Behaviour of Pre-Cracked Self-Healing Cementitious Materials under Static and Cyclic Loading

Capsule-based self-healing is increasingly being targeted as an effective way to improve the durability and sustainability of concrete infrastructures through the extension of their service life. Assessing the mechanical and durability behaviour of self-healing materials after damage and subsequent autonomous repair is essential to validate their possible use in real structures. In this study, self-healing mortars containing cementitious tubular capsules with a polyurethanic repairing agent were experimentally investigated. Their mechanical behaviour under both static and cyclic loading was analysed as a function of some factors related to the capsules themselves (production method, waterproof coating configuration, volume of repairing agent stored) or to the specimens (number, size and distribution of the capsules in the specimen). Their mechanical performances were quantified in terms of recovery of load-bearing capacity under static conditions and number of cycles to failure as a function of the peak force under cyclic conditions. Positive results were achieved, with a maximum load recovery index up to more than 40% and number of cycles to failure exceeding 10,000 in most cases, with peak force applied during cyclic loading at least corresponding to 70% of the estimated load-bearing capacity of the healed samples.

[1]  Didier Snoeck,et al.  From straw in bricks to modern use of microfibers in cementitious composites for improved autogenous healing – A review , 2015 .

[2]  Robby Caspeele,et al.  Development of an improved cracking method to reduce the variability in testing the healing efficiency of self-healing mortar containing encapsulated polymers , 2018 .

[3]  Xianming Shi,et al.  A self-healing cementitious composite using oil core/silica gel shell microcapsules , 2011 .

[4]  C. S. Cai,et al.  Prediction of bridge maximum load effects under growing traffic using non-stationary bayesian method , 2019, Engineering Structures.

[5]  Guang Ye,et al.  Feasibility of self-healing in cementitious materials – By using capsules or a vascular system? , 2014 .

[6]  Patric Jacobs,et al.  Self-healing efficiency of cementitious materials containing tubular capsules filled with healing agent , 2011 .

[7]  A. Naaman,et al.  Fatigue characteristics of high performance fiber-reinforced concrete , 1998 .

[8]  Paola Antonaci,et al.  Setup of Extruded Cementitious Hollow Tubes as Containing/Releasing Devices in Self-Healing Systems , 2015, Materials.

[9]  Marco Scalerandi,et al.  Ultrasonic Monitoring of the Interaction between Cement Matrix and Alkaline Silicate Solution in Self-Healing Systems , 2017, Materials.

[10]  R. P. Johnson,et al.  General rules and rules for buildings , 2004 .

[11]  Takatsune Kikuta,et al.  Experimental Study on Self-Healing Capability of FRCC Using Different Types of Synthetic Fibers , 2012 .

[12]  Nele De Belie,et al.  Neutron Radiography Based Visualization and Profiling of Water Uptake in (Un)cracked and Autonomously Healed Cementitious Materials , 2016, Materials.

[13]  N. De Belie,et al.  Self-healing of moving cracks in concrete by means of encapsulated polymer precursors , 2016 .

[14]  Jun Lu,et al.  Effect of loading frequency and stress level on low cycle fatigue behavior of plain concrete in direct tension , 2017 .

[15]  Nele De Belie,et al.  The efficiency of self-healing cementitious materials by means of encapsulated polyurethane in chloride containing environments , 2014 .

[16]  A. Al-Tabbaa,et al.  Microfluidic fabrication of microcapsules tailored for self-healing in cementitious materials , 2018, Construction and Building Materials.

[17]  장승엽.  CONCRETE : Microstructure, Properties, and Materials, 3rd Edition , 2009 .

[18]  S. Cavalaro,et al.  Fatigue of cracked high performance fiber reinforced concrete subjected to bending , 2019, Construction and Building Materials.

[19]  Nele De Belie,et al.  The efficiency of self-healing concrete using alternative manufacturing procedures and more realistic crack patterns , 2015 .

[20]  E. Yang,et al.  Fatigue-induced deterioration of the interface between micro-polyvinyl alcohol (PVA) fiber and cement matrix , 2016 .

[21]  Antonio Gliozzi,et al.  Correlation of elastic and mechanical properties of consolidated granular media during microstructure evolution induced by damage and repair , 2018 .

[22]  Nele De Belie,et al.  Improved multiple cracking and autogenous healing in cementitious materials by means of chemically-treated natural fibres , 2015 .

[23]  Abir Al-Tabbaa,et al.  Encapsulation of expansive powder minerals within a concentric glass capsule system for self-healing concrete , 2016 .

