스트론튬계 상전이물질의 혼입률에 따른 시멘트 복합체의 역학적 특성 평가

This paper describes experimental results on the seismic performance of SHCC (strain-hardening cement composite) infill wall for improving damage tolerance capacity of non-ductile frame. To investigate the effect of tensile strain capacity and cracking behavior of SHCC materials on the shear behavior of SHCC infill wall, three infill walls were fabricated and tested under cyclic loading. The test parameter in this study is a type of cement composites; concrete and SHCCs. The two types of SHCC materials were prepared for infill walls. In order to induce crack damages into the mid-span of the infill wall, each infill wall had two 100-mm-deep-notches on both sides. Test results indicated that SHCC infill walls showed superior crack control capacities and much larger drift ratios at the peak loads than RC (reinforced concrete) infill wall, as expected. In particular, due to the bridging actions of the reinforcing fibers, SHCC matrix used in this study would delay the stiffness degradation of infill wall after the first inclined cracking. Moreover, from the damage classes based on the cracks" maximum width in the infill walls, it was observed that PIW-SHD specimen possessed nearly threefold seismic capacities compared to PIW-SLD specimen. Also, from the results on the strain of diagonal reinforcements, it can be concluded that the SHCC matrix would resist a part of tensile stresses transferred along steel rebar in the infill wall.