mixed matrix membranes , 1994 .

[29]  W. Koros,et al.  Morphology of integral-skin layers in hollow-fiber gas-separation membranes , 2003 .

[30]  W. Koros,et al.  Aqueous quenched asymmetric polysulfone hollow fibers prepared by dry/wet phase separation , 1994 .

[31]  J. Qin,et al.  Investigation of shear stress effect within a spinneret on flux, separation and thermomechanical properties of hollow fiber ultrafiltration membranes , 2000 .

[32]  T. Chung.  Calculation of the intrusion depth and its effects on microporous composite membranes , 1997 .

[33]  William J. Koros,et al.  Mixed matrix membranes using carbon molecular sieves: I. Preparation and experimental results , 2003 .

[34]  Tai‐Shung Chung,et al.  Development of asymmetric 6FDA-2,6DAT hollow fiber membranes for CO2/CH4 separation. Part 2. Suppression of plasticization , 2003 .

[35]  G. Sakellaropoulos,et al.  Gas permeation through PSF-PI miscible blend membranes , 1996 .

[36]  Tai‐Shung Chung,et al.  Fabrication of dual-layer polyethersulfone (PES) hollow fiber membranes with an ultrathin dense-selective layer for gas separation , 2004 .

[37]  Tai‐Shung Chung,et al.  Characterization of permeability and sorption in Matrimid/C60 mixed matrix membranes , 2003 .

[38]  Tai‐Shung Chung,et al.  The effect of shear rates on gas separation performance of 6FDA-durene polyimide hollow fibers , 2000 .

[39]  Rajiv Mahajan,et al.  Mixed matrix membrane materials with glassy polymers. Part 1 , 2002 .

[40]  D. Kemp,et al.  The diffusion time lag in polymer membranes containing adsorptive fillers , 2007 .

[41]  I. Vankelecom,et al.  INCORPORATION OF ZEOLITES IN POLYIMIDE MEMBRANES , 1995 .

[42]  Tai‐Shung Chung,et al.  Chemical Cross-Linking Modification of Polyimide/Poly(ether sulfone) Dual-Layer Hollow-Fiber Membranes for Gas Separation , 2003 .

[43]  Tai‐Shung Chung,et al.  A Review of Microporous Composite Polymeric Membrane Technology for Air-Separation , 1996, Engineering Plastics.

[44]  Dongfei Li,et al.  Morphological aspects and structure control of dual-layer asymmetric hollow fiber membranes formed by a simultaneous co-extrusion approach , 2004 .