Direct 3D powder printing of biphasic calcium phosphate scaffolds for substitution of complex bone defects

The 3D printing technique based on cement powders is an excellent method for the fabrication of individual and complex bone substitutes even in the case of large defects. The outstanding bone remodeling capacity of biphasic calcium phosphates (BCPs) containing hydroxyapatite (HA) as well as tricalcium phosphate (TCP) in varying ratios makes the adaption of powder systems resulting in BCP materials to this fabrication technique a desirable aim. This study presents the synthesis and characterization of a novel powder system for the 3D printing process, intended for the production of complexly shaped BCP scaffolds by a hydraulic setting reaction of calcium carbonate and TCP with phosphoric acid. The HA/TCP ratio in the specimens could be tailored by the calcium/phosphate ratio of the starting powder. The scaffolds could be fabricated with a dimensional accuracy of >96.5% and a minimal macro pore size of 300 µm. Independent of the phase composition the printed specimens showed a microporosity of approximately 68%, while the compressive strength strongly depended on the chemical composition and increased with rising TCP content in the scaffolds to a maximum of 1.81 MPa. Post-treatment of the scaffolds with a polylactic-co-glycolic acid-solution enhanced the mechanical properties by a factor of 8. In vitro studies showed that all BCP scaffolds were cytocompatible and enhanced the cell viability as well as the cell proliferation, as compared with pure TCP. Cell proliferation is even better on BCP when compared to HA and cell viability is in a similar range on these materials.

[1]  M. van der Elst,et al.  Bone tissue response to biodegradable polymers used for intra medullary fracture fixation: a long-term in vivo study in sheep femora. , 1999, Biomaterials.

[2]  Yong Han,et al.  The in situ synthesis of biphasic calcium phosphate scaffolds with controllable compositions, structures, and adjustable properties. , 2009, Journal of biomedical materials research. Part A.

[3]  Julia Will,et al.  Porous ceramic bone scaffolds for vascularized bone tissue regeneration , 2008, Journal of materials science. Materials in medicine.

[4]  W. Hayes,et al.  The compressive behavior of bone as a two-phase porous structure. , 1977, The Journal of bone and joint surgery. American volume.

[5]  Huan Zhou,et al.  Fabrication aspects of PLA-CaP/PLGA-CaP composites for orthopedic applications: a review. , 2012, Acta biomaterialia.

[6]  H. Seitz,et al.  Three-dimensional printing of porous ceramic scaffolds for bone tissue engineering. , 2005, Journal of biomedical materials research. Part B, Applied biomaterials.

[7]  J. Planell,et al.  Hydroxyapatite ceramic bodies with tailored mechanical properties for different applications. , 2002, Journal of biomedical materials research.

[8]  Gabriele Grimm,et al.  Development of a new calcium phosphate powder-binder system for the 3D printing of patient specific implants , 2007, Journal of materials science. Materials in medicine.

[9]  J. P. LeGeros,et al.  Biphasic calcium phosphate bioceramics: preparation, properties and applications , 2003, Journal of materials science. Materials in medicine.

[10]  M. Fukushima,et al.  Fabrication of highly porous nickel with oriented micrometer-sized cylindrical pores by gelation freezing method , 2015 .

[11]  M. Viceconti,et al.  Compressive behaviour of child and adult cortical bone. , 2011, Bone.

[12]  Seong-Ho Choi,et al.  Comparative evaluation of three calcium phosphate synthetic block bone graft materials for bone regeneration in rabbit calvaria. , 2012, Journal of biomedical materials research. Part B, Applied biomaterials.

[13]  A. Mikos,et al.  In vitro degradation of thin poly(DL-lactic-co-glycolic acid) films. , 1999, Journal of biomedical materials research.

[14]  Hermann Seitz,et al.  In vitro -Osteoclastic Activity Studies on Surfaces of 3D Printed Calcium Phosphate Scaffolds , 2011, Journal of biomaterials applications.

[15]  V. Mooney,et al.  Comparative study of porous hydroxyapatite and tricalcium phosphate as bone substitute , 1985, Journal of orthopaedic research : official publication of the Orthopaedic Research Society.

