The effect of film microstructures on cracking of transparent conductive oxide (TCO) coatings on polymer substrates

Abstract We investigate the effects of film microstructures such as crystallinity and surface roughness on cracking of TCO coated on polymer substrates. Indium tin oxide (ITO), which is the most extensively used TCO for electrodes in flexible electronics, is sputter-deposited on polyethylene terephthalate (PET). Varying thickness (tf) and deposition condition, amorphous ITO (a-ITO) with different surface roughness (Rrms) and a partially crystallized ITO with similar Rrms to a-ITO of the same tf are coated on PET. Cracking in ITO under tension is analyzed by uniaxial tension test. The mode of cracking and the fracture strength are related to the crystallinity and Rrms of ITO analyzed by high resolution transmission electron microscopy (HR TEM) and atomic force microscopy (AFM), respectively. Our experimental results reveal that the strength of ITO is significantly improved with crystallinity. The important effect of Rrms on cracking is also clearly revealed. In a-ITO, fracture strength is decreased almost linearly with Rrms that increases with tf. In addition, cracks are always initiated and propagated along the valleys between protrusions on the surface regardless of crystallinity. Based on our experimental results, a low temperature deposition condition to obtain ITO with a high level of functional and mechanical properties is proposed.

[1]  D. Choi,et al.  Properties of fluorine doped ZnO thin films deposited by magnetron sputtering , 2008 .

[2]  Sigurd Wagner,et al.  Micromechanics of macroelectronics , 2005 .

[3]  K. H. Schulz,et al.  Electrical, optical and structural characteristics of indium-tin-oxide thin films deposited on glass and polymer substrates , 1997 .

[4]  Yuzo Shigesato,et al.  A microstructural study of low resistivity tin-doped indium oxide prepared by d.c. magnetron sputtering , 1994 .

[5]  Myeongkyu Lee,et al.  Highly enhanced mechanical stability of indium tin oxide film with a thin Al buffer layer deposited on plastic substrate , 2009 .

[6]  Itaru Yasui,et al.  Electrical and Structural Properties of Tin-Doped Indium Oxide Films Deposited by DC Sputtering at Room Temperature , 1999 .

[7]  K. Röll,et al.  Analysis of stress and strain distribution in thin films and substrates , 1976 .

[8]  Denis Remiens,et al.  Physical properties of RF sputtered ITO thin films and annealing effect , 2006 .

[9]  Improving the delamination resistance of indium tin oxide (ITO) coatings on polymeric substrates by O2 plasma surface treatment , 2010 .

[10]  D. Paine,et al.  A time-resolved reflectivity study of the amorphous-to-crystalline transformation kinetics in dc-magnetron sputtered indium tin oxide , 1998 .

[11]  Yonggang Huang,et al.  Stretchable and Foldable Silicon Integrated Circuits , 2008, Science.

[12]  B. Cotterell,et al.  Buckling and cracking of thin films on compliant substrates under compression , 2000 .

[13]  Gregory P. Crawford,et al.  Flexible flat panel displays , 2005 .

[14]  jin woo Park,et al.  The cohesive crack and buckle delamination resistances of indium tin oxide (ITO) films on polymeric substrates with ductile metal interlayers , 2010 .

[15]  M. Bousmina,et al.  The effect of glow discharge plasma on the surface properties of Poly (ethylene terephthalate) (PET) film , 2008 .

[16]  John Lewis.  Material challenge for flexible organic devices , 2006 .

[17]  Yves Leterrier,et al.  Mechanical integrity of transparent conductive oxide films for flexible polymer-based displays , 2004 .

[18]  Y. Leterrier,et al.  Evaluation of thin film adhesion to a compliant substrate by the analysis of progressive buckling in the fragmentation test , 2009 .

[19]  J. Yi,et al.  Growth and characterization of indium tin oxide thin films deposited on PET substrates , 2008 .

[20]  Yuzo Shigesato,et al.  Electrical and structural properties of low resistivity tin‐doped indium oxide films , 1992 .

[21]  J. Vlassak.  Channel cracking in thin films on substrates of finite thickness , 2003 .

[22]  Yves Leterrier,et al.  Mechanical analysis of ultrathin oxide coatings on polymer substrates in-situ in a scanning electron microscope , 2003 .