Abstract Fuel swelling of U–Mo alloy was modeled using the measured data from samples irradiated up to a fission density of ∼7 × 10 27  fissions/m 3 at temperatures below ∼250 °C. The overall fuel swelling was measured from U–Mo foils with as-fabricated thickness of 250 μm. Volume fractions occupied by fission gas bubbles were measured and fuel swelling caused by the fission gas bubbles was quantified. The portion of fuel swelling by solid fission products including solid and liquid fission products as well as fission gas atoms not enclosed in the fission gas bubbles is estimated by subtracting the portion of fuel swelling by gas bubbles from the overall fuel swelling. Empirical correlations for overall fuel swelling, swelling by gas bubbles, and swelling by solid fission products were obtained in terms of fission density.

[1]  B. Lustman,et al.  Phase Changes in Pile‐Irradiated Uranium‐Base Alloys , 1956 .

[2]  Kyung-Wook Paik,et al.  Characterization of U-2 wt% Mo and U-10 wt% Mo alloy powders prepared by centrifugal atomization , 1997 .

[3]  J. Rest,et al.  Analysis of intergranular fission-gas bubble-size distributions in irradiated uranium–molybdenum alloy fuel , 2009 .

[4]  Daniel M. Wachs,et al.  Transmission electron microscopy characterization of irradiated U–7Mo/Al–2Si dispersion fuel , 2010 .

[5]  D. Keiser,et al.  Electron microscopy characterization of an as-fabricated research reactor fuel plate comprised of U–7Mo particles dispersed in an Al–2Si alloy matrix , 2010 .

[6]  Jong Man Park,et al.  USE OF A CENTRIFUGAL ATOMIZATION PROCESS IN THE DEVELOPMENT OF RESEARCH REACTOR FUEL , 2007 .

[7]  J. Rest.  Evolution of fission-gas-bubble-size distribution in recrystallized U–10Mo nuclear fuel , 2010 .

[8]  Robert W. Cahn,et al.  Materials science and technology : a comprehensive treatment , 2000 .

[9]  J. Rest,et al.  The effect of irradiation-induced gas-atom re-solution on grain-boundary bubble growth , 2003 .

[10]  Y. Kim,et al.  A CLASSIFICATION OF UNIQUELY DIFFERENT TYPES OF NUCLEAR FISSION GAS BEHAVIOR , 2005 .

[11]  I. T. Young,et al.  Quantitative Microscopy , 1984, Definitions.

[12]  G. Hofman,et al.  Metallic Fast Reactor Fuels , 2006 .

[13]  J. Rest.  An analytical study of gas-bubble nucleation mechanisms in uranium-alloy nuclear fuel at high temperature☆ , 2010 .

[14]  Douglas E. Burkes,et al.  Properties of DU–10 wt% Mo alloys subjected to various post-rolling heat treatments ☆ , 2010 .