[16]  R. Legeros,et al.  Properties of osteoconductive biomaterials: calcium phosphates. , 2002, Clinical orthopaedics and related research.

[17]  R. Detsch,et al.  Indirect rapid prototyping of biphasic calcium phosphate scaffolds as bone substitutes: influence of phase composition, macroporosity and pore geometry on mechanical properties , 2010, Journal of materials science. Materials in medicine.

[18]  R. Holmes,et al.  Porous hydroxyapatite as a bone-graft substitute in metaphyseal defects. A histometric study. , 1986, The Journal of bone and joint surgery. American volume.

[19]  M Bohner,et al.  Moisture based three-dimensional printing of calcium phosphate structures for scaffold engineering. , 2013, Acta biomaterialia.

[20]  Amit Bandyopadhyay,et al.  Recent advances in bone tissue engineering scaffolds. , 2012, Trends in biotechnology.

[21]  D S Metsger,et al.  Mechanical properties of sintered hydroxyapatite and tricalcium phosphate ceramic. , 1999, Journal of materials science. Materials in medicine.

[22]  J. Chevalier,et al.  Mechanical properties and cytocompatibility of poly(ε-caprolactone)-infiltrated biphasic calcium phosphate scaffolds with bimodal pore distribution. , 2010, Acta biomaterialia.

[23]  Amit Bandyopadhyay,et al.  Microwave-processed nanocrystalline hydroxyapatite: simultaneous enhancement of mechanical and biological properties. , 2010, Acta biomaterialia.

[24]  R. Ritchie.  Mechanisms of fatigue-crack propagation in ductile and brittle solids , 1999 .

[25]  Adam J. Stevenson,et al.  Strong, tough and stiff bioinspired ceramics from brittle constituents. , 2014, Nature materials.

[26]  L. Grover,et al.  Structural changes to resorbable calcium phosphate bioceramic aged in vitro. , 2013, Colloids and Surfaces B: Biointerfaces.

[27]  Shigeki Matsuya,et al.  Fabrication of freeform bone-filling calcium phosphate ceramics by gypsum 3D printing method. , 2009, Journal of biomedical materials research. Part B, Applied biomaterials.

[28]  J MEAD,et al.  Mechanical properties of lungs. , 1961, Physiological reviews.

[29]  L. Grover,et al.  Preparation of tricalcium phosphate/calcium pyrophosphate structures via rapid prototyping , 2008, Journal of materials science. Materials in medicine.

[30]  M Epple,et al.  A thorough physicochemical characterisation of 14 calcium phosphate-based bone substitution materials in comparison to natural bone. , 2004, Biomaterials.

[31]  Jian Li,et al.  Mechanical and Biological Properties of Hydroxyapatite/tricalcium Phosphate Scaffolds Coated with Poly(lactic-co-glycolic Acid) , 2007 .

[32]  P. Ma,et al.  Porous poly(L-lactic acid)/apatite composites created by biomimetic process. , 1999, Journal of biomedical materials research.

[33]  Uwe Gbureck,et al.  Antimicrobial titanium/silver PVD coatings on titanium , 2006, Biomedical engineering online.

[34]  Y. Carvalho,et al.  Porous titanium scaffolds produced by powder metallurgy for biomedical applications , 2008 .

[35]  D. Dunand,et al.  Mechanical properties of directionally freeze-cast titanium foams , 2011 .

[36]  Jorge Rodrigues,et al.  Structural evaluation of scaffolds prototypes produced by three-dimensional printing , 2011 .

[37]  A. Wennerberg,et al.  Bone ingrowth of various porous titanium scaffolds produced by a moldless and space holder technique: an in vivo study in rabbits , 2016, Biomedical materials.

[38]  Amy J Wagoner Johnson,et al.  A review of the mechanical behavior of CaP and CaP/polymer composites for applications in bone replacement and repair. , 2011, Acta biomaterialia.

[39]  Kriskrai Sitthiseripratip,et al.  3D printing of hydroxyapatite: Effect of binder concentration in pre-coated particle on part strength , 2007 .

[40]  B D Boyan,et al.  Role of material surfaces in regulating bone and cartilage cell response. , 1996, Biomaterials.

