Hydrophilic MacroRAFT-Mediated Emulsion Polymerization: Synthesis of Latexes for Cross-Linked and Surfactant-Free Films

A major drawback of conventional emulsion polymers arises from the presence of migrating low molar mass surfactants that contribute to poor water barrier properties and low adhesion to substrates. In this paper, we demonstrate how living polymer chains obtained by reversible addition–fragmentation chain transfer (RAFT) can be used as an efficient stabilizer in emulsion polymerization, leading to the production of surfactant-free latexes, which then form cross-linked films with beneficial properties. Hydrophilic poly(methacrylic acid) (PMAA) chains obtained by RAFT performed in water are used to mediate emulsion polymerization and produce film-forming latex particles from mixtures of methyl methacrylate, n-butyl acrylate, and styrene. Stable dispersions of particles with sizes between 100 and 200 nm are obtained, with very low amounts of coagulum (<0.5 wt %). The particles are stabilized by the PMAA segment of amphiphilic block copolymers formed during the polymerization. Remarkably, low amounts of PMAA ch...

[1]  J. Rieger,et al.  Water-based acrylic coatings reinforced by PISA-derived fibers , 2017 .

[2]  J. Asua,et al.  Effect of ionic monomer concentration on latex and film properties for surfactant-free high solids content polymer dispersions , 2017 .

[3]  J. Rieger,et al.  Mechanical properties of nanostructured films with an ultralow volume fraction of hard phase , 2017 .

[4]  Y. Holl,et al.  Simulation of Vertical Surfactant Distributions in Drying Latex Films. , 2017, Langmuir : the ACS journal of surfaces and colloids.

[5]  J. Rieger,et al.  Surfactant-free poly(vinylidene chloride) latexes via one-pot RAFT-mediated aqueous polymerization , 2016 .

[6]  M. Lansalot,et al.  From well-defined poly(N-acryloylmorpholine)-stabilized nanospheres to uniform mannuronan- and guluronan-decorated nanoparticles by RAFT polymerization-induced self-assembly , 2016 .

[7]  J. Rieger,et al.  Polymerization‐Induced Self‐Assembly: The Contribution of Controlled Radical Polymerization to The Formation of Self‐Stabilized Polymer Particles of Various Morphologies , 2016 .

[8]  S. Armes,et al.  A Critical Appraisal of RAFT-Mediated Polymerization-Induced Self-Assembly , 2016, Macromolecules.

[9]  Xuewei Zhang,et al.  The Effect of Hydrophile Topology in RAFT-Mediated Polymerization-Induced Self-Assembly. , 2016, Angewandte Chemie.

[10]  S. Armes,et al.  Polymerization-induced self-assembly of block copolymer nanoparticles via RAFT non-aqueous dispersion polymerization , 2016 .

[11]  J. Rieger.  Guidelines for the Synthesis of Block Copolymer Particles of Various Morphologies by RAFT Dispersion Polymerization. , 2015, Macromolecular rapid communications.

[12]  Yang Liu,et al.  Water Vapor Sorption and Diffusion in Secondary Dispersion Barrier Coatings: A Critical Comparison with Emulsion Polymers. , 2015, ACS applied materials & interfaces.

[13]  R. Tuinier,et al.  Self-Assembled Structures of PMAA–PMMA Block Copolymers: Synthesis, Characterization, and Self-Consistent Field Computations , 2015 .

[14]  Steven P. Armes,et al.  Polymerization-Induced Self-Assembly of Block Copolymer Nano-objects via RAFT Aqueous Dispersion Polymerization , 2014, Journal of the American Chemical Society.

[15]  J. Rieger,et al.  Soft nanostructured films with an ultra-low volume fraction of percolating hard phase. , 2013, Macromolecular rapid communications.

[16]  Olivier Boyron,et al.  Effect of the pH on the RAFT Polymerization of Acrylic Acid in Water. Application to the Synthesis of Poly(acrylic acid)-Stabilized Polystyrene Particles by RAFT Emulsion Polymerization , 2013 .

[17]  J. Rieger,et al.  RAFT-mediated one-pot aqueous emulsion polymerization of methyl methacrylate in presence of poly(methacrylic acid-co-poly(ethylene oxide) methacrylate) trithiocarbonate macromolecular chain transfer agent , 2013 .

[18]  J. Barton̆,et al.  Emulsion polymerization of butyl acrylate , 2013 .

[19]  R. Antoine,et al.  Batch Emulsion Polymerization Mediated by Poly(methacrylic acid) MacroRAFT Agents: One-Pot Synthesis of Self-Stabilized Particles , 2012 .

[20]  J. Rieger,et al.  Polymerization-Induced Self-Assembly: From Soluble Macromolecules to Block Copolymer Nano-Objects in One Step , 2012 .

[21]  J. Rieger,et al.  Toward a Better Understanding of the Parameters that Lead to the Formation of Nonspherical Polystyrene Particles via RAFT-Mediated One-Pot Aqueous Emulsion Polymerization , 2012 .

[22]  M. Lansalot,et al.  RAFT Polymerization of Methacrylic Acid in Water , 2012 .

[23]  J. Rieger,et al.  One-Pot Synthesis of Poly(methacrylic acid-co-poly(ethylene oxide) methyl ether methacrylate)-b-polystyrene Amphiphilic Block Copolymers and Their Self-Assemblies in Water via RAFT-Mediated Radical Emulsion Polymerization. A Kinetic Study , 2011 .

[24]  J. Rieger,et al.  Controlled radical polymerization of styrene in miniemulsion mediated by PEO-based trithiocarbonate macromolecular RAFT agents , 2011 .

