Experimental fabrication and characterization of out-of-plane fiber waviness in continuous fiber-reinforced composites

This study presents the development of fabrication techniques and experimental measurements of out-of-plane fiber waviness in a continuous fiber-reinforced polymer composite. Literature on characterization and fabrication techniques was briefly reviewed. Three fabrication methods were developed: the transverse-strip method, ply-drop method, and constant-thickness ply-drop method. Experimental characterization demonstrated that specimens with a range of waviness parameters can be easily manufactured. The most important features of the techniques are ease of fabrication and simplicity of experimental setup. An industrial part was characterized optically to validate the techniques, showing a maximum misalignment angle of 5.3°.

[1]  K. Potter,et al.  UNDERSTANDING THE ORIGINS OF DEFECTS AND VARIABILITY IN COMPOSITES MANUFACTURE , 2009 .

[2]  Robert A Smith,et al.  Automated analysis and advanced defect characterisation from ultrasonic scans of composites , 2009 .

[3]  Mpf Sutcliffe,et al.  A multiple field image analysis procedure for characterisation of fibre alignment in composites , 2001 .

[4]  Robert F. Anastasi,et al.  Investigation of fiber waviness in a thick glass composite beam using THz NDE , 2008, SPIE Smart Structures and Materials + Nondestructive Evaluation and Health Monitoring.

[5]  A. Wronski,et al.  Compressive failure and kinking in uniaxially aligned glass-resin composite under superposed hydrostatic pressure , 1982 .

[6]  Ole Thybo Thomsen,et al.  A Novel Image Analysis Procedure for Measuring Fibre Misalignment in Unidirectional Fibre Composites , 2009 .

[7]  S. W. Yurgartis.  Measurement of small angle fiber misalignments in continuous fiber composites , 1987 .

[8]  M. Piggott,et al.  Compressive properties of unidirectional carbon fibre laminates: II. The effects of unintentional and intentional fibre misalignments , 1993 .

[9]  M. Hyer,et al.  Effects of Layer Waviness on the Compression Strength of Thermoplastic Composite Laminates , 1993 .

[10]  K. Potter,et al.  Simulation of process induced defects in resin transfer moulded woven carbon fibre laminates and their effect on mechanical behaviour , 2006 .

[11]  Daniel O. Adams,et al.  Compression strength reductions in composite laminates due to multiple-layer waviness , 1995 .

[12]  A Caiazzo,et al.  The Effects of Marcel Defects on Composite Structural Properties , 2001 .

[13]  Chen-Ming Kuo,et al.  Effect of Fiber Waviness on the Nonlinear Elastic Behavior of Flexible Composites , 1988 .

[14]  Bernard Budiansky,et al.  Mechanics of materials and material characterizationMicromechanics , 1983 .

[15]  A. S. Argon,et al.  Fracture of Composites , 1972 .

[16]  M. Wisnom,et al.  Compressive Failure Due to Shear Instability: Experimental Investigation of Waviness and Correlation with Analysis , 1996 .

[17]  Christian Germain,et al.  Microstructure reconstruction of fibrous C/C composites from X-ray microtomography , 2007 .

[18]  Paul M. Weaver,et al.  A concept for the generation of out-of-plane distortion from tailored FRP laminates , 2004 .

[19]  N. C. Davidson,et al.  A novel technique for determining the 3D spatial distribution of glass fibres in polymer composites , 1995 .

[20]  J. Crookston.  Prediction of elastic behaviour and initial failure of textile composites , 2004 .

[21]  Sumit Sharma.  Micromechanics , 1965, Nature.

[22]  S. Fakirov,et al.  Direct determination of the orientation of short glass fibers in an injection-molded poly (ethylene terephthalate) system , 1985 .

[23]  Isaac M Daniel,et al.  EFFECT OF FIBER WAVINESS ON STIFFNESS AND STRENGTH REDUCTION OF UNIDIRECTIONAL COMPOSITES UNDER COMPRESSIVE LOADING , 1996 .

[24]  B. Harris,et al.  The compression strength of composites with kinked, misaligned and poorly adhering fibres , 1981 .

[25]  M. R. Piggott.  A theoretical framework for the compressive properties of aligned fibre composites , 1981 .