[41]  Y. M. Lee,et al.  The bone regenerative effect of platelet-derived growth factor-BB delivered with a chitosan/tricalcium phosphate sponge carrier. , 2000, Journal of periodontology.

[42]  Jake E. Barralet,et al.  3D Powder Printing of β‐Tricalcium Phosphate Ceramics Using Different Strategies , 2008 .

[43]  A. Bandyopadhyay,et al.  Effect of grain size on mechanical, surface and biological properties of microwave sintered hydroxyapatite. , 2013, Materials science & engineering. C, Materials for biological applications.

[44]  A. Roosen,et al.  Quantitative Analysis of Crystalline and Amorphous Phases in Glass–Ceramic Composites Like LTCC by the Rietveld Method , 2006 .

[45]  D. Dunand,et al.  Directionally freeze-cast titanium foam with aligned, elongated pores , 2008 .

[46]  G. Daculsi,et al.  Elaboration conditions influence physicochemical properties and in vivo bioactivity of macroporous biphasic calcium phosphate ceramics , 1999, Journal of materials science. Materials in medicine.

[47]  Y. Carvalho,et al.  Novel production method of porous surface Ti samples for biomedical application , 2012, Journal of Materials Science: Materials in Medicine.

[48]  J. Weng,et al.  Improving mechanical and biological properties of macroporous HA scaffolds through composite coatings. , 2009, Colloids and surfaces. B, Biointerfaces.

[49]  J. L. Ackerman,et al.  Porous block hydroxyapatite in orthognathic surgery. , 1991, The Angle orthodontist.

[50]  Yunqing Kang,et al.  Enhanced mechanical performance and biological evaluation of a PLGA coated β-TCP composite scaffold for load-bearing applications. , 2011, European polymer journal.

[51]  Hyoun‐Ee Kim,et al.  Dynamic freeze casting for the production of porous titanium (Ti) scaffolds. , 2013, Materials science & engineering. C, Materials for biological applications.

[52]  Z. Zyman,et al.  Preparation and characterization of biphasic calcium phosphate ceramics of desired composition , 2008, Journal of materials science. Materials in medicine.

[53]  Jiandong Ye,et al.  Alginate/poly (lactic-co-glycolic acid)/calcium phosphate cement scaffold with oriented pore structure for bone tissue engineering. , 2009, Journal of biomedical materials research. Part A.

[54]  C. Wen,et al.  Bone formation following implantation of titanium sponge rods into humeral osteotomies in dogs: a histological and histometrical study. , 2010, Clinical implant dentistry and related research.

[55]  E. Toyserkani,et al.  Solid freeform fabrication and characterization of porous calcium polyphosphate structures for tissue engineering purposes. , 2010, Journal of biomedical materials research. Part B, Applied biomaterials.

[56]  U Gbureck,et al.  Hydraulic setting Mg3(PO4)2 powders for 3D printing technology , 2011 .

[57]  M. Cima,et al.  Mechanical properties of dense polylactic acid structures fabricated by three dimensional printing. , 1996, Journal of biomaterials science. Polymer edition.

[58]  Clemens A van Blitterswijk,et al.  Osteoconduction and osteoinduction of low-temperature 3D printed bioceramic implants. , 2008, Biomaterials.

[59]  R. Pilliar.  Powder metal-made orthopedic implants with porous surface for fixation by tissue ingrowth. , 1983, Clinical orthopaedics and related research.

[60]  G. Daculsi,et al.  A comparative study of biphasic calcium phosphate ceramics for human mesenchymal stem-cell-induced bone formation. , 2005, Biomaterials.

[61]  S. Komarova,et al.  Perfluorodecalin and bone regeneration. , 2013, European cells & materials.

[62]  Steve Weiner,et al.  THE MATERIAL BONE: Structure-Mechanical Function Relations , 1998 .

[63]  Sylvain Deville,et al.  Freeze-Casting of Porous Ceramics: A Review of Current Achievements and Issues , 2008, 1710.04201.

[64]  Frank A. Müller,et al.  Resorbable Dicalcium Phosphate Bone Substitutes Prepared by 3D Powder Printing , 2007 .

