Mechanical Compatibility between Mg3(Sb,Bi)2 and MgAgSb in Thermoelectric Modules.

Thermoelectric (TE) modules are exposed to temperature gradients and repeated thermal cycles during their operation; therefore, mechanically robust n- and p-type legs are required to ensure their structural integrity. The difference in the coefficients of thermal expansion (CTEs) of the two legs of a TE module can cause stress buildup and the deterioration of performance with frequent thermal cycles. Recently, n-type Mg3Sb2 and p-type MgAgSb have become two promising components of low-temperature TE modules because of to their high TE performance, nontoxicity, and abundance. However, the CTEs of n-Mg3Sb2 and p-MgAgSb differ by approximately 10%. Furthermore, the oxidation resistances of these materials at increased temperatures are unclear. This work manipulates the thermal expansion of Mg3Sb2 by alloying it with Mg3Bi2. The addition of Bi to Mg3Sb2 reduces the coefficient of linear thermal expansion from 22.6 × 10-6 to 21.2 × 10-6 K-1 for Mg3Sb1.5Bi0.5, which is in excellent agreement with that of MgAgSb (21 × 10-6 K-1). Furthermore, thermogravimetric data indicate that both Mg3Sb1.5Bi0.5 and MgAgSb are stable in air and Ar at temperatures below ∼570 K. The results suggest the compatibility and robustness of Mg3Sb1.5Bi0.5 and MgAgSb as a pair of thermoelectric legs for low-temperature TE modules.

[1]  Chengyan Liu,et al.  Interface and Surface Engineering Realized High Efficiency of 13% and Improved Thermal Stability in Mg3Sb1.5Bi0.5‐Based Thermoelectric Generation Devices , 2022, Advanced Energy Materials.

[2]  K. Suekuni,et al.  An effective synthesis route for high-performance α-MgAgSb thermoelectric material , 2022, Journal of Materials Science.

[3]  K. Nielsch,et al.  Geometrical Optimization and Thermal-Stability Characterization of Te-Free Thermoelectric Modules Based on MgAgSb/Mg3 (Bi,Sb)2. , 2022, Small.

[4]  Chengyan Liu,et al.  A general design strategy for thermoelectric interface materials in n-type Mg3Sb1.5Bi0.5 single leg used in TEGs , 2021, Acta Materialia.

[5]  K. Tsuchiya,et al.  Demonstration of ultrahigh thermoelectric efficiency of ∼7.3% in Mg3Sb2/MgAgSb module for low-temperature energy harvesting , 2021 .

[6]  S. Pennycook,et al.  High-entropy-stabilized chalcogenides with high thermoelectric performance , 2021, Science.

[7]  Z. Ren,et al.  Towards tellurium-free thermoelectric modules for power generation from low-grade heat , 2021, Nature Communications.

[8]  H. Nishiate,et al.  Thermoelectric properties of yttrium-doped Mg3(Sb,Bi)2 synthesized by melting method , 2020 .

[9]  Z. Ren,et al.  N-type Mg3Sb2-Bi with improved thermal stability for thermoelectric power generation , 2020 .

[10]  G. Najafi,et al.  A review of industrial waste heat recovery system for power generation with Organic Rankine Cycle: Recent challenges and future outlook , 2020 .

[11]  Yang Wang,et al.  Enhanced electrical transport performance through cation site doping in Y-doped Mg3.2Sb2 , 2020 .

[12]  Y. Thimont,et al.  Characterization of the thermo-mechanical properties of p-type (MnSi1.77) and n-type (Mg2Si0.6Sn0.4) thermoelectric materials , 2019, Scripta Materialia.

[13]  Gang Chen,et al.  High thermoelectric cooling performance of n-type Mg3Bi2-based materials , 2019, Science.

[14]  Zhiwei Chen,et al.  Extraordinary n‐Type Mg3SbBi Thermoelectrics Enabled by Yttrium Doping , 2019, Advanced materials.

[15]  Chun Yang,et al.  Perspectives for low-temperature waste heat recovery , 2019, Energy.

[16]  Z. Ren,et al.  Realizing high conversion efficiency of Mg3Sb2-based thermoelectric materials , 2019, Journal of Power Sources.

[17]  M. Kanatzidis,et al.  All-Scale Hierarchically Structured p-Type PbSe Alloys with High Thermoelectric Performance Enabled by Improved Band Degeneracy. , 2019, Journal of the American Chemical Society.

[18]  Bo Zhang,et al.  Quantification of global waste heat and its environmental effects , 2019, Applied Energy.

[19]  David J. Singh,et al.  Discovery of TaFeSb-based half-Heuslers with high thermoelectric performance , 2019, Nature Communications.

[20]  Y. Liu,et al.  Mg3+δSbxBi2−x Family: A Promising Substitute for the State‐of‐the‐Art n‐Type Thermoelectric Materials near Room Temperature , 2018, Advanced Functional Materials.

