Deformation stages in a stabilized loading cycle of fatigued FCC metals (I) experimental results

Stabilized hysteresis loops from fatigue tests on polycrystalline nickel and on nickel monocrystals have been analysed.

C. Holste | W. Kleinert | W. Fischer

[1] H. Mughrabi,et al. Dislocation wall and cell structures and long-range internal stresses in deformed metal crystals , 1983 .

[2] M. Klesnil,et al. THE HYSTERESIS LOOP 2. AN ANALYSIS OF THE LOOP SHAPE , 1982 .

[3] M. Klesnil,et al. THE HYSTERESIS LOOP 3. STRESS‐DIP EXPERIMENTS , 1982 .

[4] M. Klesnil,et al. THE HYSTERESIS LOOP 1. A STATISTICAL THEORY , 1982 .

[5] C. Blochwitz,et al. Plateau Behaviour of Fatigued FCC Single Crystals , 1982 .

[6] H. Burmeister,et al. Change of activation area during cyclic deformation. II. Quantitative interpretation with a model of heterogeneous plastie deformation , 1981 .

[7] O. B. Pedersen,et al. Fatigue of copper polycrystals at low plastic strain amplitudes , 1980 .

[8] H. Burmeister,et al. Change of long-range stresses in cyclic deformation , 1980 .

[9] H. Mughrabi,et al. The cyclic hardening and saturation behaviour of copper single crystals , 1978 .

[10] Petr Lukáš,et al. Cyclic stress-strain response and fatigue life of metals in low amplitude region , 1973 .

[11] H. Conrad. The athermal component of the flow stress in crystalline solids , 1970 .

[12] C. Feltner,et al. Microplastic Strain Hysteresis Energy as a Criterion for Fatigue Fracture , 1961 .

[13] A. Cottrell,et al. Dislocations and plastic flow in crystals , 1953 .