[65]  S. Dorozhkin,et al.  Biphasic, triphasic and multiphasic calcium orthophosphates. , 2012, Acta biomaterialia.

[66]  K. Leong,et al.  Solid freeform fabrication of three-dimensional scaffolds for engineering replacement tissues and organs. , 2003, Biomaterials.

[67]  Donald R. Ulrich,et al.  Chemical Processing of Ceramics , 1990 .

[68]  G. Hannink,et al.  Bioresorbability, porosity and mechanical strength of bone substitutes: what is optimal for bone regeneration? , 2011, Injury.

[69]  J. M. Kumar,et al.  Evaluation of nano-biphasic calcium phosphate ceramics for bone tissue engineering applications: In vitro and preliminary in vivo studies , 2013, Journal of biomaterials applications.

[70]  M. Vallet‐Regí,et al.  In vitro structural changes in porous HA/beta-TCP scaffolds in simulated body fluid. , 2009, Acta biomaterialia.

[71]  Fupo He,et al.  In vitro degradation, biocompatibility, and in vivo osteogenesis of poly(lactic-co-glycolic acid)/calcium phosphate cement scaffold with unidirectional lamellar pore structure. , 2012, Journal of biomedical materials research. Part A.

[72]  Hermann Seitz,et al.  Different Calcium Phosphate Granules for 3‐D Printing of Bone Tissue Engineering Scaffolds , 2009 .

[73]  D. Kaplan,et al.  Porosity of 3D biomaterial scaffolds and osteogenesis. , 2005, Biomaterials.

[74]  G. Daculsi,et al.  Calcium phosphate scaffold and bone marrow for bone reconstruction in irradiated area: a dog study. , 2005, Bone.

[75]  R. Delgado-Ruiz,et al.  Histomorphometric and mineral degradation study of Ossceram: a novel biphasic B-tricalcium phosphate, in critical size defects in rabbits. , 2012, Clinical oral implants research.

[76]  K. Hing.  Bone repair in the twenty–first century: biology, chemistry or engineering? , 2004, Philosophical Transactions of the Royal Society of London. Series A: Mathematical, Physical and Engineering Sciences.

[77]  D. Bartlett,et al.  Surface texture measurement for dental wear applications , 2015 .

[78]  J. Sawai.  Quantitative evaluation of antibacterial activities of metallic oxide powders (ZnO, MgO and CaO) by conductimetric assay. , 2003, Journal of microbiological methods.

[79]  Peter Greil,et al.  Osteoinduction and survival of osteoblasts and bone-marrow stromal cells in 3D biphasic calcium phosphate scaffolds under static and dynamic culture conditions , 2012, Journal of cellular and molecular medicine.

[80]  L. Grover,et al.  Comparing physicochemical properties of printed and hand cast biocements designed for ligament replacement , 2011 .

[81]  S. Putic,et al.  Microwave sintering improves the mechanical properties of biphasic calcium phosphates from hydroxyapatite microspheres produced from hydrothermal processing , 2010 .

[82]  D. Seo,et al.  Dissolution of Calcium Phosphate Powders with Different Compositions in Simulated Body Fluid , 2007 .

[83]  T. Arinzeh,et al.  Biphasic Calcium Phosphate Ceramics for Bone Regeneration and Tissue Engineering Applications , 2010, Materials.

[84]  Miguel Castilho,et al.  Fabrication of computationally designed scaffolds by low temperature 3D printing , 2013, Biofabrication.

[85]  Hyoun‐Ee Kim,et al.  Reverse freeze casting: a new method for fabricating highly porous titanium scaffolds with aligned large pores. , 2012, Acta biomaterialia.

[86]  P. Voorhees,et al.  Morphological analysis of pores in directionally freeze-cast titanium foams , 2009 .

[87]  B. Su,et al.  Tailored graded pore structure in zirconia toughened alumina ceramics using double-side cooling freeze casting , 2012 .

[88]  R. Detsch,et al.  Influence of Phase Composition on Degradation and Resorption of Biphasic Calcium Phosphate Ceramics , 2007 .

[89]  Uwe Gbureck,et al.  Low temperature fabrication of magnesium phosphate cement scaffolds by 3D powder printing , 2010, Journal of materials science. Materials in medicine.