Synthesis, physical characterization, and biological performance of sequential homointerpenetrating polymer network sponges based on poly(2-hydroxyethyl methacrylate).

A limitation in the use of hydrophilic poly(2-hydroxyethyl methacrylate) (PHEMA) sponges as implantable devices is their inherently poor mechanical strength. This precludes proper surgical manipulation, especially in the eye where the size of the implant is usually small. In this study a new method was developed to produce mechanically stronger PHEMA sponges. Sequential homointerpenetrating polymer network (homo-IPN) sponges were made by using HEMA as the precursor for generating both the first network and the successive interpenetrated networks. Following the formation of network I, the sponge was squeezed to remove the interstitial water, soaked in the second monomer (also HEMA), and squeezed again to remove the excess monomer from the pores before being subjected to the second polymerization leading to the formation of network II. Two two-component IPN sponges (K2 and K4) with increasing HEMA content in the network II and a three-component IPN sponge (K3) were produced, and their properties were compared to those of a homopolymer PHEMA sponge (control). Apart from elongation, the tensile properties were all significantly enhanced in the IPN sponges; the water content was the same as in the control sponge, except for sponge K4, which was lower. Light microscopy revealed similar pore morphologies of the control and IPN sponges K2 and K3, and the majority of the pores were around 25 microm. Sponge K4 displayed smaller pores of around 10 microm. Cellular invasion into the sponges was examined in vitro (incubation with 3T3 fibroblasts) and in vivo (implantation in rabbit corneas). Although the in vitro assay detected a change in the cell behavior in the early stage of invasion, which was probably due to the formation of IPNs, such changes were not reflected in the longer term in vivo experiment. There was a proper integration of sponges K2 and K3 with the corneal stroma, but much less cellular invasion and no neovascularization in sponge K4. We concluded that IPN formation is a valid method to enhance the strength of PHEMA sponges, provided that the content of HEMA in the successive networks is not too high.

[1]  M. Watsky.  Keratocyte gap junctional communication in normal and wounded rabbit corneas and human corneas. , 1995, Investigative ophthalmology & visual science.

[2]  I. Constable,et al.  Histologic Evaluation During Healing of Hydrogel Core‐and-Skirt Keratoprostheses in the Rabbit Eye , 1997, Cornea.

[3]  P. Dalton,et al.  Hydrophilic sponges based on 2-hydroxyethyl methacrylate. III. Effect of incorporating a hydrophilic crosslinking agent on the equilibrium water content and pore structure , 1997 .

[4]  P. Bartl,et al.  Water-soluble methacrylate as an embedding medium for the preparation of ultrathin sections. , 1960, Journal of ultrastructure research.

[5]  I. Constable,et al.  Preliminary evaluation of a hydrogel core-and-skirt keratoprosthesis in the rabbit cornea. , 1996, Journal of refractive surgery.

[6]  J. Calnan,et al.  Clinical and experimental studies of polyhydroxyethylmethacrylate gel ("Hydron") for reconstructive surgery. , 1971, British journal of plastic surgery.

[7]  Z Voldrich,et al.  Long-term experience with poly(glycol monomethacrylate) gel in plastic operations of the nose. , 1975, Journal of biomedical materials research.

[8]  S. J. Huang,et al.  Hydrophilic—Hydrophobic Interpenetrating Polymer Networks and Semi-interpenetrating Polymer Networks , 1994 .

[9]  K. Povodator,et al.  Evidence for a micro-mesomorphic structure in poly (2-hydroxyethyl methacrylate) hydrogels , 1970 .

[10]  H. Xie,et al.  Castor Oil Polyurethane—Acrylic or Vinyl Polymer Interpenetrating Polymer Networks Cured at Room Temperature , 1994 .

[11]  M. Kon,et al.  A Poly (HEMA) Sponge for Restoration of Articular Cartilage Defects , 1981, Plastic and reconstructive surgery.

[12]  T. Chirila,et al.  Enhancement of mechanical strength of poly(2-hydroxyethyl methacrylate) sponges. , 1995, Journal of biomedical materials research.

[13]  I. Constable,et al.  Interpenetrating polymer network (IPN) as a permanent joint between the elements of a new type of artificial cornea. , 1994, Journal of biomedical materials research.

[14]  Usman Sorathia,et al.  Interpenetrating Polymer Networks: An Overview , 1990 .

[15]  Simpson Bj.  Hydron: a hydrophilic polymer. , 1969 .

[16]  R. A. Haldon,et al.  Structure and permeability of porous films of poly(hydroxy ethyl methacrylate) , 1972 .

[17]  W. Stone,et al.  Hydrogels of poly(hydroxyethyl methacrylate) and hydroxyethyl methacrylate—glycerol monomethacry‐late copolymers , 1966 .

[18]  I. Constable,et al.  Keratoprosthesis: preliminary results of an artificial corneal button as a full-thickness implant in the rabbit model. , 1996, Australian and New Zealand journal of ophthalmology.

[19]  J. Steer,et al.  The modulation of cellular responses to poly(2-hydroxyethyl methacrylate) hydrogel surfaces: phosphorylation decreases macrophage collagenase production in vitro. , 1998, Journal of biomaterials science. Polymer edition.

[20]  Ian Constable,et al.  Hydrophilic sponges based on 2−hydroxyethyl methacrylate. I: Effect of monomer mixture composition on the pore size , 1993 .

[21]  I J Constable,et al.  Poly(2-hydroxyethyl methacrylate) sponges as implant materials: in vivo and in vitro evaluation of cellular invasion. , 1993, Biomaterials.

[22]  W. Prins,et al.  Polymer-Diluent Interaction in Cross-Linked Gels of Poly(2-hydroxyethyl methacrylate) , 1972 .

[23]  I. Constable,et al.  Clinical results of implantation of the Chirila keratoprosthesis in rabbits , 1998, The British journal of ophthalmology.

[24]  I J Constable,et al.  Tissue Interaction with Hydrogel Sponges Implanted in the Rabbit Cornea , 1993, Cornea.

[25]  B. Stockar,et al.  Use of spongy hydron in plastic surgery. , 1968, Journal of biomedical materials research.

[26]  X. Lou,et al.  Hydrophilic sponges based on 2‐hydroxyethyl methacrylate. V. effect of crosslinking agent reactivity on mechanical properties , 1997 .

[27]  X. Lou,et al.  Hydrophilic Sponges Based on 2-Hydroxyethyl Methacrylate. IV. Novel Synthetic Routes to Hydroxyl-Containing Crosslinking Agents and Their Effect on the Mechanical Strength of Sponges , 1997 .

[28]  B. Tighe,et al.  Macroporous hydrogels for biomedical applications: methodology and morphology. , 1993, Biomaterials.