Self-weaving WO3 nanoflake films with greatly enhanced electrochromic performance

Vertically oriented WO3 nanoflakes woven from nanowires were obtained using a crystal-seed-assisted hydrothermal technique on a glass substrate coated with fluorine-doped tin oxide (FTO). Investigation of the growth process revealed that two types of nanowire, along the (100) and (002) planes, respectively, were formed in the early stages. In the presence of oxalic acid and urea, these nanowires were then interwoven to give a flake-like nanofabric. This process is similar to weaving on a loom, in which the two types of nanowire act as “warp and weft threads” and the oxalic acid and urea act as the “shuttle”. The as-prepared films exhibit tunable transmittance modulation under different voltages, and repeated cycling between the coloration and bleaching states has no deleterious effect on their electrochromic performance after 1000 cycles. A larger optical modulation of 68% at 632.8 nm at a potential of −3.0 V, faster switching speeds of tc(90%) = 9.3 s and tb(90%) = 5.7 s for coloration and bleaching, respectively, and a higher coloration efficiency of 134.4 cm2 C−1 than those previously reported for the electrochromic performances of nanostructured films were achieved for this self-weaving nanoflake film.

[1]  Liejin Guo,et al.  Vertically aligned WO₃ nanowire arrays grown directly on transparent conducting oxide coated glass: synthesis and photoelectrochemical properties. , 2011, Nano letters.

[2]  Jinmin Wang,et al.  Synthesis, Assembly, and Electrochromic Properties of Uniform Crystalline WO3 Nanorods , 2008 .

[3]  S. Balaji,et al.  Hexagonal Tungsten Oxide Based Electrochromic Devices: Spectroscopic Evidence for the Li Ion Occupancy of Four-Coordinated Square Windows , 2009 .

[4]  J. Yao,et al.  Controllable assembly of WO3 nanorods/nanowires into hierarchical nanostructures. , 2006, The journal of physical chemistry. B.

[5]  T. Brezesinski,et al.  Electrochromic Stability of WO3 Thin Films with Nanometer-Scale Periodicity and Varying Degrees of Crystallinity , 2007 .

[6]  Jen‐Sue Chen,et al.  Outperformed electrochromic behavior of poly(ethylene glycol)-template nanostructured tungsten oxide films with enhanced charge transfer/transport characteristics. , 2009, Physical chemistry chemical physics : PCCP.

[7]  C. E. Tracy,et al.  Electrochromic coloration efficiency of a-WO3−y thin films as a function of oxygen deficiency , 1999 .

[8]  Claes-Göran Granqvist,et al.  Electrochromic tungsten oxide films: Review of progress 1993–1998 , 2000 .

[9]  Fu-Rong Chen,et al.  WO3−x nanowires based electrochromic devices , 2006 .

[10]  Bozhi Tian,et al.  Synthesis and Characterization of Chromium‐Doped Mesoporous Tungsten Oxide for Gas Sensing Applications , 2007 .

[11]  Aryasomayajula Subrahmanyam,et al.  Optical and electrochromic properties of oxygen sputtered tungsten oxide (WO3) thin films , 2007 .

[12]  S. A. Agnihotry,et al.  A comparison of electrochromic properties of sol–gel derived amorphous and nanocrystalline tungsten oxide films , 2007 .

[13]  Xiuli Wang,et al.  Hydrothermally synthesized WO3 nanowire arrays with highly improved electrochromic performance , 2011 .

[14]  S. A. Agnihotry,et al.  Nanostructured mesoporous tungsten oxide films with fast kinetics for electrochromic smart windows , 2006, Nanotechnology.

[15]  Bobby To,et al.  Crystalline WO3 Nanoparticles for Highly Improved Electrochromic Applications , 2006 .

[16]  S. A. Agnihotry,et al.  Effect of oxalic acid dihydrate on optical and electrochemical properties of sol–gel derived amorphous electrochromic WO3 films , 2005 .

[17]  J. Yao,et al.  Self-assembly of highly oriented one-dimensional h-WO3 nanostructures. , 2005, Chemical communications.

[18]  Claes-Göran Granqvist,et al.  Electrochromic coatings and devices: survey of some recent advances , 2003 .

[19]  Markus Antonietti,et al.  Highly crystalline WO3 thin films with ordered 3D mesoporosity and improved electrochromic performance. , 2006, Small.

[20]  Liejin Guo,et al.  Nanostructured WO₃/BiVO₄ heterojunction films for efficient photoelectrochemical water splitting. , 2011, Nano letters.

[21]  Thomas F. Jaramillo,et al.  Enhancement of Photocatalytic and Electrochromic Properties of Electrochemically Fabricated Mesoporous WO3 Thin Films , 2003 .

[22]  R. Custelcean,et al.  Crystal engineering with urea and thiourea hydrogen-bonding groups. , 2008, Chemical communications.

[23]  Xiao Wei Sun,et al.  Efficient synthesis of plate-like crystalline hydrated tungsten trioxide thin films with highly improved electrochromic performance. , 2012, Chemical communications.

[24]  Anne C. Dillon,et al.  Metal-oxide films for electrochromic applications: present technology and future directions , 2010 .

[25]  Jinmin Wang,et al.  Controlled synthesis of WO3 nanorods and their electrochromic properties in H2SO4 electrolyte , 2009 .

[26]  Spiros Papaefthimiou,et al.  Advanced electrochromic devices based on WO3 thin films , 2001 .

[27]  Hongjun Gao,et al.  Strong photoluminescence of nanostructured crystalline tungsten oxide thin films , 2005 .

[28]  Nicolae Barsan,et al.  Template-free synthesis and assembly of single-crystalline tungsten oxide nanowires and their gas-sensing properties. , 2005, Angewandte Chemie.

[29]  A. Urbano,et al.  The Beer-Lambert law for electrochromic tungsten oxide thin films , 1999 .

[30]  Francesco Tortorella,et al.  Gas recognition by activated WO3 thin-film sensors array , 2001 .

[31]  Xiao Wei Sun,et al.  Hydrothermally grown nanostructured WO3 films and their electrochromic characteristics , 2010 .

[32]  G. Leftheriotis,et al.  The effect of precursor aging on the morphology and electrochromic performance of electrodeposited tungsten oxide films , 2011 .