Development of a strain based fracture assessment procedure for undermatched pipe girth welds subjected to bending

Abstract Structural integrity assessment of pipeline girth welds subjected to high strain levels which arises from the reel-lay method relies on precise crack driving force estimation procedures. Recent developments in subsea technology favor the use of high strength carbon steel pipelines with an internal corrosion resistant layer to increase protection against corrosive fluids. In contrast to homogeneous structural components, the bimetal configuration may induce the occurrence of weld strength undermatch, with a strong impact on the relationship between remote applied load and crack tip constraint. This work explores the development of a crack driving force estimation procedure based on a strain-based version of the EPRI J estimation scheme coupled with the equivalent stress-strain relationship method (ESSRM) and a weld geometry simplification procedure. The proposed framework takes advantage of the displacement controlled nature of the reeling process. Extensive 3D analyses provide a large set of fracture parameters applicable to the strain-based EPRI methodology followed by parametric analyses conducted to assess the accuracy of the new procedure. Subsequently, a case study is performed to determine the tolerable crack sizes in an idealized pipe installation. The procedure shows an overall good agreement to the benchmark analyses and increased accuracy when compared to the recommended approach proposed by DNV.

[1]  Claudio Ruggieri,et al.  Engineering approach for circumferential flaws in girth weld pipes subjected to bending load , 2015 .

[2]  Claudio Ruggieri,et al.  J and CTOD estimation procedure for circumferential surface cracks in pipes under bending , 2010 .

[3]  Nicola Bonora,et al.  Fracture Integrity Assessment of Flawed Bi-Metallic Girth Weld Joint , 2013 .

[4]  Robert A. Ainsworth,et al.  The estimation of J in three-point-bend specimens with a crack in a mismatched weld , 1997 .

[5]  Claudio Ruggieri,et al.  Estimation procedure of J-resistance curves for SE(T) fracture specimens using unloading compliance , 2007 .

[6]  Claudio Ruggieri,et al.  A numerical investigation of constraint effects in circumferentially cracked pipes and fracture specimens including ductile tearing , 2014 .

[7]  Robert A. Ainsworth,et al.  The assessment of defects in structures of strain hardening material , 1984 .

[8]  Claudio Ruggieri,et al.  Fracture assessments of clad pipe girth welds incorporating improved crack driving force solutions , 2015 .

[9]  Zhiliang Zhang,et al.  A framework for fracture assessments of dissimilar girth welds in offshore pipelines under bending , 2016 .

[10]  Erling Østby.  Fracture Control — Offshore Pipelines: New Strain-Based Fracture Mechanics Equations Including the Effects of Biaxial Loading, Mismatch, and Misalignment , 2005 .

[11]  Bård Nyhus,et al.  SENT Specimens an Alternative to SENB Specimens for Fracture Mechanics Testing of Pipelines , 2003 .

[12]  Pei-Ning Li,et al.  Limit load and J estimates of a centre cracked plate with an asymmetric crack in a mismatched weld , 1999 .

[13]  Nicola Bonora,et al.  Simplified Approach for Fracture Integrity Assessment of Bimetallic Girth Weld Joint , 2013 .

[14]  Nikzad Nourpanah,et al.  Development of a reference strain approach for assessment of fracture response of reeled pipelines , 2010 .

[15]  Aurélien Pépin,et al.  Methodology for Assessment of Surface Defects in Undermatched Pipeline Girth Welds , 2015 .

[16]  Rudi Denys,et al.  J-integral analysis of heterogeneous mismatched girth welds in clamped single-edge notched tension specimens , 2014 .

[17]  F. M. Burdekin,et al.  Engineering critical analyses to BS 7910 — the UK guide on methods for assessing the acceptability of flaws in metallic structures , 2000 .

[18]  Erling Østby,et al.  Fracture response of pipelines subjected to large plastic deformation under tension , 2004 .

[19]  James C. Newman,et al.  Stress-intensity factors for a wide range of semi-elliptical surface cracks in finite-thickness plates , 1979 .

[20]  Robert A. Ainsworth,et al.  A J integral estimation method for cracks in welds with mismatched mechanical properties , 1997 .

[21]  Noel P. O’Dowd,et al.  Fully-Plastic Strain-Based J Estimation Scheme for Circumferential Surface Cracks in Pipes Subjected to Reeling , 2015 .

[22]  A. Cornec,et al.  Plastic stress-strain fields and limit loads of a plane strain cracked tensile panel with a mismatched welded joint , 1997 .

[23]  Tomasz Tkaczyk,et al.  Fracture Assessment Procedures for Steel Pipelines Using a Modified Reference Stress Solution , 2009 .

[24]  Erlend Olso̸,et al.  New Assessment Approach For ECA of Clad And Lined Pipes Based On Shell And Line-spring Finite Elements , 2011 .

[25]  Stelios Kyriakides,et al.  Mechanics of Offshore Pipelines , 2007 .

[26]  Zhongmin Xiao,et al.  On 3-D crack problems in offshore pipeline with large plastic deformation , 2013 .

[27]  Claudio Ruggieri,et al.  Further results in J and CTOD estimation procedures for SE(T) fracture specimens – Part II: Weld centerline cracks , 2012 .

[28]  N. Dowling.  Mechanical Behavior of Materials: Engineering Methods for Deformation, Fracture, and Fatigue , 1993 .

[29]  J. Hutchinson.  Fundamentals of the Phenomenological Theory of Nonlinear Fracture Mechanics , 1983 .

[30]  R. Steinbuch,et al.  Critical crack sizes in ductile piping , 1981 .