Microstructural Changes and Estimated Strengthening Contributions in a Gamma Alloy Ti-45Al-5Nb Pack-Rolled Sheet (Preprint)

Abstract Thin sheets made of a gamma-titanium aluminide alloy, Ti–45Al–5Nb, produced by a pack-rolling process, were evaluated for microstructure variation and evolution taking place during aging and annealing treatments. The as-received sheet material was characterized by remarkably high yield strength, 810 MPa, and a complex bimodal microstructure. The microstructure consisted of a matrix of twinned gamma-phase grains and fine-lath lamellar grain microconstituent, together with a dispersed ultra-fine-grained gamma + alpha-2 mixture microconstituent. High-temperature isothermal aging treatments changed the microstructure to a stable mixture of gamma-phase grains (matrix) and coarse alpha-2-phase particles, having size distributions and volume fractions that were specific to the aging temperature. A concurrent strength loss reflects this trend and results in a stable strength level of 550 MPa upon aging at 1000 °C for 144 h. Using composition estimates from the phase-boundary shifts that occur from the Nb addition to a Ti–45Al base alloy and, the rule of mixtures, an analysis was made to show that the gamma-phase matrix has an intrinsic strength of 178 MPa. This is a significant intrinsic strength level, well over that of ∼70 MPa for the Ti–45Al binary alloy. This is rationalized as the solid-solution strengthening effect from shifts of the Ti and Nb levels in the gamma phase and, by an added effect due to increased oxygen solubility in the gamma phase. The overall strength of Ti–45Al–5Nb, however, is roughly the same as that of Ti–45Al, and this is explained by a drastic reduction in the volume fraction of alpha-2-phase in Ti–45Al–5Nb alloy, which is a result of the Nb-induced phase-boundary shifts.

[1]  T. Nakano,et al.  Effect of compositional deviations from stoichiometry on the plastic behaviour of Ti3Al single crystals , 1993 .

[2]  T. Nakano,et al.  Effect of Nb addition on the plastic behavior of TiAl crystals containing oriented lamellae , 1992 .

[3]  H. Inui,et al.  Plastic deformation of single crystals of a DO19 compound with an off-stoichiometric composition (Ti-36·5 at.% Al) at room temperature , 1993 .

[4]  Young-Won Kim,et al.  Microstructural evolution and mechanical properties of a forged gamma titanium aluminide alloy , 1992 .

[5]  Young-Won Kim.  Effects of microstructure on the deformation and fracture of γ-TiAl alloys , 1995 .

[6]  A. Menand,et al.  Interstitial solubility in γ and α2 phases of TiAl-based alloys , 1996 .

[7]  R. Wagner,et al.  The compression behaviour of niobium alloyed γ-titanium alumindies , 1998 .

[8]  H. Mecking,et al.  General aspects of the thermomechanical , 1993, Metallurgical and Materials Transactions A.

[9]  Toshimitsu Tetsui,et al.  Endurance and composition and microstructure effects on endurance of TiAl used in turbochargers , 1999 .

[10]  Dennis M. Dimiduk,et al.  Systems engineering of gamma titanium aluminides: impact of fundamentals on development strategy , 1998 .

[11]  D. Seidman,et al.  Atomic Scale Chemistry of α2/γ Interfaces in a Multi-Component TiAl Alloy , 2004 .

[12]  Y-W. Kim,et al.  Microstructure/property relationships in titanium aluminides and alloys , 1990 .

[13]  M. Gibson,et al.  Zone-axis convergent-beam electron diffraction and ALCHEMI analysis of Ti-Al alloys with ternary additions , 1996 .

[14]  Dennis M. Dimiduk,et al.  The role of grain size and selected microstructural parameters in strengthening fully lamellar TiAl alloys , 1998 .

[15]  Young-Won Kim.  Strength and ductility in TiAl alloys , 1998 .

[16]  Young-Won Kim,et al.  Gamma titanium aluminides , 1995 .

[17]  W. J. Zhang,et al.  On the origin of superior high strength of Ti–45Al–10Nb alloys , 2002 .

[18]  R. Wagner,et al.  Novel design concepts for gamma-base titanium aluminide alloys , 2000 .

[19]  Yan Song,et al.  Site occupancy of alloying additions in titanium aluminides and its application to phase equilibrium evaluation , 2000 .