Through-hole membranes of nanoporous alumina formed by anodizing in oxalic acid and their applications in fabrication of nanowire arrays

Abstract The nanopore arrays were fabricated by two-step self-organized anodization of aluminum carried out in 0.3 M oxalic acid at the temperature of 20 °C. This relatively high temperature shortens significantly the anodizing time and allows to fabricate quickly thick through-hole membranes without the additional operating cost of a cooling circuit. The structural features of anodic porous alumina such as pore diameter, interpore distance, porosity, pore density and pore circularity were investigated at various durations of pore opening/widening process carried out in 5% H 3 PO 4 . An excellent agreement of AAO structural features measured in FE-SEM images of the studied samples with results from software calculations was observed. The pore shape can be monitored qualitatively by fast Fourier transforms (FFTs) and quantitatively by calculation the percentage of pore circularity. Additionally, the regularity of the hexagonal arrangement of nanopores in through-hole AAO membranes was compared for various opening/widening time ranging from 40 to 100 min. It was shown that three-dimensional (3D) representations of FE-SEM images and their surface-height distribution diagrams provide interesting information about the surface roughness evolution during the pore opening/widening process. A template-assisted fabrication of Ag and Sn nanowire arrays by electrochemical deposition into the pores of the prepared AAO templates was also successfully demonstrated.

[1]  G. Sulka,et al.  Anodising potential influence on well-ordered nanostructures formed by anodisation of aluminium in sulphuric acid , 2006 .

[2]  Falong Jia,et al.  Non‐Aqueous Sol–Gel Approach towards the Controllable Synthesis of Nickel Nanospheres, Nanowires, and Nanoflowers , 2008 .

[3]  K. Asakawa,et al.  Selective growth of ordered InGaAs quantum dots on patterned substrates with nano-hole arrays , 2007 .

[4]  K. Nishio,et al.  Control of Pitting Sites on Al for Electrolytic Capacitors Using Patterned Masking Film , 2006 .

[5]  W. Xu,et al.  Fabrication of controllable free-standing ultrathin porous alumina membranes , 2005 .

[6]  C. R. Martin,et al.  Template preparation of nanoelectrode ensembles. Achieving the ‘pure-radial’ electrochemical-response limiting case , 1996 .

[7]  Ralf B. Wehrspohn,et al.  Moiré Pattern Formation on Porous Alumina Arrays Using Nanoimprint Lithography , 2003 .

[8]  R. Inguanta,et al.  Synthesis of self-standing Pd nanowires via galvanic displacement deposition , 2009 .

[9]  Chengde Mao,et al.  DNA-Templated Fabrication of 1D Parallel and 2D Crossed Metallic Nanowire Arrays , 2003 .

[10]  Ning Wang,et al.  Growth of nanowires , 2008 .

[11]  F. Favier,et al.  Metal nanowire arrays by electrodeposition. , 2003, Chemphyschem : a European journal of chemical physics and physical chemistry.

[12]  G. Sulka,et al.  Temperature influence on well-ordered nanopore structures grown by anodization of aluminium in sulphuric acid , 2007 .

[13]  S. Juodkazis,et al.  Aluminum Oxide Photonic Crystals Grown by a New Hybrid Method , 2001 .

[14]  Zhongai Hu,et al.  Large-scale synthesis of defect-free silver nanowires by electrodeless deposition , 2007 .

[15]  G. A. Shafeev,et al.  NANOSTRUCTURES: Formation of nanostructures upon laser ablation of silver in liquids , 2006 .

[16]  Younan Xia,et al.  One‐Dimensional Nanostructures: Synthesis, Characterization, and Applications , 2003 .

[17]  U. Gösele,et al.  Silicon nanowhiskers grown on 〈111〉Si substrates by molecular-beam epitaxy , 2004 .

[18]  G. Borghs,et al.  Effect of Tensile Stress on Growth of Self-Organized Nanostructures on Anodized Aluminum , 2004 .

