Copolymers of ethylene with bicyclic dienes

The copolymerization of ethylene (E) with dicyclopentadiene (DCP), ethylidene norbornene (ENB) or methyl endomethylene hexahydronaphthalene (MEHN) by ZIEGLER-NATTA catalysts in presence of H2 affords low-mol.-wt. products over a wide range of unsaturation. In this paper some characteristic features of the copolymerization and some physical properties of the raw products are discussed. For the catalytic system VOCI3-Al2Et3Cl3 differences in catalyst efficiency, copolymer composition, diene incorporation and viscosity can be seen as a function of type and amount of diene monomer. Physical properties of the copolymers are strongly dependent on composition. Incorporation of dience results in lowered melting points of the parent PE. In case of E-DCP and E-ENB the materials become amorphous beyond 15-20 mole-% diene. At this composition minimum glass transition temperatures are seen. Bei der Copolymerisation von Athylen (E) mit Dicyclopentadien (DCP), Athylidennorbornen (ENB) oder Methyl-Endomethylen-Hexahydronaphthalin (MEHN) durch ZIEGLER-NATTA-Katalysatoren in Gegenwart von H2 entstehen niedermolekulare Produkte uber einen weiten. Bereich an Ungesattigtheit. In dieser Arbeit wird uber einige charakteristische Einzelheiten dieser Copolymerisationen und einige physikalische Eigenschaften der Rohpolymeren berichtet. Diskutiert werden fur das Katalysatorsystem VOCl3-Al2Et3Cl3 Unterschlede in Katalysatorwirksamkeit, Copolymerzusammensetzung, Dieneinbauverhaltnis und Viskositat in Abhangigkeit von der Art und der Menge des Diens. Die physikalischen Eigenschaften der Copolymeren hagen stark von der Zusammensetzung ab. Der Einbau des Comonomeren ausert sich in einer Erniedrigung des Polyathylenschmelzpunktes. Im Fall von E-DCP und E-ENB werden die Produkte bei 15-20 Mol- % Dien aniorph und zeigen ein Mininimum im Glasubergangspunkt.