Scaling Effects in Notched Composites

A program of scaled tests on unnotched and open-hole tension and compression specimens is summarized. Quasi-isotropic IM7/8552 carbon-fiber epoxy specimens have been tested using two different scaling techniques: sub-laminate-level ([45/90/ - 45/0]ns) and ply-level scaling ([45n/90 n/ - 45n/0n]s), independently varying the thickness and in-plane dimensions. Significant scaling effects are shown, with both strength and failure mechanisms changing with specimen size and the thickness scaling method having a particularly important effect. Failure mechanisms and scaling behavior are compared between tension and compression and models presented that predict the observed size effects from fundamental material parameters without any fitting factors.

[1]  Michael R Wisnom,et al.  A concise interface constitutive law for analysis of delamination and splitting in composite materials and its application to scaled notched tensile specimens , 2007 .

[2]  Isaac M Daniel,et al.  Is there a thickness effect on compressive strength of unnotched composite laminates? , 1999 .

[3]  Constantinos Soutis,et al.  Measuring the notched compressive strength of composite laminates : Specimen size effects , 2008 .

[4]  M. Wisnom,et al.  Reduction in compressive strain to failure with increasing specimen size in pin-ended buckling tests , 1997 .

[5]  Michael R Wisnom,et al.  The Effect of Stacking Sequence on Thickness Scaling of Tests on Open Hole Tensile Composite Specimens , 2007 .

[6]  Fu-Kuo Chang,et al.  Damage Tolerance of Laminated Composites Containing an Open Hole and Subjected to Tensile Loadings , 1991 .

[7]  Constantinos Soutis,et al.  Thickness effect on the compressive strength of T800/924C carbon fibre-epoxy laminates , 2005 .

[8]  Michael R Wisnom,et al.  The role of delamination in strength, failure mechanism and hole size effect in open hole tensile tests on quasi-isotropic laminates , 2009 .

[9]  Costas Soutis,et al.  Strain energy release rate associated with local delamination in cracked composite laminates , 1994 .

[10]  Paul A. Lagace,et al.  Notch Sensitivity and Stacking Sequence of Laminated Composites , 1986 .

[11]  Norman A. Fleck,et al.  Failure Prediction Technique for Compression Loaded Carbon Fibre-Epoxy Laminate with Open Holes , 1991 .

[12]  Maria Kashtalyan,et al.  Strain Energy Release Rate for Off-Axis Ply Cracking in Laminated Composites , 2001 .

[13]  Michael R Wisnom,et al.  Full-field assessment of the damage process of laminated composite open-hole tensile specimens. Part II: experimental results , 2007 .

[14]  Zdeněk P. Bažant,et al.  Size effect on compression strength of fiber composites failing by kink band propagation , 1999 .

[15]  John W. Gillespie,et al.  Notched Strength of Composite Materials , 1979 .

[16]  Jonathan Awerbuch,et al.  Notched Strength of Composite Laminates: Predictions and Experiments—A Review , 1985 .

[17]  Michael R Wisnom,et al.  Effect of Stacking Sequence on Open-Hole Tensile Strength of Composite Laminates , 2009 .

[18]  Michael R Wisnom,et al.  Size effects in the testing of fibre-composite materials , 1999 .

[19]  Constantinos Soutis,et al.  A method for predicting the fracture toughness of CFRP laminates failing by fibre microbuckling , 2000 .

[20]  John Morton,et al.  Apparent strength scaling in continuous fiber composite laminates , 2000 .

[21]  Maria Kashtalyan,et al.  Analysis of composite laminates with intra- and interlaminar damage , 2005 .

[22]  Michael R Wisnom,et al.  An experimental investigation into the tensile strength scaling of notched composites , 2007 .

[23]  Constantinos Soutis,et al.  Size effect on compressive strength of T300/924C carbon fibre-epoxy laminates , 2002 .

[24]  Wisnom,et al.  Specimen size effects on the notched strength of composite laminates loaded in tension , 2007 .

[25]  Michael R Wisnom,et al.  An experimental and numerical investigation into the damage mechanisms in notched composites , 2009 .

[26]  Constantinos Soutis,et al.  A study on the compressive strength of thick carbon fibre-epoxy laminates , 2007 .

[27]  Michael R Wisnom,et al.  Reduction in tensile and flexural strength of unidirectional glass fibre-epoxy with increasing specimen size , 1997 .

[28]  Zdenek P. Bazant,et al.  Size Effect and Fracture Characteristics of Composite Laminates , 1996 .

[29]  J. Whitney,et al.  Stress Fracture Criteria for Laminated Composites Containing Stress Concentrations , 1974 .

[30]  M. Wisnom,et al.  Size effects in unnotched tensile strength of unidirectional and quasi-isotropic carbon/epoxy composites , 2008 .

[31]  C. Sun,et al.  Effect of Ply Thickness on Fracture of Notched Composite Laminates , 1998 .

[32]  John Morton,et al.  Scale Effects in the Response and Failure of Fiber Reinforced Composite Laminates Loaded in Tension and in Flexure , 1992 .

[33]  Carl-Gustaf Aronsson,et al.  Strength of Tensile Loaded Graphite/Epoxy Laminates Containing Cracks, Open and Filled Holes , 1990 .

[34]  J. Eisenmann,et al.  Macroscopic Fracture Mechanics of Advanced Composite Materials , 1971 .

[35]  Open-hole tensile strength of quasi-isotropic laminates , 2000 .