Implications of the lead crack philosophy and the role of short cracks in combat aircraft

Abstract The Australian Defence Science and Technology (DSTO)/Royal Australian Air Force (RAAF) approach to the management of fatigue cracking in combat and trainer aircraft makes use of the “lead crack” concept. In this approach crack growth is assumed to initiate from small naturally occurring defects/discontinuities with dimensions of approximately 10 μm and growth is assumed to commence from day one. As a result, for certification purposes, we need to address the so called short crack anomaly, whereby for a given Δ K the crack growth rate ( da / dN ) is significantly greater for short cracks than it is for long cracks. In this paper we reveal that there are several instances where this anomaly vanishes if da / dN is represented as a function of (Δ K  − Δ K thr ), where Δ K thr can be thought of as an apparent threshold. We then show that for operational aircraft the “true” da / dN versus Δ K curve is an amalgam of the short and long crack growth curves. We next show that existing test procedures used to establish the effect of composite repairs to cracks in fleet aircraft overestimate their effect. We also show that the growth of cracks from small naturally occurring defects exhibits little, if any, R ratio effects.

[1]  Dietmar Eifler,et al.  An analysis of the growth of short fatigue cracks , 1991 .

[2]  Satoshi Sunada,et al.  Prediction of corrosion fatigue lives of aluminium alloy on the basis of corrosion pit growth law , 2006 .

[3]  Ian F. C. Smith,et al.  Fatigue crack growth in a fillet welded joint , 1983 .

[4]  A. Merati.  A study of nucleation and fatigue behavior of an aerospace aluminum alloy 2024-T3 , 2005 .

[5]  Reji John,et al.  Stress Ratio Effects on Small Fatigue Crack Growth in Ti-6Al-4V (Preprint) , 2008 .

[6]  Manfred A. Hirt,et al.  Fatigue crack propagation in steels , 1983 .

[7]  Diran Apelian,et al.  Closure mechanisms in Al–Si–Mg cast alloys and long-crack to small-crack corrections , 2005 .

[8]  M. James,et al.  Mechanical Data for Use in Damage Tolerance Analyses , 2013 .

[9]  E. Lara‐Curzio,et al.  A model for the formation of fatigue striations and its relationship with small fatigue crack growth in an aluminum alloy , 2010 .

[10]  Alan Baker,et al.  Repair of mirage III aircraft using the BFRP crack-patching technique , 1984 .

[11]  Chuan-yao Chen,et al.  Fatigue Crack Growth and Control of 14MnNbq Welding Plates Used for Bridges , 2012 .

[12]  J. Schijve.  Fatigue life until small cracks in aircraft structures: Durability and damage tolerance , 1994 .

[13]  Peter Chalkley,et al.  Service History of the F-111 Wing Pivot Fitting Upper Surface Boron/Epoxy Doublers , 1998 .

[14]  A. K. Vasudevan,et al.  Two critical stress intensities for threshold fatigue crack propagation , 1993 .

[15]  D. V. Ramsamooj,et al.  Analytical prediction of short to long fatigue crack growth rate using small- and large-scale yielding fracture mechanics , 2003 .

[16]  Kwai S. Chan,et al.  Variability of large-crack fatigue-crack-growth thresholds in structural alloys , 2004 .

[17]  R. Pippan,et al.  Short cracks initiated in Al 6013-T6 with the focused ion beam (FIB)-technology , 2007 .

[18]  Rong Wang,et al.  A fracture model of corrosion fatigue crack propagation of aluminum alloys based on the material elements fracture ahead of a crack tip , 2008 .

[19]  Simon Barter,et al.  Experimental studies into short crack growth , 2011 .

[20]  Robert O. Ritchie,et al.  ON THE BEHAVIOR OF SMALL FATIGUE CRACKS IN COMMERCIAL ALUMINUM-LITHIUM ALLOYS , 1988 .

[21]  David Thevenet,et al.  Short surface fatigue cracks growth under constant and variable amplitude loading , 2009 .