[25]  A. Routh,et al.  Fundamentals of Latex Film Formation: Processes and Properties , 2010 .

[26]  A. Routh,et al.  Fundamentals of Latex Film Formation , 2010 .

[27]  J. Rieger,et al.  Surfactant-Free Controlled/Living Radical Emulsion (Co)polymerization of n-Butyl Acrylate and Methyl Methacrylate via RAFT Using Amphiphilic Poly(ethylene oxide)-Based Trithiocarbonate Chain Transfer Agents , 2009 .

[28]  H. Minami,et al.  Emulsifier-Free, Organotellurium-Mediated Living Radical Emulsion Polymerization of Butyl Acrylate† , 2009 .

[29]  Adam E. Smith,et al.  Aqueous RAFT Synthesis of pH-Responsive Triblock Copolymer mPEO−PAPMA−PDPAEMA and Formation of Shell Cross-Linked Micelles† , 2008 .

[30]  Xuejun Cui,et al.  Preparation and characterization of emulsifier-free core–shell interpenetrating polymer network-fluorinated polyacrylate latex particles , 2008 .

[31]  J. Keddie,et al.  The diacetone acrylamide crosslinking reaction and its influence on the film formation of an acrylic latex , 2008 .

[32]  C. Pichot,et al.  Sub-Micrometer Sized Hairy Latex Particles Synthesized by Dispersion Polymerization Using Hydrophilic Macromolecular RAFT Agents , 2007 .

[33]  A. Santos,et al.  Combining steric and electrostatic stabilization using hydrophilic MacroRAFT agents in an Ab initio emulsion polymerization of styrene , 2007 .

[34]  Jae Heung Lee,et al.  Microwave‐Irradiated Copolymerization of Styrene and Butyl Acrylate , 2007 .

[35]  B. Klumperman,et al.  Surfactant-free artificial latexes from modified styrene-maleic anhydride (SMA) copolymers , 2006 .

[36]  Maud Save,et al.  Batch Emulsion Polymerization of Styrene Stabilized by a Hydrophilic Macro‐RAFT Agent , 2006 .

[37]  Chaocan Zhang,et al.  Emulsifier-free latex of fluorinated acrylate copolymer , 2006 .

[38]  J. Prins.  Directive 2003/98/EC of the European Parliament and of the Council , 2006 .

[39]  T. Fukuda,et al.  Kinetic study on reversible addition–fragmentation chain transfer (RAFT) process for block and random copolymerizations of styrene and methyl methacrylate , 2005 .

[40]  Catherine Lefay,et al.  Surfactant-free synthesis of amphiphilic diblock copolymer nanoparticles via nitroxide-mediated emulsion polymerization. , 2005, Chemical communications.

[41]  M. Winnik,et al.  Functional latex and thermoset latex films , 2004 .

[42]  C. Fellows,et al.  Effect of surfactant systems on the water sensitivity of latex films , 2004 .

[43]  Catherine Lefay,et al.  First Nitroxide-Mediated Controlled Free-Radical Polymerization of Acrylic Acid , 2003 .

[44]  Y. K. Chong,et al.  Thiocarbonylthio Compounds [SC(Ph)S−R] in Free Radical Polymerization with Reversible Addition-Fragmentation Chain Transfer (RAFT Polymerization). Role of the Free-Radical Leaving Group (R) , 2003 .

[45]  R. Sanderson,et al.  The use of selected acrylate and acrylamide-based surfmers and polysoaps in the emulsion polymerization of styrene , 2003 .

[46]  M. Winnik,et al.  Epoxy-functionalized, low-glass-transition-temperature latex. II. Interdiffusion versus crosslinking in the presence of a diamine , 2002 .

[47]  Brian S. Hawkett,et al.  Effective ab Initio Emulsion Polymerization under RAFT Control , 2002 .

[48]  C. Barner‐Kowollik,et al.  Propagation Rate Coefficients of Acrylate−Methacrylate Free-Radical Bulk Copolymerizations , 2001 .

[49]  P. Gennes,et al.  Strengthening of a Polymer Interface: Interdiffusion and Crosslinking , 2000, cond-mat/0009183.

[50]  B. Momper,et al.  Influence of nonionic emulsifiers on the properties of vinyl acetate/VeoVa10® and vinyl acetate/ethylene emulsions and paints , 1999 .

[51]  E. Pérez,et al.  Flattening of Latex Film Surface: Theory and Experiments by Atomic Force Microscopy , 1999 .

[52]  B. Schlarb,et al.  Hydroresin dispersions: new emulsifier free binders for aqueous coatings , 1995 .

[53]  A. Rudin,et al.  Practical aspects of the emulsifier-free emulsion polymerization of styrene , 1994 .

[54]  A. Zosel,et al.  Influence of crosslinking on structure, mechanical properties, and strength of latex films , 1993 .

[55]  A. Rennie,et al.  Formation of bilayers and Plateau borders during the drying of film-forming latexes as investigated by small-angle neutron scattering , 1992 .

[56]  A. G. Rejon.  Copolymérisation en émulsion styrène-acrylate de butyle en réacteur fermé , 1985 .

[57]  D. H. Napper,et al.  Kinetics of emulsion polymerization of methyl methacrylate , 1984 .

[58]  D. H. Napper,et al.  Application of electron spin resonance spectroscopy to emulsion polymerization , 1984 .

[59]  W. Lane.  Determination of Solubility of Styrene in Water and of Water in Styrene , 1946 .