[21]  G. J. Snyder,et al.  Heat capacity of Mg3Sb2, Mg3Bi2, and their alloys at high temperature , 2018, Materials Today Physics.

[22]  George Kosmadakis,et al.  Industrial waste heat: Estimation of the technically available resource in the EU per industrial sector, temperature level and country , 2018, Applied Thermal Engineering.

[23]  Yue Chen,et al.  3D charge and 2D phonon transports leading to high out-of-plane ZT in n-type SnSe crystals , 2018, Science.

[24]  Gian-Marco Rignanese,et al.  An Unlikely Route to Low Lattice Thermal Conductivity: Small Atoms in a Simple Layered Structure , 2018, Joule.

[25]  G. J. Snyder,et al.  Improving the thermoelectric performance in Mg3+xSb1.5Bi0.49Te0.01 by reducing excess Mg , 2018 .

[26]  B. Iversen,et al.  Elaborating the Crystal Structures of MgAgSb Thermoelectric Compound: Polymorphs and Atomic Disorders , 2017 .

[27]  Z. Ren,et al.  Mechanical properties of nanostructured thermoelectric materials α-MgAgSb , 2017 .

[28]  T. Kanno,et al.  Isotropic Conduction Network and Defect Chemistry in Mg3+δSb2‐Based Layered Zintl Compounds with High Thermoelectric Performance , 2016, Advanced materials.

[29]  Xiaodong Zhang,et al.  Structural, elastic, electronic, and thermodynamic properties of MgAgSb investigated by density functional theory* , 2016 .

[30]  Clemens Forman,et al.  Estimating the global waste heat potential , 2016 .

[31]  Qi Zhang,et al.  Capturing the invisible resource: Analysis of waste heat potential in Chinese industry , 2016 .

[32]  Xinbing Zhao,et al.  Realizing high figure of merit in heavy-band p-type half-Heusler thermoelectric materials , 2015, Nature Communications.

[33]  Philippe Ghosez,et al.  Optimization of Thermoelectric Properties of MgAgSb-Based Materials: A First-Principles Investigation , 2015 .

[34]  Yaniv Gelbstein,et al.  Functional Graded Germanium–Lead Chalcogenide‐Based Thermoelectric Module for Renewable Energy Applications , 2015 .

[35]  Wenqing Zhang,et al.  High Performance α-MgAgSb Thermoelectric Materials for Low Temperature Power Generation , 2015 .

[36]  Kenneth McEnaney,et al.  High thermoelectric performance of MgAgSb-based materials , 2014 .

[37]  M. Kanatzidis,et al.  Ultralow thermal conductivity and high thermoelectric figure of merit in SnSe crystals , 2014, Nature.

[38]  E. Case,et al.  Room-Temperature Mechanical Properties and Slow Crack Growth Behavior of Mg2Si Thermoelectric Materials , 2012, Journal of Electronic Materials.

[39]  J. S. Liu,et al.  Thermal stability and elastic properties of Mg3Sb2 and Mg3Bi2 phases from first-principles calculations , 2010 .

[40]  Edward J. Timm,et al.  Room temperature Young's modulus, shear modulus, Poisson's ratio and hardness of PbTe–PbS thermoelectric materials , 2010 .

[41]  S. Yamanaka,et al.  Thermal expansion and melting temperature of the half-Heusler compounds: MNiSn (M = Ti, Zr, Hf) , 2010 .

[42]  D Kraemer,et al.  Thermoelectric properties and efficiency measurements under large temperature differences. , 2009, The Review of scientific instruments.

[43]  William T. Choate,et al.  Waste Heat Recovery. Technology and Opportunities in U.S. Industry , 2008 .

[44]  G. J. Snyder,et al.  Complex thermoelectric materials. , 2008, Nature materials.

[45]  G. J. Snyder,et al.  Yb14MnSb11: New High Efficiency Thermoelectric Material for Power Generation , 2006 .

[46]  A. Watanabe,et al.  Electronic structures of Mg3Pn2 (Pn=N, P, As, Sb and Bi) and Ca3N2 calculated by a first-principle pseudopotential method , 2006 .

[47]  G. J. Snyder,et al.  Disordered zinc in Zn4Sb3 with phonon-glass and electron-crystal thermoelectric properties , 2004, Nature materials.

[48]  W. Howells,et al.  Fast-ion conduction and the structure of beta -Mg3Bi2 , 1994 .

[49]  K. Schubert,et al.  Über messingartige Phasen mit A3-verwandter Struktur , 1959 .

[50]  M. U. Cohen,et al.  Precision Lattice Constants from X‐Ray Powder Photographs , 1935 .

[51]  E. Husemann.,et al.  Bindungsart und Gitterbau binärer Magnesiumverbindungen , 1933 .