[22]  David Hui,et al.  Application of the Hartman–Schijve equation to represent Mode I and Mode II fatigue delamination growth in composites , 2012 .

[23]  Sotomi Ishihara,et al.  Study of the fatigue lifetimes and crack propagation behaviour of a high speed steel as a function of the R value , 2010 .

[24]  R. S. Piascik,et al.  The Growth of Small Corrosion Fatigue Cracks in Alloy 7075 , 1993 .

[25]  C. Rodopoulos,et al.  On the use of supersonic particle deposition to restore the structural integrity of damaged aircraft structures , 2011 .

[26]  Brad Lee Boyce,et al.  On the application of the Kitagawa-Takahashi diagram to foreign-object damage and high-cycle fatigue , 2002 .

[27]  R. Wang,et al.  Corrosion fatigue crack propagation of an aluminum alloy under periodic overloads , 2012 .

[28]  Brad L. Boyce,et al.  Effect of load ratio and maximum stress intensity on the fatigue threshold in Ti–6Al–4V , 2001 .

[29]  A. Baker,et al.  Bonded repair of aircraft structures , 1988 .

[30]  David L. Davidson,et al.  The dependence of crack closure on fatigue loading variables , 1988 .

[31]  J. C. Newman,et al.  Crack closure under high load-ratio conditions for Inconel-718 near threshold behavior , 2009 .

[32]  Bo Alfredsson,et al.  Fatigue growth of short cracks in Ti-17 : experiments and simulations , 2007 .

[33]  Lorrie Molent,et al.  Experimentally derived crack growth models for different stress concentration factors , 2008 .

[34]  Russell Wanhill,et al.  The lead crack fatigue lifing framework , 2011 .

[35]  R. Forman,et al.  Numerical Analysis of Crack Propagation in Cyclic-Loaded Structures , 1967 .

[36]  K. N. Pandey,et al.  Fatigue crack growth model for constant amplitude loading , 2004 .

[37]  A. Hartman,et al.  The effects of environment and load frequency on the crack propagation law for macro fatigue crack growth in aluminium alloys , 1970 .

[38]  A. J. Mcevily,et al.  Prediction of the behavior of small fatigue cracks , 2007 .

[39]  Lorrie Molent,et al.  Fatigue crack growth in a diverse range of materials , 2012 .

[40]  Rhys Jones,et al.  An experimental evaluation of crack face energy dissipation , 2006 .

[41]  Y. Kondo,et al.  Short Crack Growth Behavior and Its Relation to Notch Sensitivity and VHCF , 2013 .

[42]  C. Atkinson,et al.  The development of a general fatigue crack growth predictive model , 1977 .

[43]  J. Sheldon,et al.  Investigation of the effects of shed-rate, initial Kmax, and geometric constraint on ΔKth in Ti–6Al–4V at room temperature , 1999 .

[44]  Paul C. Paris,et al.  Reflections on identifying the real ΔKeffective in the threshold region and beyond , 2008 .

[45]  James C. Newman,et al.  Improved test method for very low fatigue‐crack‐growth‐rate data , 2008 .

[46]  L. Molent,et al.  Crack growth of physically small cracks , 2007 .

[47]  Rhys Jones.  A scientific evaluation of the approximate 2D theories for composite repairs to cracked metallic components , 2009 .

[48]  Rhys Jones,et al.  Characterization of the durability of adhesive bonds , 2012 .

[49]  H. W. Liu,et al.  A quantitative analysis of structure sensitive fatigue crack growth in steels , 1984 .

[50]  Paul C. Paris,et al.  Service load fatigue damage — a historical perspective , 1999 .

[51]  P. C. Paris,et al.  A Critical Analysis of Crack Propagation Laws , 1963 .

[52]  K. T. Venkateswara.  ON THE BEHAVIOR OF SMALL FATIGUE CRACKS IN COMMERCIAL ALUMINUM-LITHIUM ALLOYS , 1988 .