Comparison of the effect of pore architecture and bead size on the extent of plasmachemical amine functionalisation of poly(styrene-co-divinylbenzene) permanently porous resins

Poly(styrene-co-divinylbenzene) (PS/DVB) permanently porous resins suitable for plasmachemical modification with allylamine were prepared by suspension polymerisation. Experimental design methods were employed to investigate simultaneously the influence of crosslinker content, porogen type and porogen level on the surface area, pore volume and pore diameter of the resins. From this, it was found that the porogen has a greater influence than the crosslinker. Variation of porogen type and level while keeping crosslinker level constant then lead to the maximisation of each parameter of interest, resulting in a set of samples with a wide range of values. Six samples were then chosen, representing high and low values of each property, and were subjected to plasmachemical modification with allylamine. It was found that pore volume had the greatest influence on the extent of modification. However, subsequent experiments indicated that the extent of modification is much greater for smaller beads. It is concluded that plasmachemical functionalisation occurs mainly on the external surface of the beads.

[1]  D. Sherrington,et al.  Porosity analysis of some poly(styrene/divinylbenzene)beads by nitrogen sorption and mercury intrusion porosimetry , 2000 .

[2]  M. Dias,et al.  Porous structure and swelling properties of styrene–divinylbenzene copolymers for size exclusion chromatography , 1997 .

[3]  D. Sherrington,et al.  Polymer-supported reactions in organic synthesis , 1980 .

[4]  Steven V. Ley,et al.  Multi-step organic synthesis using solid-supported reagents and scavengers: a new paradigm in chemical library generation , 2000 .

[5]  D. Rabelo,et al.  Structure and properties of styrene-divinylbenzene copolymers , 1994 .

[6]  D. Rabelo,et al.  Structure and properties of styrene-divinylbenzene copolymers. III: Mixtures of different diluents with alcohols as pore forming agents , 1994 .

[7]  D. Rabelo,et al.  Porous volume determination of styrene-divinylbenzene copolymers by water uptake measurements , 1993 .

[8]  D. Rabelo,et al.  Porous structure formation and swelling properties of styrene-divinylbenzene copolymers , 1994 .

[9]  J. Badyal,et al.  Plasmachemical Functionalization of Porous Polystyrene Beads , 2001 .

[10]  A. Guyot,et al.  Styrene divinyl benzene copolymers. I. Texture of macroporous copolymers with ethyl‐2‐hexanoic acid in diluent , 1979 .

[11]  E. Teller,et al.  ADSORPTION OF GASES IN MULTIMOLECULAR LAYERS , 1938 .

[12]  G. Øye,et al.  Plasmachemical Amine Functionalization of Porous Polystyrene Beads: The Importance of Pore Architecture , 2002 .

[13]  L. Errede Polymer swelling. 8. Sorption of 1-iodoalkanes by poly(styrene-co-divinylbenzene) , 1990 .

[14]  Young‐Tae Chang,et al.  Understanding the effects of the polymer support on reaction rates and kinetics: knowledge toward efficient synthetic design. , 2003, Current opinion in chemical biology.

[15]  M. Bradley,et al.  The synthesis of the cyclic antibacterial peptide Kawaguchipeptin B on 11 different DVB cross-linked PS resins , 2000 .

[16]  K. Sing Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity (Recommendations 1984) , 1985 .

[17]  H. Gstach,et al.  Symmetric building blocks and combinatorial functional group transformation as versatile strategies in combinatorial chemistry. , 2000, Biotechnology and bioengineering.

[18]  K. Janda,et al.  Investigating highly crosslinked macroporous resins for solid-phase synthesis. , 1998, Bioorganic & medicinal chemistry letters.

[19]  D. Sherrington,et al.  Syntheses and Separations Using Functional Polymers , 1988 .

[20]  David C. Sherrington,et al.  Polymer-supported reagents, catalysts, and sorbents: evolution and exploitation - a personalized view , 2001 .

[21]  F. M. B. Coutinho,et al.  Synthesis and characterization of styrene–divinylbenzene loaded with di(2‐ethylhexyl)phosphonic acid. I. Influence of diluent mixture on the porous structure of the copolymer , 1998 .

[22]  David C. Sherrington,et al.  PREPARATION, STRUCTURE AND MORPHOLOGY OF POLYMER SUPPORTS , 1999 .

[23]  S. M. Rezende,et al.  Copolymers based on styrene and divinylbenzene synthesized in the presence of DEHPA—I. Structural characterization , 1995 .

[24]  D. Sherrington,et al.  Preparation and Porosity Characterization of Highly Cross-Linked Polymer Resins Derived from Multifunctional (Meth)acrylate Monomers , 2002 .

[25]  S. Koontz,et al.  A new solid-phase support for oligonucleotide synthesis. , 1999, Bioorganic & medicinal chemistry letters.

[26]  K. Sing,et al.  The use of nitrogen adsorption for the characterisation of porous materials , 2001 .

[27]  A. Guyot,et al.  Design and properties of polymers as materials for fine chemistry , 1982 .

[28]  O. Okay,et al.  Macroporous copolymer networks , 2000 .

[29]  R. Cid,et al.  Styrene-divinylbenzene copolymers-formation of porous structure by using precipitants as diluents in suspension polymerization , 1990 .

[30]  F. Dörwald Organic Synthesis on Solid Phase , 2002 .

[31]  D. G. Smith,et al.  33. Solvent-modified polymer networks. Part I. The preparation and characterisation of expanded-network and macroporous styrene–divinylbenzene copolymers and their sulphonates , 1963 .

[32]  R. Nicewonger,et al.  Alternative base matrices for solid phase quenching reagents , 2000 .

[33]  C. Vlad,et al.  Effect of polymeric porogens on the properties of poly(styrene-co-divinylbenzene) , 1997 .

[34]  P. F. Onyon Polymer Handbook , 1972, Nature.

[35]  Jean M. J. Fréchet,et al.  New Designs of Macroporous Polymers and Supports: From Separation to Biocatalysis , 1996, Science.

[36]  E. Barrett,et al.  (CONTRIBUTION FROM THE MULTIPLE FELLOWSHIP OF BAUGH AND SONS COMPANY, MELLOX INSTITUTE) The Determination of Pore Volume and Area Distributions in Porous Substances. I. Computations from Nitrogen Isotherms , 1951 .

[37]  D. Rabelo,et al.  Porous structure formation and swelling properties of styrene–divinylbenzene copolymers – effect of diluent nature , 1994 .

[38]  D. Rabelo,et al.  Scanning electron microscopy of styrene-divinylbenzene copolymers , 1995 .

[39]  J. Seidl,et al.  Makroporöse Styrol-Divinylbenzol-Copolymere und ihre Verwendung in der Chromatographie und zur Darstellung von Ionenaustauschern , 1967 .

[40]  S. Koontz,et al.  The pellicular monolith: pore-surface functionalization and surface-phase construction in macroporous polymeric materials , 1999 .

[41]  D. Rabelo,et al.  Scanning electron microscopy study of styrene-divinylbenzene copolymers , 1992 .

[42]  W. Sederel,et al.  Styrene–divinylbenzene copolymers. Construction of porosity in styrene divinylbenzene matrices , 1973 .

[43]  A. Sutherland,et al.  Use of a scintillant-containing macroporous resin in both solid phase synthesis and subsequent on-bead scintillation-based analysis , 2000 .