Active vacuum brazing of CNT films to metal substrates for superior electron field emission performance

Abstract The joining of macroscopic films of vertically aligned multiwalled carbon nanotubes (CNTs) to titanium substrates is demonstrated by active vacuum brazing at 820 °C with a Ag–Cu–Ti alloy and at 880 °C with a Cu–Sn–Ti–Zr alloy. The brazing methodology was elaborated in order to enable the production of highly electrically and thermally conductive CNT/metal substrate contacts. The interfacial electrical resistances of the joints were measured to be as low as 0.35 Ω. The improved interfacial transport properties in the brazed films lead to superior electron field-emission properties when compared to the as-grown films. An emission current of 150 μA was drawn from the brazed nanotubes at an applied electric field of 0.6 V μm−1. The improvement in electron field-emission is mainly attributed to the reduction of the contact resistance between the nanotubes and the substrate. The joints have high re-melting temperatures up to the solidus temperatures of the alloys; far greater than what is achievable with standard solders, thus expanding the application potential of CNT films to high-current and high-power applications where substantial frictional or resistive heating is expected.

[1]  U. E. Klotz,et al.  Influence of brazing parameters and alloy composition on interface morphology of brazed diamond , 2008 .

[2]  Niina Halonen,et al.  Carbon‐Nanotube‐Based Electrical Brush Contacts , 2009 .

[3]  P. Singjai,et al.  Joining carbon nanotubes. , 2011, Nanoscale.

[4]  Y. Naidich,et al.  Investigation of the wetting of diamond and graphite by molten metals and alloys , 1965 .

[5]  L. Schlapbach,et al.  Field emission properties of nanocrystalline chemically vapor deposited-diamond films , 1999 .

[6]  C. Leinenbach,et al.  High-temperature processable carbon–silicate nanocomposite cold electron cathodes for miniature X-ray sources , 2013 .

[7]  Raymond F. Wegman,et al.  Copper and Copper Alloys , 2013 .

[8]  B. Griffin,et al.  HELIUM ION MICROSCOPE , 2010 .

[9]  Changxin Chen,et al.  Ultrasonic nanowelding of carbon nanotubes to metal electrodes , 2006 .

[10]  U. E. Klotz,et al.  Experimental investigation of the Cu–Ti–Zr system at 800 °C , 2007 .

[11]  Chwee Teck Lim,et al.  Versatile transfer of aligned carbon nanotubes with polydimethylsiloxane as the intermediate , 2008, Nanotechnology.

[12]  Yiping Zhao,et al.  Nanocarpet Effect: Pattern Formation during the Wetting of Vertically Aligned Nanorod Arrays , 2004 .

[13]  Kenneth A. Dean,et al.  Degradation and failure of carbon nanotube field emitters , 2003 .

[14]  C. Leinenbach,et al.  X-ray source downscaling enabled by combining microfabricated electrodes with carbon nanotube cold electron emitters , 2014 .

[15]  L. Schlapbach,et al.  Microscopic characterization of electron field emission , 2002 .

[16]  Mustafa Yavuz,et al.  Vacuum brazing of carbon nanotube bundles , 2008 .

[17]  C. Leinenbach,et al.  Microstructure, residual stresses and shear strength of diamond–steel-joints brazed with a Cu–Sn-based active filler alloy , 2012 .

[18]  E. .. Mittemeijer,et al.  The solubility of C in solid Cu , 2004 .

[19]  U. E. Klotz,et al.  Experimental investigation and thermodynamic assessment of the Cu-Sn-Ti ternary system , 2011 .

[20]  Hongjie Dai,et al.  Metal coating on suspended carbon nanotubes and its implication to metal–tube interaction , 2000 .

[21]  C. Leinenbach,et al.  Influence of the brazing parameters on microstructure, residual stresses and shear strength of diamond–metal joints , 2010 .

[22]  Lingbo Zhu,et al.  Well-aligned open-ended carbon nanotube architectures: an approach for device assembly. , 2006, Nano letters.

[23]  N. Tai,et al.  Field emission properties of carbon nanotube arrays through the pattern transfer process , 2006 .

[24]  M. Kaiser,et al.  Microscopic analysis of performance variations in carbon nanotube field emission cathodes: Implications for device optimization , 2012 .

[25]  Kiran Shankar Hazra,et al.  Dramatic enhancement of the emission current density from carbon nanotube based nanosize tips with extremely low onset fields. , 2009, ACS nano.

[26]  C. Bittencourt,et al.  Study of the interaction between copper and carbon nanotubes , 2012 .

[27]  Ado Jorio,et al.  Carbon Nanotubes: Advanced Topics in the Synthesis, Structure, Properties and Applications , 2007 .

[28]  O. Zhou,et al.  Very large current density from carbon nanotube field emitters , 1999, International Electron Devices Meeting 1999. Technical Digest (Cat. No.99CH36318).

[29]  Omkaram Nalamasu,et al.  Contact transfer of aligned carbon nanotube arrays onto conducting substrates , 2006 .

[30]  S. Seal,et al.  Interfacial phenomena in thermally sprayed multiwalled carbon nanotube reinforced aluminum nanocomposite , 2007 .

[31]  M. Dresselhaus.  Carbon nanotubes , 1995 .

[32]  Gaurav Mittal,et al.  Recent progress in nanostructured next-generation field emission devices , 2014 .

[33]  A. Marchand,et al.  Caracterisation de materiaux carbones par microspectrometrie Raman , 1984 .

[34]  Pierre Legagneux,et al.  Achieving high-current carbon nanotube emitters. , 2005, Nano letters.

[35]  Erik Dujardin,et al.  WETTING OF SINGLE SHELL CARBON NANOTUBES , 1998 .

[36]  Krisztian Kordas,et al.  Chip cooling with integrated carbon nanotube microfin architectures , 2007 .

[37]  J. Robertson,et al.  Growth of ultrahigh density single-walled carbon nanotube forests by improved catalyst design. , 2012, ACS nano.

[38]  T. Ebbesen,et al.  Capillarity and Wetting of Carbon Nanotubes , 1994, Science.