Effect of Cold Rolling on Cluster(1) Dissolvability during Artificial Aging and Formability during Natural Aging in Al-0.6Mg-1.0Si-0.5Cu Alloy

Natural aging after solution treatment has a negative effect on the precipitation strengthening of Al–Mg–Si alloys since Cluster(1) formed at a room temperature cannot be dissolved or transformed into precipitates during artificial aging at 170 °C. In this study, cold rolling is focused on as an alternative solution to pre-aging, which is a conventional method to prevent Cluster(1) formation. It is known that excess vacancies are necessary for cluster formation. Cold rolling suppresses cluster formation because excess vacancies disappear at dislocations introduced by cold rolling. In addition, it is expected that cold rolling accelerates the precipitation behavior because the diffusion of solute atoms is promoted by introduced lattice defects. The transition of Cluster(1) was evaluated by Micro Vickers hardness tests, tensile tests, electrical conductivity measurements and differential scanning calorimetry analyses. Results showed the negative effect of natural aging was almost suppressed in 10% cold-rolled samples and completely suppressed in 30% cold-rolled samples since Cluster(1) dissolved during artificial aging at 170 °C due to lowering of the temperature of Cluster(1) dissolution by cold rolling. It was found that the precipitation in cold-rolled samples was accelerated since the hardness peak of 10% cold-rolled samples appeared earlier than T6 and pre-aged samples.

[1]  S. Kuramoto,et al.  Effect of 90% cold rolling on precipitation behavior of Al-0.6Mg-1.0Si-0.5Cu alloy , 2021, Journal of Japan Institute of Light Metals.

[2]  A. Maltais,et al.  Effects of natural aging and pre-aging on the strength and electrical conductivity in Al-Mg-Si AA6201 conductor alloys , 2021, Materials Science and Engineering: A.

[3]  R. Holmestad,et al.  Linking mechanical properties to precipitate microstructure in three Al-Mg-Si(-Cu) alloys , 2021 .

[4]  S. Ringer,et al.  Design of solute clustering during thermomechanical processing of AA6016 Al–Mg–Si alloy , 2021 .

[5]  S. Xiong,et al.  Atomistic determination on stability, cluster and microstructures in terms of crystallographic and thermo-kinetic integration of Al−Mg−Si alloys , 2020 .

[6]  R. Holmestad,et al.  The effect of low Cu additions on precipitate crystal structures in overaged Al-Mg-Si(-Cu) alloys , 2020 .

[7]  K. Matsuda,et al.  The effect of heavy deformation on the precipitation in an Al-1.3Cu-1.0Mg-0.4Si wt.% alloy , 2020 .

[8]  P. Sanders,et al.  Composition dependent thermal stability and evolution of solute clusters in Al-Mg-Si analyzed using atom probe tomography , 2018 .

[9]  Tatsuo Sato,et al.  Formulation of initial artificial age-hardening response in an Al-Mg-Si alloy based on the cluster classification using a high-detection-efficiency atom probe , 2018 .

[10]  Tatsuo Sato,et al.  Effects of cluster characteristics on two-step aging behavior in Al-Mg-Si alloys with different Mg/Si ratios and natural aging periods , 2018 .

[11]  R. Holmestad,et al.  Strengthening mechanisms in ultrafine grained Al-Mg-Si alloy processed by hydrostatic extrusion – Influence of ageing temperature , 2016 .

[12]  R. Holmestad,et al.  The Effect of Cu and Ge Additions on Strength and Precipitation in a lean 6xxx Aluminium Alloy , 2015 .

[13]  R. Jayaganthan,et al.  Effect of ageing on tensile behavior of ultrafine grained Al 6061 alloy , 2015 .

[14]  Man Liu,et al.  DSC analyses of static and dynamic precipitation of an Al–Mg–Si–Cu aluminum alloy , 2015 .

[15]  N. Tsuji,et al.  Mechanical properties and microstructure of 6061 aluminum alloy severely deformed by ARB process and subsequently aged at low temperatures , 2014 .

[16]  R. Holmestad,et al.  The effects of quench rate and pre-deformation on precipitation hardening in Al–Mg–Si alloys with different Cu amounts , 2014 .

[17]  R. Holmestad,et al.  The Effects of Low Cu Additions and Predeformation on the Precipitation in a 6060 Al-Mg-Si Alloy , 2013, Metallurgical and Materials Transactions A.

[18]  Tatsuo Sato,et al.  Effect of cold rolling on the formation and distribution of nanoclusters during pre-aging in an Al–Mg–Si alloy , 2013 .

[19]  A. Deschamps,et al.  Mesoscopic modelling of precipitation: A tool for extracting physical parameters of phase transformations in metallic alloys , 2010 .

[20]  W. Poole,et al.  The characterization of dislocation–nanocluster interactions in Al–Mg–Si(–Cu/Ag) alloys , 2010 .

[21]  T. Masuda,et al.  Combined effect of pre-straining and pre-aging on bake-hardening behavior of an Al-0.6 mass %Mg-1.0 mass % Si alloy , 2010 .

[22]  P. Mascher,et al.  Study of the early stages of clustering in Al–Mg–Si alloys using the electrical resistivity measurements , 2009 .

[23]  Tatsuo Sato,et al.  Three-Dimensional Atom Probe Characterization of Nanoclusters Responsible for Multistep Aging Behavior of an Al-Mg-Si Alloy , 2008 .

[24]  E. Cerri,et al.  Influence of severe plastic deformation on aging of Al–Mg–Si alloys , 2005 .

[25]  H. Weiland,et al.  The effect of predeformation on the β″ and β′ precipitates and the role of Q′ phase in an Al–Mg–Si alloy; AA6022 , 2005 .

[26]  達雄 里,et al.  Al-Mg-Si系合金におけるクラスタ形成と二段時効挙動 , 2001 .

[27]  Paul Shewmon,et al.  Diffusion in Solids , 2016 .