An investigation of the mechanisms for strength gain or loss of geopolymer mortar after exposure to elevated temperature

When fly ash-based geopolymer mortars were exposed to a temperature of 800 °C, it was found that the strength after the exposure sometimes decreased, but at other times increased. This paper shows that ductility of the mortars has a major correlation to this strength gain/loss behaviour. Specimens prepared with two different fly ashes, with strengths ranging from 5 to 60 MPa, were investigated. Results indicate that the strength losses decrease with increasing ductility, with even strength gains at high levels of ductility. This correlation is attributed to the fact that mortars with high ductility have high capacity to accommodate thermal incompatibilities. It is believed that the two opposing processes occur in mortars: (1) further geopolymerisation and/or sintering at elevated temperatures leading to strength gain; (2) the damage to the mortar because of thermal incompatibility arising from non-uniform temperature distribution. The strength gain or loss occurs depending on the dominant process.

[1]  Pierre Kalifa,et al.  High-temperature behaviour of HPC with polypropylene fibres: From spalling to microstructure , 2001 .

[2]  Kwesi Sagoe-Crentsil,et al.  Factors affecting the performance of metakaolin geopolymers exposed to elevated temperatures , 2008 .

[3]  J. Davidovits.  Geopolymers : inorganic polymeric new materials , 1991 .

[4]  J.S.J. van Deventer,et al.  The Role of Mathematical Modelling and Gel Chemistry in Advancing Geopolymer Technology , 2005 .

[5]  Chi Sun Poon,et al.  COMPRESSIVE BEHAVIOR OF FIBER REINFORCED HIGH-PERFORMANCE CONCRETE SUBJECTED TO ELEVATED TEMPERATURES , 2004 .

[6]  J. Deventer,et al.  Thermal evolution of metakaolin geopolymers: Part 1 – Physical evolution , 2006 .

[7]  S. Alonso,et al.  Alkaline activation of metakaolin and calcium hydroxide mixtures: influence of temperature, activator concentration and solids ratio , 2001 .

[8]  J. Deventer,et al.  Understanding the relationship between geopolymer composition, microstructure and mechanical properties , 2005 .

[9]  J. Sanjayan,et al.  Phase transformations and mechanical strength of OPC/Slag pastes submitted to high temperatures , 2007 .

[10]  Á. Palomo,et al.  The role played by the reactive alumina content in the alkaline activation of fly ashes , 2006 .

[11]  Grant C. Lukey,et al.  Physical evolution of Na-geopolymer derived from metakaolin up to 1000 °C , 2007 .

[12]  T. Bakharev,et al.  Geopolymeric materials prepared using Class F fly ash and elevated temperature curing , 2005 .

[13]  M. Weil,et al.  The influence of calcium content on the structure and thermal performance of fly ash based geopolymers , 2007 .

[14]  N. Banthia,et al.  Concrete under severe conditions : environment and loading : proceedings of the International Conference on Concrete Under Severe Conditions, CONSEC '95, Sapporo, Japan, 2-4 August, 1995 , 1995 .

[15]  Gabriel A. Khoury,et al.  Compressive strength of concrete at high temperatures: a reassessment , 1992 .

[16]  J. Wastiels,et al.  Low-temperature synthesized aluminosilicate glasses , 1996 .

[17]  S. Upadhyay,et al.  Effect of micellar aggregates on the kinetics of oxidation of α-aminoacids by chloramine-T in perchloric acid medium , 2005 .

[18]  B. Vijaya Rangan,et al.  ON THE DEVELOPMENT OF FLY ASH-BASED GEOPOLYMER CONCRETE , 2004 .

[19]  Kwesi Sagoe-Crentsil,et al.  Comparative performance of geopolymers made with metakaolin and fly ash after exposure to elevated temperatures , 2007 .

[20]  Jay G. Sanjayan,et al.  Damage behavior of geopolymer composites exposed to elevated temperatures , 2008 .

[21]  Ángel Palomo,et al.  Alkali-activated fly ashes: A cement for the future , 1999 .

[22]  J.S.J. van Deventer,et al.  The characterisation of source materials in fly ash-based geopolymers , 2003 .

[23]  J. Wastiels,et al.  Low-temperature synthesized aluminosilicate glasses , 1996 .

[24]  B. V. Rangan,et al.  Fly ash-based geopolymer concrete: study of slender reinforced columns , 2007 .

[25]  J. Sanjayan,et al.  Green house gas emissions due to concrete manufacture , 2007 .