论文信息 - Determination of the thermodynamic properties of \{xMgO + (1 - x)MnO\} (s, sln) from a solid-electrolyte galvanic cell in the temperature range 1163 to 1318 K - 字舞流文

Determination of the thermodynamic properties of \{xMgO + (1 - x)MnO\} (s, sln) from a solid-electrolyte galvanic cell in the temperature range 1163 to 1318 K

G. Iyengar | K. Abraham | S. Raghavan

[1] B. Langanke,et al. Determination of the standard Gibbs free energies of formation of the silicates of cobalt, magnesium, and strontium by e.m.f. measurements , 1974 .

[2] W. Hahn,et al. Activities of the oxide components in NioMnOMgO solid solutions , 1970 .

[3] E. Woermann,et al. Derivation of approximate activity-composition relations in MgOMnO solid solutions , 1970 .

[4] A. Muan,et al. Activity-composition relations at 1100°C in the system calcium oxide-iron oxide-manganese oxide in contact with metallic iron , 1970 .

[5] R. W. Taylor,et al. The Free Energy of Formation of Some Titanates, Silicates, and Magnesium Aluminate from Measurements Made with Galvanic Cells Involving Solid Electrolytes , 1964 .

[6] C. Wagner,et al. THERMODYNAMICS OF THE SOLID SYSTEM CaO—SiO2 FROM ELECTROMOTIVE FORCE DATA , 1961 .

[7] S. Pizzini,et al. E.m.f. measurements with solid electrolyte galvanic cells on the calcium oxide + zirconia system. Determination of the phase relationships , 1972 .

[8] L. Orgel,et al. Electronic properties of transition-metal oxides-II: Cation distribution amongst octahedral and tetrahedral sites , 1957 .