[19]  C. Chao,et al.  Fabrication of single-crystal tin nanowires by hydraulic pressure injection , 2006 .

[20]  Ali Eftekhari,et al.  Nanostructured Materials in Electrochemistry , 2008 .

[21]  Faqiang Xu,et al.  Cyclic voltammetry for the fabrication of high dense silver nanowire arrays with the assistance of AAO template , 2005 .

[22]  A. Kolmakov,et al.  Topotactic Thermal Oxidation of Sn Nanowires: Intermediate Suboxides and Core-Shell Metastable Structures , 2003 .

[23]  J. Gómez‐Herrero,et al.  WSXM: a software for scanning probe microscopy and a tool for nanotechnology. , 2007, The Review of scientific instruments.

[24]  Ralf B. Wehrspohn,et al.  Hexagonally Arranged Monodisperse Silver Nanowires with Adjustable Diameter and High Aspect Ratio , 2003 .

[25]  Jean-Eric Wegrowe,et al.  Template synthesis of nanomaterials , 2005 .

[26]  Sudipta Seal,et al.  One dimensional nanostructured materials , 2007 .

[27]  Kun-Hong Lee,et al.  Fabrication of highly ordered pore array in anodic aluminum oxide , 2002 .

[28]  S. Mashiko,et al.  Lasing from Two‐Dimensional Photonic Crystals Using Anodic Porous Alumina , 2006 .

[29]  Ralf B. Wehrspohn,et al.  Self-ordering Regimes of Porous Alumina: The 10% Porosity Rule , 2002 .

[30]  Ralf B. Wehrspohn,et al.  Highly ordered monocrystalline silver nanowire arrays , 2002 .

[31]  U. Gösele,et al.  Monodisperse metal nanowire arrays on Si by integration of template synthesis with silicon technology , 2003 .

[32]  L Zaraska,et al.  Properties of nanostructures obtained by anodization of aluminum in phosphoric acid at moderate potentials , 2009 .

[33]  K. Nishio,et al.  Fabrication of Nanocomposites by Filling Nanoholes in Highly Ordered Anodic Porous Alumina by Vacuum Deposition of Metal , 2005 .

[34]  C. Haynes,et al.  Nanosphere Lithography: A Versatile Nanofabrication Tool for Studies of Size-Dependent Nanoparticle Optics , 2001 .

[35]  G. Borghs,et al.  Synthesis of Well-Ordered Nanopores by Anodizing Aluminum Foils in Sulfuric Acid , 2002 .

[36]  Jian Gong,et al.  Silver nanowires prepared by modified AAO template method , 2007 .

[37]  P. Atanassov,et al.  Growth of Patterned Nanopore Arrays of Anodic Aluminum Oxide , 2003 .

[38]  A. Jagminas,et al.  Concentration effect of the solutions for alumina template ac filling by metal arrays , 2003 .

[39]  Woo Y. Lee,et al.  Templated Fabrication of Nanowire and Nanoring Arrays Based on Interference Lithography and Electrochemical Deposition , 2006 .

[40]  C. Ross,et al.  Wafer-scale Ni imprint stamps for porous alumina membranes based on interference lithography. , 2006, Small.

[41]  Deng,et al.  Hierarchically ordered oxides , 1998, Science.

[42]  Massimo Lazzari,et al.  Block Copolymers as a Tool for Nanomaterial Fabrication , 2003 .

[43]  Y. Yao,et al.  Formation of Pt nanorods on nanoporous anodic aluminum oxides by controlled nucleation sites , 2009 .

[44]  Wei Zhang,et al.  Sub-10 nm imprint lithography and applications , 1997, 1997 55th Annual Device Research Conference Digest.

[45]  Kornelius Nielsch,et al.  Polycrystalline nanopore arrays with hexagonal ordering on aluminum , 1999 .

[46]  W. J. Stępniowski,et al.  Structural features of self-organized nanopore arrays formed by anodization of aluminum in oxalic acid at relatively high temperatures , 2009 .