On the bulk β-Ga2O3 single crystals grown by the Czochralski method

Abstract The growth of bulkx β-Ga 2 O 3 single crystals by the Czochralski method is reported and discussed in terms of crucial growth conditions and correlated with basic electrical and optical properties of the obtained crystals. β-Ga 2 O 3 crystals have a tendency to a spiral formation due to free carrier absorption in the near infrared (NIR) wavelength range, which hampers radiative heat transfer through the growing crystal. Moderate or low free electron concentrations ( 17  cm −3 ) lead to cylindrical crystals with a high crystallized fraction ( g ≥0.5). The use of a CO 2 -containing growth atmosphere provides oxygen partial pressures between 0.8 and 4.4×10 −2  bar that is sufficient to obtain cylindrical and semiconducting crystals. Doping with Sn increases the free electron concentration in the crystals to high values (~10 19  cm −3 ) that lead to an immediate spiral formation, while doping with Mg (>6 wt ppm) provides insulating crystals with reduced probability of the spiral formation. The estimated Mg equilibrium segregation coefficient across the liquid–solid interface is 0.10–0.12. Annealing of undoped crystals in an oxidizing atmosphere at temperatures ≥1200 °C for 20 h decreases the bulk free electron concentration by about one order of magnitude, while the crystal surface becomes insulating. However, Mg:β-Ga 2 O 3 crystals are insensitive to annealing in both oxygen- and hydrogen-containing atmospheres. The transmittance spectra showed a steep absorption edge at 260 nm and virtually full transparency in the visible and NIR wavelength range for low and moderate free electron concentrations. We also demonstrated the possibility of growing 2 in. diameter β-Ga 2 O 3 single crystals by the Czochralski method. The good crystal quality is evidenced by rocking curve FWHM values of below 50". We noted that most dislocations propagate parallel to (100) plane. Further, we also provide thermal properties of the crystals as a function of temperature.

[1]  K. Shimamura,et al.  Growth and characteristics of optical single crystals for UV/VUV applications , 2011 .

[2]  Akito Kuramata,et al.  Development of gallium oxide power devices , 2014 .

[3]  Steffen Ganschow,et al.  Czochralski growth and characterization of β‐Ga2O3 single crystals , 2010 .

[4]  Takayoshi Oshima,et al.  Ga2O3 Thin Film Growth on c-Plane Sapphire Substrates by Molecular Beam Epitaxy for Deep-Ultraviolet Photodetectors , 2007 .

[5]  R. Fornari,et al.  Schottky barrier height of Au on the transparent semiconducting oxide β-Ga2O3 , 2012 .

[6]  Hideo Hosono,et al.  Anisotropy of electrical and optical properties in β-Ga2O3 single crystals , 1997 .

[7]  D. Schwabe,et al.  An analysis of and a model for spiral growth of Czochralski-grown oxide crystals with high melting point , 2011 .

[8]  High-voltage field effect transistors with wide-bandgap β-Ga2O3 nanomembranes , 2013, 1310.6824.

[9]  Hisao Suzuki,et al.  β‐Gallium Oxide as Oxygen Gas Sensors at a High Temperature , 2007 .

[10]  Hideo Hosono,et al.  Synthesis and control of conductivity of ultraviolet transmitting β-Ga2O3 single crystals , 1997 .

[11]  Noboru Ichinose,et al.  Large-size β-Ga2O3 single crystals and wafers , 2004 .

[12]  J. Woods,et al.  Some electrical properties of the semiconductor βGa2O3 , 1966 .

[13]  K. Nakajima,et al.  Characterization of transparent and conducting Sn-doped β-Ga2O3 single crystal after annealing , 2008 .

[14]  A. Chase.  Growth of β‐Ga2, O3 by the Verneuil Technique , 1964 .

[15]  Jun Xu,et al.  Growth and characterization of new transparent conductive oxides single crystals β-Ga2O3: Sn , 2006 .

[16]  Marius Grundmann,et al.  Determination of the mean and the homogeneous barrier height of Cu Schottky contacts on heteroepitaxial β‐Ga2O3 thin films grown by pulsed laser deposition , 2014 .

[17]  T. Harwig,et al.  Electrical properties of β-Ga2O3 single crystals , 1976 .

[18]  A. Yoshikawa,et al.  Floating zone growth of β-Ga2O3: a new window material for optoelectronic device applications , 2001 .

[19]  Akira Ohtomo,et al.  Formation of Semi-Insulating Layers on Semiconducting β-Ga2O3 Single Crystals by Thermal Oxidation , 2013 .

[20]  Kiyoshi Shimamura,et al.  Electrical conductivity and carrier concentration control in β-Ga2O3 by Si doping , 2008 .

[21]  Hideo Aida,et al.  Growth of β-Ga2O3 Single Crystals by the Edge-Defined, Film Fed Growth Method , 2008 .

[22]  M. Neubert,et al.  Quantitative approaches in laser scattering tomography , 2001 .

[23]  Shinji Nakagomi,et al.  Solar-blind photodiodes composed of a Au Schottky contact and a β-Ga2O3 single crystal with a high resistivity cap layer , 2011 .

[24]  Akito Kuramata,et al.  MBE grown Ga2O3 and its power device applications , 2013 .

[25]  J. Schoonman,et al.  Electrical properties of β-Ga2O3 single crystals. II , 1978 .

[26]  Akito Kuramata,et al.  Gallium oxide (Ga2O3) metal-semiconductor field-effect transistors on single-crystal β-Ga2O3 (010) substrates , 2012 .

[27]  R. Uecker,et al.  Growth of oxide compounds under dynamic atmosphere composition , 2008, 0805.2217.

[28]  R. Roy,et al.  Flux Growth and Characterization of β‐Ga2O3 Single Crystals , 1966 .

[29]  Peter Reiche,et al.  Czochralski grown Ga2O3 crystals , 2000 .

[30]  Hideo Hosono,et al.  Growth, structure and carrier transport properties of Ga2O3 epitaxial film examined for transparent field-effect transistor , 2006 .

[31]  On the chemical transport of gallium oxide in the Ga2O3/N-H-Cl system , 1986 .

[32]  Bin Li,et al.  Growth and spectral characterization of β-Ga2O3 single crystals , 2006 .

[33]  Tohru Honda,et al.  Correlation between blue luminescence intensity and resistivity in β-Ga2O3 single crystals , 2013 .

[34]  Reinhard Uecker,et al.  Electrical properties of β-Ga2O3 single crystals grown by the Czochralski method , 2011 .