Carbonation characteristics of γ-dicalcium silicate for low-carbon building material

Abstract γ-Dicalcium silicate (γ-C2S) is characterized by its high carbonation reactivity and has the potential to be utilized as a construction material with the added benefit of CO2 sequestration. The present work addresses the characteristics of pressure-molded γ-C2S samples subjected to accelerated carbonation curing, including the developments in microstructure, carbonation degree and mechanical strength. The results indicate that the mechanical strength and surface density of carbonated γ-C2S block correlate well with its carbonation degree, which is attributed to the generation of more voluminous carbonation products. This strengthens the structure and densifies the matrix. The carbonation products include calcite as the primary morphology and aragonite as the minor phase, and amorphous Ca-modified silica gel formed by coordinated SiO4 tetrahedrons. Conductivity and ion concentration measurement elucidates the accelerated Ca2+ ion dissolution in the presence of CO2 is the reason for the high carbonation reactivity of γ-C2S. A conceptual model of carbonation process is proposed based on the distribution of Ca-modified silica gel and calcium carbonates. Additionally, the ecological evaluation demonstrates that γ-C2S would hopefully reduce 40% of the CO2 emissions compared to ordinary cement, which opens up a new area of a novel low-carbon construction material.

[1]  H. Hashim,et al.  Low carbon measures for cement plant a review , 2015 .

[2]  John E. Oakey,et al.  CO2 Capture Technologies for Cement Industry , 2009 .

[3]  S. C. Parker,et al.  Computer simulation of the structure and stability of forsterite surfaces , 1997 .

[4]  Pierre-Claude Aitcin,et al.  Cements of yesterday and today Concrete of tomorrow , 2000 .

[5]  T. C. Powers,et al.  Structure and Physical Properties of Hardened Portland Cement Paste , 1958 .

[6]  O. Jensen,et al.  Synthesis of pure Portland cement phases , 2009 .

[7]  N. Otsuki,et al.  Carbonation of γ-Ca2SiO4 and the Mechanism of Vaterite Formation , 2010 .

[8]  Jun Chang,et al.  The role of β-C2S and γ-C2S in carbon capture and strength development , 2016 .

[9]  Ming Zhao,et al.  Quantitative Control of C2S Crystal Transformation , 2011 .

[10]  Christopher M. Dobson,et al.  Progressive Changes in the Structure of Hardened C3S Cement Pastes due to Carbonation , 1991 .

[11]  E. Gartner.  Industrially interesting approaches to “low-CO2” cements ☆ , 2004 .

[12]  R. L. Berger,et al.  Reactivity and strength development of CO2 activated non-hydraulic calcium silicates , 1979 .

[13]  M. Engelhard,et al.  The role of H2O in the carbonation of forsterite in supercritical CO2 , 2011 .

[14]  Koji Sakai,et al.  Concrete Sustainability Forum III , 2011 .

[15]  Takayuki Higuchi,et al.  Development of a new ecological concrete with CO2 emissions below zero , 2014 .

[16]  The alcohol-glycerol method for the determination of free lime. , 1951, Canadian journal of chemistry.

[17]  Karen L. Scrivener,et al.  Innovation in use and research on cementitious material , 2008 .

[18]  E. Tazawa,et al.  Chemical shrinkage and autogenous shrinkage of hydrating cement paste , 1995 .

[19]  P. Walker.  Strength, durability and shrinkage characteristics of cement stabilised soil blocks , 1995 .

[20]  Chunhua Feng,et al.  The hardening behavior of γ-C2S binder using accelerated carbonation , 2016 .

[21]  D. Hoyt,et al.  Metal Carbonation of Forsterite in Supercritical CO2 and H2O Using Solid State 29Si, 13C NMR Spectroscopy , 2010 .

[22]  Gregg Marland,et al.  China: Emissions pattern of the world leader in CO2 emissions from fossil fuel consumption and cement production , 2008 .

[23]  Yokozeki Kosuke,et al.  New Ecological Concrete that Reduces CO2 Emissions Below Zero Level ∼ New Method for CO2 Capture and Storage ∼☆ , 2013 .

[24]  N. Otsuki,et al.  Corrosion of Steel Bars in Autoclaved Concrete Pile Containing γ-2CaO·SiO 2 with an Accelerated Carbonation Curing Submerged in the Real Marine Environment , 2012 .

[25]  L. Price,et al.  CARBON DIOXIDE EMISSIONS FROM THE GLOBAL CEMENT INDUSTRY , 2001 .

[26]  Abir Al-Tabbaa,et al.  Accelerated carbonation and performance of concrete made with steel slag as binding materials and aggregates , 2017 .

[27]  William T. Choate,et al.  Energy and Emission Reduction Opportunities for the Cement Industry , 2003 .

[28]  Dale P. Bentz,et al.  A review of early-age properties of cement-based materials , 2008 .

[29]  Zaid Ghouleh,et al.  Reaction Products in Carbonation-Cured Lightweight Concrete , 2013 .

[30]  M. Daimon,et al.  High durability cementitious material with mineral admixtures and carbonation curing. , 2006, Waste management.

[31]  S. Simons,et al.  A review of accelerated carbonation technology in the treatment of cement-based materials and sequestration of CO2. , 2004, Journal of hazardous materials.

[32]  Herbert T. Schaef,et al.  Water reactivity in the liquid and supercritical CO2 phase: Has half the story been neglected? , 2009 .

[33]  Duo Zhang,et al.  Review on carbonation curing of cement-based materials , 2017 .

[34]  Minoru Fukuhara,et al.  Calcium Silicate Carbonation Products , 1995 .

[35]  S. Kerisit,et al.  Water and carbon dioxide adsorption at olivine surfaces , 2013 .

[36]  Warda Ashraf,et al.  Carbonation of cement-based materials: Challenges and opportunities , 2016 .

[37]  Jun Chang,et al.  Microstructure changes of waste hydrated cement paste induced by accelerated carbonation , 2015 .

[38]  H. Hirao,et al.  A review of alternative approaches to the reduction of CO2 emissions associated with the manufacture of the binder phase in concrete , 2015 .

[39]  M. Daimon,et al.  Carbonation Reaction of Calcium Silicate Hydrates by Hydrothermal Synthesis at 150°C in OPC-γ-Ca2SiO4-α-Quartz Systems , 2007 .

[40]  V. Lagneau,et al.  Experimental measurement of portlandite carbonation kinetics with supercritical CO2 , 2009 .