Influence of Sugarcane Bagasse Ash and Silica Fume on the Mechanical and Durability Properties of Concrete

Cement production is environmentally unsustainable due to the high anthropogenic carbon emissions produced. Supplementary cementitious materials (SCMs), derived from the by-products of different industries, have been deemed an effective way to reduce carbon emissions. The reduction in carbon emissions is achieved by lowering the clinker factor of cement, through a partial replacement with an SCM. Sugarcane Bagasse Ash (SCBA) is produced as an agricultural waste from the sugarcane industry and has gained a lot of attention for being a feasible and readily available pozzolanic material, underutilised as an SCM. This study evaluates alkali-activated sugarcane bagasse ash’s mechanical and durability performance, at varied contents, in binary blended cement concrete and ternary blended cement concrete containing silica fume (SF). Potassium Hydroxide (KOH), used as the alkali activator, is intended to enhance the reactivity of the ash, with the possibility of a high-volume SCBA content. The mechanical performance was investigated by compressive and split tensile strength tests, and durability performance was investigated using the Oxygen Permeability Index (OPI) test. In addition, a micro-CT porosity test was conducted to assess how the microstructure and porosity of the concrete affect the mechanical and durability performance. The results indicated that using SCBA in a ternary blend with SF can significantly improve the overall performance and create less porous concrete. At 30% SCBA and 10% SF replacement, the performance tests revealed the highest mechanical strength and the lowest permeability, outperforming the control concrete and the binary blended cement concrete containing only SCBA.

[1]  B. Panda,et al.  Use of industrial waste materials for 3D printing of sustainable concrete: A review , 2022, Journal of Cleaner Production.

[2]  A. J. Babafemi,et al.  State-of-the-art review on the use of sugarcane bagasse ash in cementitious materials , 2021 .

[3]  Lochana Poudyal,et al.  Environmental sustainability in cement industry: An integrated approach for green and economical cement production , 2021, Resources, Environment and Sustainability.

[4]  K. O. Olusola,et al.  Blended cement binders containing bamboo leaf ash and ground clay brick waste for sustainable concrete , 2021 .

[5]  Sara Martins Torres,et al.  Assessing the pozzolanic activity of sugarcane bagasse ash using X-ray diffraction , 2020 .

[6]  P. Chindaprasirt,et al.  Heat evolution, strengths, and drying shrinkage of concrete containing high volume ground bagasse ash with different LOIs , 2020 .

[7]  P. Chindaprasirt,et al.  Mechanical properties, chloride resistance and microstructure of Portland fly ash cement concrete containing high volume bagasse ash , 2020 .

[8]  A. J. Babafemi,et al.  Performance of concrete containing Nigerian electric arc furnace steel slag aggregate towards sustainable production , 2020 .

[9]  V. Sairam,et al.  An overview of the influences of mechanical and chemical processing on sugarcane bagasse ash characterisation as a supplementary cementitious material , 2020 .

[10]  A. Bahurudeen,et al.  Sugarcane Bagasse Ash-Blended Concrete for Effective Resource Utilization Between Sugar and Construction Industries , 2020, Sugar Tech.

[11]  Mehmood Ali,et al.  Characterization of Sugarcane Bagasse Ash as Pozzolan and Influence on Concrete Properties , 2020 .

[12]  P. Awoyera,et al.  A critical review on application of alkali activated slag as a sustainable composite binder , 2019 .

[13]  Anton du Plessis,et al.  A review of X-ray computed tomography of concrete and asphalt construction materials , 2019, Construction and Building Materials.

[14]  K. Arunachalam,et al.  Durability characteristics of Ultra High Strength Concrete with treated sugarcane bagasse ash , 2018 .

[15]  Sabbie A. Miller Supplementary cementitious materials to mitigate greenhouse gas emissions from concrete: can there be too much of a good thing? , 2018 .

[16]  J. Monzó,et al.  Vegetable ashes as Supplementary Cementitious Materials , 2017, Cement and Concrete Research.

[17]  A. Ramezanianpour,et al.  A new approach for application of silica fume in concrete: Wet granulation , 2017 .

[18]  Vasudha D. Katare,et al.  Experimental characterization of sugarcane biomass ash – A review , 2017 .

[19]  Yufei Wu,et al.  Pozzolanic reaction of sugarcane bagasse ash and its role in controlling alkali silica reaction , 2017 .

[20]  S. Ferreiro,et al.  Influence of the Ca/Si ratio on the compressive strength of cementitious calcium–silicate–hydrate binders , 2017 .

[21]  G. C. Cordeiro,et al.  Effect of mechanical processing on sugar cane bagasse ash pozzolanicity , 2017 .

[22]  Chris Broeckhoven,et al.  Laboratory x-ray micro-computed tomography: a user guideline for biological samples , 2017, GigaScience.

[23]  L. M. Tavares,et al.  Improved pozzolanic activity of sugar cane bagasse ash by selective grinding and classification , 2016 .

[24]  C. Jaturapitakkul,et al.  Strength, chloride resistance, and expansion of concretes containing ground bagasse ash , 2015 .

[25]  R. Murugesan,et al.  Micro-analytical studies on sugar cane bagasse ash , 2015 .

[26]  Hans Beushausen,et al.  Oxygen permeability of concrete and its relation to carbonation , 2015 .

[27]  M. Santhanam,et al.  Performance evaluation of sugarcane bagasse ash blended cement in concrete , 2015 .

[28]  M. Santhanam,et al.  Influence of different processing methods on the pozzolanic performance of sugarcane bagasse ash , 2015 .

[29]  Lukman Ismail,et al.  Comparison of Using NaOH and KOH Activated Fly Ash-Based Geopolymer on the Mechanical Properties , 2014 .

[30]  M. S. Jaafar,et al.  The effect of various chemical activators on pozzolanic reactivity: A review , 2012 .

[31]  J. Bullard,et al.  Mechanisms of cement hydration , 2011 .

[32]  R. Siddique Utilization of silica fume in concrete: Review of hardened properties , 2011 .

[33]  Longtu Li,et al.  A review: The comparison between alkali-activated slag (Si + Ca) and metakaolin (Si + Al) cements , 2010 .

[34]  Almir Sales,et al.  Use of Brazilian sugarcane bagasse ash in concrete as sand replacement. , 2010, Waste management.

[35]  Renato Baciocchi,et al.  Storage of carbon dioxide captured in a pilot-scale biogas upgrading plant by accelerated carbonation of industrial residues , 2010 .

[36]  Eduardo de Moraes Rego Fairbairn,et al.  Effect of calcination temperature on the pozzolanic activity of sugar cane bagasse ash , 2009 .

[37]  K. Rajagopal,et al.  Evaluation of bagasse ash as supplementary cementitious material , 2007 .

[38]  M. Shannag,et al.  HIGH STRENGTH CONCRETE CONTAINING NATURAL POZZOLAN AND SILICA FUME , 2000 .

[39]  T. Naik CONCRETE DURABILITY AS INFLUENCED BY DENSITY AND/OR POROSITY , 1997 .

[40]  Ivan Odler,et al.  Investigations on the relationship between porosity structure and strength of hydrated portland cement pastes III. Effect of clinker composition and gypsum addition , 1987 .

[41]  I. Odler,et al.  Investigations on the relationship between porosity, structure and strength of hydrated portland cement pastes I. Effect of porosity , 1985 .