The non-oxidative dissolution of galena nanocrystals: Insights into mineral dissolution rates as a function of grain size, shape, and aggregation state

Abstract The acidic, non-oxidative dissolution of galena (PbS) nanocrystals has been studied in detail using transmission electron microscopy (TEM) to follow the evolution of the size and shape of the nanocrystals before and after dissolution experiments, X-ray photoelectron spectroscopy (XPS) to follow particle chemistry, and dissolution rate analysis to compare dissolution rates between nanocrystalline and bulk galena. Dissolution characteristics were also studied as a function of nanocrystal access to bulk vs. confined solution due to the degree of proximity of next-nearest grains. Nearly monodisperse galena nanocyrstals with an average diameter of 14.4 nm were synthesized for this study, and samples were exposed to pH 3, deoxygenated HCl solutions for up to 3 h at 25 °C. Detailed XPS analysis showed the nanocrystals to be free of unwanted contamination, surface complexes, and oxidative artifacts, except for small amounts of lead-containing oxidation species in both pre- and post-dissolution samples which have been observed in fresh, natural bulk galena. Depending on the calculation methods used, galena nanocrystals, under the conditions of our experiments, dissolve at a surface area normalized rate of one to two orders of magnitude faster than bulk galena under similar conditions. We believe that this reflects the higher percentage of reactive surface area on nanocrystalline surfaces vs. surfaces on larger crystals. In addition, it was shown that {1 1 1} and {1 1 0} faces dissolve faster than {1 0 0} faces on nanocrystals, rationalized by the average coordination number of ions on each of these faces. Finally, dissolution was greatly inhibited for galena nanocrystal surfaces that were closely adjacent (1–2 nm, or less) to other nanocyrstals, a direct indication of the properties of aqueous solutions and ion transport in extremely confined spaces and relevant to dissolution variations that have been suspected within aggregates.

[1]  Y. Awakura,et al.  A kinetic study of nonoxidative dissolution of galena in aqueous acid solution , 1980 .

[2]  R. Smart,et al.  Oxidation of Galena Surfaces: I. X-Ray Photoelectron Spectroscopic and Dissolution Kinetics Studies , 1994 .

[3]  J. Tester,et al.  Correlating quartz dissolution kinetics in pure water from 25 to 625°C , 1994 .

[4]  J. Banfield,et al.  Nanoparticles and the Environment , 2001 .

[5]  Eric A. Meulenkamp,et al.  Size Dependence of the Dissolution of ZnO Nanoparticles , 1998 .

[6]  Takehiko Kitamori,et al.  NMR study of water molecules confined in extended nanospaces. , 2007, Angewandte Chemie.

[7]  A. Gerson,et al.  A quantum chemical investigation of the oxidation and dissolution mechanisms of Galena , 2003 .

[8]  D. Sparks,et al.  Nanominerals, Mineral Nanoparticles, and Earth Systems , 2008, Science.

[9]  D. R. Penn,et al.  Calculations of electron inelastic mean free paths. III. Data for 15 inorganic compounds over the 50–2000 eV range , 1991 .

[10]  Banfield,et al.  Imperfect oriented attachment: dislocation generation in defect-free nanocrystals , 1998, Science.

[11]  Takehiko Kitamori,et al.  Nanochannels on a Fused-Silica Microchip and Liquid Properties Investigation by Time-Resolved Fluorescence Measurements , 2002 .

[12]  I. Kartio,et al.  XPS and SR-XPS techniques applied to sulphide mineral surfaces , 1997 .

[13]  W. Vogelsberger,et al.  Dissolution kinetics of nanodispersed gamma-alumina in aqueous solution at different pH: unusual kinetic size effect and formation of a new phase. , 2006, Journal of colloid and interface science.

[14]  A. S. Madden,et al.  A test of geochemical reactivity as a function of mineral size: Manganese oxidation promoted by hematite nanoparticles , 2005 .

[15]  K. Soga,et al.  Particle shape characterisation using Fourier descriptor analysis , 2001 .

[16]  A. Lasaga.  Kinetic theory in the earth sciences , 1998 .

[17]  A. Rossi,et al.  Mechanisms of galena dissolution in oxygen-saturated solutions : Evaluation of pH effect on apparent activation energies and mineral-water interface , 2005 .

[18]  M. Arnold,et al.  Anomalien bei der Ablösung von KieselsÄure von der OberflÄche feinkörniger Siliziumdioxydpulver , 1961 .

[19]  Michael F. Hochella,et al.  Insights for size-dependent reactivity of hematite nanomineral surfaces through Cu2+ sorption , 2006 .

[20]  David W. Luerkins.  Theory and Application of Morphological Analysis: Fine Particles and Surfaces , 1991 .

[21]  J. Banfield,et al.  Chemical weathering of silicates in nature; a microscopic perspective with theoretical considerations , 1995 .

[22]  Jun Chen,et al.  Relationship between solubility and solubility product: The roles of crystal sizes and crystallographic directions , 2006 .

[23]  C. Ayora,et al.  Rate law for galena dissolution in acidic environment , 2007 .

[24]  R. Smart,et al.  STM and XPS investigation of reaction of galena in air , 1993 .

[25]  G. H. Nancollas,et al.  Mechanism of dissolution of sparingly soluble electrolytes. , 2001, Journal of the American Chemical Society.

[26]  W. Stickle,et al.  Handbook of X-Ray Photoelectron Spectroscopy , 1992 .

[27]  J. Langford,et al.  Scherrer after sixty years: a survey and some new results in the determination of crystallite size , 1978 .

[28]  S. Zhang,et al.  Dissolution kinetics of galena in acid NaCl solutions at 25—75 °C , 2004 .

[29]  Ludovico Cademartiri,et al.  Multigram scale, solventless, and diffusion-controlled route to highly monodisperse PbS nanocrystals. , 2006, The journal of physical chemistry. B.

[30]  T. Hyeon,et al.  Generalized and facile synthesis of semiconducting metal sulfide nanocrystals. , 2003, Journal of the American Chemical Society.

[31]  D. R. Penn,et al.  Calculations of Electron Inelastic Mean Free Paths II. Data for 27 Elements over the 50-2000 eV Range | NIST , 1991 .

[32]  Jillian F. Banfield,et al.  Nanoparticles in the Environment , 2001 .

[33]  M. Hochella,et al.  The calculation of STM images, STS spectra, and XPS peak shifts for galena: New tools for understanding mineral surface chemistry , 1996 .

[34]  Jinwoo Cheon,et al.  Single-crystalline star-shaped nanocrystals and their evolution: programming the geometry of nano-building blocks. , 2002, Journal of the American Chemical Society.

[35]  A. Lasaga,et al.  Mineralogical approaches to fundamental crystal dissolution kinetics , 2004 .

[36]  C. Croxton.  Fluid interfacial phenomena , 1986 .

[37]  Eric I Corwin,et al.  Kinetically driven self assembly of highly ordered nanoparticle monolayers , 2006, Nature materials.

[38]  S. Pizer,et al.  The Image Processing Handbook , 1994 .