Temperature and ion irradiation dependence of magnetic domains and microstructure in Co/Pt multilayers

Microstructure and magnetic properties of Co/Pt multilayers with perpendicular anisotropy were studied as a function of growth temperature (TG) and ion irradiation. With increased TG, larger columnar grain size and an improved 〈111〉 texture were observed. Up to a critical temperature (Tcrit), a monotonic increase in coercivity (HC) with TG was measured, followed by a decrease in HC with further increase in TG. Magnetic domains of films grown below Tcrit were irregular, with their submicron size decreasing gradually with increasing TG. Films grown at 390 °C>Tcrit had fine domains on the sub-100 nm length scale. Both HC and domain size were reduced after the multilayers were exposed.

[1]  B. Terris,et al.  Magnetic imaging of ion-irradiation patterned Co/Pt multilayers using complementary electron and photon probes , 2001 .

[2]  D. Attwood,et al.  A full field transmission X-ray microscope as a tool for high-resolution magnetic imaging , 2001 .

[3]  E. Fullerton,et al.  Growth, structural, and magnetic properties of high coercivity Co/Pt multilayers , 2001 .

[4]  K. Krishnan,et al.  Domain structures and temperature-dependent spin reorientation transitions in c-axis oriented Co–Cr thin films , 2000 .

[5]  Margaret Evans Best,et al.  Ion induced magnetization reorientation in Co/Pt multilayers for patterned media , 2000 .

[6]  Peter Vettiger,et al.  Ion-beam patterning of magnetic films using stencil masks , 1999 .

[7]  T. Devolder,et al.  SUB-50 NM PLANAR MAGNETIC NANOSTRUCTURES FABRICATED BY ION IRRADIATION , 1999 .

[8]  T. Devolder,et al.  Planar patterned magnetic media obtained by ion irradiation , 1998, Science.

[9]  P. Fischer,et al.  Imaging of magnetic domains with the X-ray microscope at BESSY using X-ray magnetic circular dichroism , 1997 .

[10]  S. Shiomi,et al.  Dependence of Magnetic Properties of Co/Pt Multilayers on Deposition Temperature of Pt Buffer Layers , 1993 .

[11]  P. Carcia,et al.  Co thickness dependence of the microstructure of Pt/Co multilayers , 1993 .

[12]  P. Carcia.  Perpendicular magnetic anisotropy in Pd/Co and Pt/Co thin‐film layered structures , 1988 .

[13]  Roger Wood,et al.  The feasibility of magnetic recording at 1 Terabit per square inch , 2000 .

[14]  David B. Williams,et al.  Transmission Electron Microscopy: A Textbook for Materials Science , 1996 .

[15]  R. Farrow,et al.  Interface and Volume Anisotropy of MBE-Grown Co/Pt (111), (110) and (001) and Sputtered CO/Pt Multilayers , 1993 .