Mitigation of autogenous shrinkage in alkali activated slag mortars by internal curing

Alkali activated slag shows considerable promise as an environmentally friendly alternative to binders produced from ordinary portland cement. The shrinkage behavior of alkali activated slags, however, is not well understood, and is a hurdle to widespread adoption. The use of pre-wetted lightweight aggregate-based internal curing to mitigate shrinkage in slags activated by Na2CO3 solution or waterglass/NaOH solution has been investigated. Chemical shrinkage measurements were used to determine the amount of additional curing water needed by the mixtures, and autogenous and total shrinkage measurements used to determine the effects of internal curing on the overall shrinkage of the systems. Internal curing can completely mitigate autogenous shrinkage; however, in the systems examined here, drying shrinkage was the dominant shrinkage factor. In such a case, the benefits of internal curing are most clearly observed during the first 7 days.

[1]  N. Roussel,et al.  An environmental evaluation of geopolymer based concrete production: reviewing current research trends , 2011 .

[2]  E. Gartner.  Industrially interesting approaches to “low-CO2” cements ☆ , 2004 .

[3]  Hamlin M. Jennings,et al.  Density and water content of nanoscale solid C–S–H formed in alkali-activated slag (AAS) paste and implications for chemical shrinkage , 2012 .

[4]  Michael Golias,et al.  Absorption and desorption properties of fine lightweight aggregate for application to internally cured concrete mixtures , 2011 .

[5]  J. Deventer,et al.  The Role of Inorganic Polymer Technology in the Development of ‘Green Concrete’ , 2007 .

[6]  Mehmet Ali Tasdemir,et al.  Effects of distribution of lightweight aggregates on internal curing of concrete , 2010 .

[7]  J. Deventer,et al.  Geopolymer technology: the current state of the art , 2007 .

[8]  A. Atkinson,et al.  Sodium silicate-based, alkali-activated slag mortars: Part I. Strength, hydration and microstructure , 2002 .

[9]  Jeffrey J. Thomas,et al.  Influence of nucleation seeding on the hydration kinetics and compressive strength of alkali activated slag paste , 2011 .

[10]  John L. Provis,et al.  The mechanism of geopolymer gel formation investigated through seeded nucleation , 2008 .

[11]  Alfred Wisser,et al.  MATERIALS AND STRUCTURES , 2015 .

[12]  D. Bentz,et al.  Standard Test Method for Autogenous Strain of Cement Paste and Mortar , 2007 .

[13]  J. Phair.  Green chemistry for sustainable cement production and use , 2006 .

[14]  R. Cloots,et al.  (Micro)-structural comparison between geopolymers, alkali-activated slag cement and Portland cement , 2006 .

[15]  L. Price,et al.  CARBON DIOXIDE EMISSIONS FROM THE GLOBAL CEMENT INDUSTRY , 2001 .

[16]  J. Ideker,et al.  Advances in alternative cementitious binders , 2011 .

[17]  Ernst Worrell,et al.  Emission Reduction of Greenhouse Gases from the Cement Industry , 2003 .

[18]  Edward J. Garboczi,et al.  Estimation of the degree of hydration of blended cement pastes by a scanning electron microscope point-counting procedure , 2004 .

[19]  Abraham S. Grader,et al.  Water Movement During Internal Curing: Direct Observation Using X-Ray Microtomography , 2006 .

[20]  Pietro Lura,et al.  Mixture Proportioning for Internal Curing , 2005 .

[21]  William L. George,et al.  A parallel reaction-transport model applied to cement hydration and microstructure development , 2010 .

[22]  O. Jensen,et al.  Water-entrained cement-based materials: II. Experimental observations , 2002 .

[23]  M. Barsoum,et al.  Chemical and Microstructural Characterization of 20‐Month‐Old Alkali‐Activated Slag Cements , 2010 .

[24]  B. Lothenbach,et al.  Hydration of calcium sulfoaluminate cements — Experimental findings and thermodynamic modelling , 2010 .

[25]  C. Shi,et al.  Alkali-Activated Cements and Concretes , 2003 .

[26]  Jay G. Sanjayan,et al.  Resistance of alkali-activated slag concrete to alkali–aggregate reaction , 2001 .

[27]  J. Sykes,et al.  Sodium silicate-based alkali-activated slag mortars: Part II. The retarding effect of additions of sodium chloride or malic acid , 2000 .

[28]  Francisca Puertas,et al.  Effect of Shrinkage-reducing Admixtures on the Properties of Alkali-activated Slag Mortars and Pastes , 2007 .

[29]  John L. Provis,et al.  The role of particle technology in developing sustainable construction materials , 2010 .

[30]  Aaron R. Sakulich,et al.  Reinforced geopolymer composites for enhanced material greenness and durability , 2011 .

[31]  P. Banfill,et al.  Alkali activated fly ash: effect of admixtures on paste rheology , 2009 .

[32]  Miguel Angel Sanjuán,et al.  Standardization for an innovative world , 2011 .

[33]  John L. Provis,et al.  LOW CO 2 CONCRETE: ARE WE MAKING ANY PROGRESS? , 2008 .

[34]  S. Erdoğan,et al.  Alkali activation of a slag at ambient and elevated temperatures , 2012 .

[35]  Wellington Longuini Repette,et al.  Drying and autogenous shrinkage of pastes and mortars with activated slag cement , 2008 .

[36]  Caijun Shi,et al.  A calorimetric study of early hydration of alkali-slag cements , 1995 .

[37]  D. Bentz,et al.  Protected paste volume in concrete: Extension to internal curing using saturated lightweight fine aggregate , 1999 .

[38]  Hua Xu,et al.  Characterization of Aged Slag Concretes , 2008 .

[39]  Anders Kaestner,et al.  Release of internal curing water from lightweight aggregates in cement paste investigated by neutron and X-ray tomography , 2011 .

[40]  Jay G. Sanjayan,et al.  Resistance of alkali-activated slag concrete to acid attack , 2003 .

[41]  D. Bentz,et al.  Influence of Exposure Conditions on the Efficiency of Internal Curing in Concrete , 2013 .

[42]  Aaron R. Sakulich,et al.  Mechanical and microstructural characterization of an alkali-activated slag/limestone fine aggregate concrete , 2009 .