Mesocellular polymer foams with unprecedented uniform large mesopores and high surface areas.

Mesocellular polymer foams with uniform approximately 17 nm cellular pores were fabricated using mesocellular silica foams as inorganic templates. The mesocellular polymer foams have high surface areas up to approximately 600 m(2)g(-1) and pore volumes of 1.6 cm(3)g(-1).

[1]  Jong‐Sung Yu,et al.  Synthesis of highly ordered mesoporous polymer networks , 2001 .

[2]  T. Kyotani,et al.  Very High Surface Area Microporous Carbon with a Three-Dimensional Nano-Array Structure: Synthesis and Its Molecular Structure , 2001 .

[3]  Juhyoun Kwak,et al.  Ordered nanoporous arrays of carbon supporting high dispersions of platinum nanoparticles , 2001, Nature.

[4]  P. Davidson,et al.  Existence of a Microporous Corona around the Mesopores of Silica-Based SBA-15 Materials Templated by Triblock Copolymers , 2000 .

[5]  T. Hyeon,et al.  Fabrication of New Nanoporous Carbons through Silica Templates and Their Application to the Adsorption of Bulky Dyes , 2000 .

[6]  Dongyuan Zhao,et al.  Hexagonal to Mesocellular Foam Phase Transition in Polymer-Templated Mesoporous Silicas , 2000 .

[7]  Taeghwan Hyeon,et al.  Electric double-layer capacitor performance of a new mesoporous carbon , 2000 .

[8]  M. Jaroniec,et al.  Characterization of the Porous Structure of SBA-15 , 2000 .

[9]  Seung M. Oh,et al.  Development of a New Mesoporous Carbon Using an HMS Aluminosilicate Template , 2000 .

[10]  G. Stucky,et al.  Microemulsion Templating of Siliceous Mesostructured Cellular Foams with Well-Defined Ultralarge Mesopores , 2000 .

[11]  Kageyama,et al.  Extrusion polymerization: catalyzed synthesis of crystalline linear polyethylene nanofibers within a mesoporous silica , 1999, Science.

[12]  Sang Hoon Joo,et al.  Synthesis of highly ordered carbon molecular sieves via template-mediated structural transformation , 1999 .

[13]  P. J. Ollivier,et al.  Ordered mesoporous polymers of tunable pore size from colloidal silica templates. , 1999, Science.

[14]  Baughman,et al.  Carbon structures with three-dimensional periodicity at optical wavelengths , 1998, Science.

[15]  A. Baxter,et al.  Preparation and Use of a Polymer Supported BINAP Hydrogenation Catalyst , 1998 .

[16]  F. Švec,et al.  Preparation of macroporous, monodisperse, functionalized styrene-divinylbenzene copolymer beads : Effect of the nature of the monomers and total porogen volume on the porous properties , 1998 .

[17]  J. Mayoral,et al.  Polymer-Grafted Ti-TADDOL Complexes. Preparation and Use as Catalysts in Diels-Alder Reactions. , 1997, The Journal of organic chemistry.

[18]  T. Bein,et al.  Conducting Carbon Wires in Ordered, Nanometer-Sized Channels , 1994, Science.

[19]  Chun-Guey Wu,et al.  Conducting Polyaniline Filaments in a Mesoporous Channel Host , 1994, Science.

[20]  Jean M. J. Fréchet,et al.  Continuous rods of macroporous polymer as high-performance liquid chromatography separation media , 1992 .

[21]  Bradley F. Chmelka,et al.  MESOCELLULAR SILICEOUS FOAMS WITH UNIFORMLY SIZED CELLS AND WINDOWS , 1999 .