[24]  N. De Belie,et al.  Monitoring crack movement in polymer-based self-healing concrete through digital image correlation, acoustic emission analysis and SEM in-situ loading , 2017 .

[25]  Nele De Belie,et al.  Acoustic emission analysis for the quantification of autonomous crack healing in concrete , 2012 .

[26]  Luciano Di Maio,et al.  Use of polypropylene fibers coated with nano-silica particles into a cementitious mortar , 2015 .

[27]  John Dalsgaard Sørensen,et al.  Quantification of traffic and temperature effects on the fatigue safety of a reinforced-concrete bridge deck based on monitoring data , 2019, Engineering Structures.

[28]  Bo Pang,et al.  Autogenous and engineered healing mechanisms of carbonated steel slag aggregate in concrete , 2016 .

[29]  S. K. Kaushik,et al.  Fatigue strength of steel fibre reinforced concrete in flexure , 2003 .

[30]  Enzo Martinelli,et al.  Tensile strength of flax fabrics to be used as reinforcement in cement-based composites: experimental tests under different environmental exposures , 2019, Composites Part B: Engineering.

[31]  Liberato Ferrara,et al.  A “fracture testing” based approach to assess crack healing of concrete with and without crystalline admixtures , 2014 .

[32]  Nele De Belie,et al.  Self-Healing in Cementitious Materials—A Review , 2013 .

[33]  H. Cifuentes,et al.  Influence of the fiber content on the compressive low-cycle fatigue behavior of self-compacting SFRC , 2017 .

[34]  K. Pilakoutas,et al.  Fatigue resistance and cracking mechanism of concrete pavements reinforced with recycled steel fibres recovered from post-consumer tyres , 2012 .

[35]  Liberato Ferrara,et al.  A Review of Self‐Healing Concrete for Damage Management of Structures , 2018 .

[36]  Nele De Belie,et al.  Quantification of the Service Life Extension and Environmental Benefit of Chloride Exposed Self-Healing Concrete. , 2016 .

[37]  Veerle Cnudde,et al.  Comparison of different approaches for self-healing concrete in a large-scale lab test , 2016 .

[38]  Abir Al-Tabbaa,et al.  Glass encapsulated minerals for self-healing in cement based composites , 2015 .

[39]  Liberato Ferrara,et al.  Experimental characterization of the self-healing capacity of cement based materials and its effects on the material performance: A state of the art report by COST Action SARCOS WG2 , 2018 .

[40]  F. Xing,et al.  Flexural Fatigue Properties of Ultra-High Performance Engineered Cementitious Composites (UHP-ECC) Reinforced by Polymer Fibers , 2018, Polymers.

[41]  Liberato Ferrara,et al.  A methodology to assess crack-sealing effectiveness of crystalline admixtures under repeated cracking-healing cycles , 2018, Construction and Building Materials.

[42]  Nele De Belie,et al.  Self-healing phenomena in cement-based materials , 2013 .

[43]  Robby Caspeele,et al.  Novel active crack width control technique to reduce the variation on water permeability results for self-healing concrete , 2019, Construction and Building Materials.

[44]  E. Yang,et al.  Fatigue-induced in-situ strength deterioration of micro-polyvinyl alcohol (PVA) fiber in cement matrix , 2017 .

[45]  Tomoya Nishiwaki,et al.  Self-Healing Capability of Fiber Reinforced Cementitious Composites , 2011 .

[46]  Paola Antonaci,et al.  Experimental analysis of self-healing cement-based materials incorporating extruded cementitious hollow tubes , 2016 .

[47]  Qing-hua Li,et al.  Fatigue Deformation Model of Plain and Fiber-Reinforced Concrete Based on Weibull Function , 2019, Journal of Structural Engineering.

[48]  Erik Schlangen,et al.  Simulation-Aided Design of Tubular Polymeric Capsules for Self-Healing Concrete , 2016, Materials.

[49]  Zhang Jun,et al.  Fatigue Performance in Flexure of Fiber Reinforced Concrete , 1998 .

[50]  Eugene J. O'Brien,et al.  The Effect of Traffic Growth on Characteristic Bridge Load Effects , 2016 .

[51]  Tran Diep Phuoc Thao,et al.  Implementation of self-healing in concrete – Proof of concept , 2009 .

[52]  José Sena-Cruz,et al.  Pullout Behavior of Steel Fibers in Self-Compacting Concrete , 2010 .

[53]  G. Plizzari,et al.  Post-peak fatigue performance of steel fiber reinforced concrete under flexure , 2016 .