Stress adaptation in ceramic thin films.

Two mechanisms by which an inorganic thin film may reversibly adapt to externally imposed strain have been considered: (1) the chemical strain effect and (2) self-organization of polycrystalline macro-domains. The chemical strain effect is due to the transformation of the elastic energy of an externally applied stress into chemical energy of interacting point defects. This effect may be observed in solids with a large concentration of interacting point defects if the interaction is accompanied by a large change in specific volume. Self-organization of polycrystalline macro-domains may take place when single-domain ferroelastic grains minimize intergrain strain via approximate mutual alignment of their crystallographic axes. Each such macro-domain region has a preferred size and direction of alignment. In the presence of externally applied stress, these regions may reorganize, thereby partially converting the elastic energy of the external stress into the elastic energy of intergrain stress. Although very different in nature, both mechanisms result in reversible strain-relaxation. The conditions under which each of these effects may be present are understood well enough to provide clear guidance for preparation of materials and for their incorporation into practical devices.

[1]  P. Hendriksen,et al.  Oxygen nonstoichiometry and transport properties of strontium substituted lanthanum cobaltite , 2006 .

[2]  W. Haije,et al.  Oxygen stoichiometry and chemical expansion of Ba0.5Sr0.5Co0.8Fe0.2O3- δ measured by in situ neutron diffraction , 2006 .

[3]  E. Wachtel,et al.  Elasticity of Solids with a Large Concentration of Point Defects , 2006 .

[4]  E. Wachtel,et al.  Anomalous pre-nucleation volume expansion of amorphous BaTiO3 , 2005 .

[5]  V. Lyahovitskaya,et al.  Polycrystalline Macro‐Domains Formed by Self‐Organization of Ferroelectric Grains , 2005 .

[6]  Xiyong Chen,et al.  Thermal and Chemical Expansion of Sr-Doped Lanthanum Cobalt Oxide (La1-xSrxCoO3-δ) , 2005 .

[7]  Zongping Shao,et al.  A thermally self-sustained micro solid-oxide fuel-cell stack with high power density , 2005, Nature.

[8]  E. Wachtel,et al.  Self-organization of ferroelectric grains in self-supported nanocrystalline films , 2005 .

[9]  A. Studer,et al.  Direct observation of ferroelastic domain switching in polycrystalline BaTiO3 using in situ neutron diffraction , 2005 .

[10]  François Maréchal,et al.  Fuel Cell Modeling and Simulations , 2004 .

[11]  L. Gauckler,et al.  Tape casting of nanocrystalline ceria gadolinia powder , 2004 .

[12]  Klavs F. Jensen,et al.  Fabrication and structural characterization of self-supporting electrolyte membranes for a micro solid-oxide fuel cell , 2004 .

[13]  E. Wachtel,et al.  Room Temperature Phase Transition in CeO2 Nanocrystalline Films , 2004 .

[14]  R. Harrison,et al.  Dynamical excitation and anelastic relaxation of ferroelastic domain walls in LaAlO 3 , 2004 .

[15]  E. Wachtel,et al.  Anomalous Expansion of CeO2 Nanocrystalline Membranes , 2003 .

[16]  Jordan E. Massad,et al.  A Domain Wall Model for Hysteresis in Ferroelastic Materials , 2003 .

[17]  M. Dokiya,et al.  Expansion Behavior of Ce1 − y Gd y O 2.0 − 0.5y − δ under Various Oxygen Partial Pressures Evaluated by HTXRD , 2003 .

[18]  M. Dokiya,et al.  The oxygen transport in Gd-doped ceria , 2002 .

[19]  Rainer Waser,et al.  Imaging three-dimensional polarization in epitaxial polydomain ferroelectric thin films , 2002 .

[20]  A. Roytburd,et al.  Deformation of adaptive materials. Part III: Deformation of crystals with polytwin product phases , 2001 .

[21]  R. Waser,et al.  Thermodynamic theory of epitaxial ferroelectric thin films with dense domain structures , 2001, cond-mat/0102460.

[22]  F. Güthoff,et al.  Single-Crystal Neutron Diffraction Investigations on the Phase Transitions in CeO1.800 and CeO1.765 , 2000 .

[23]  Mogens Bjerg Mogensen,et al.  Physical, chemical and electrochemical properties of pure and doped ceria , 2000 .

[24]  E. Kümmerle,et al.  The Structures of C–Ce2O3+δ, Ce7O12, and Ce11O20 , 1999 .

[25]  A. Roytburd,et al.  DEFORMATION OF POLYDOMAIN CRYSTALS , 1999 .

[26]  C. Chou,et al.  Banded Structure and Domain Arrangements in PbTiO3 Single Crystals , 1998 .

[27]  S. Alpay,et al.  Thermodynamics of polydomain heterostructures. III. Domain stability map , 1998 .

[28]  A. Roytburd Thermodynamics of polydomain heterostructures. II. Effect of microstresses , 1998 .

[29]  E. Kramer,et al.  Stress relaxation of a main-chain, smectic, polydomain liquid crystalline elastomer , 1998 .

[30]  A. Atkinson Chemically-induced stresses in gadolinium-doped ceria solid oxide fuel cell electrolytes , 1997 .

[31]  Budai,et al.  Domain formation and strain relaxation in epitaxial ferroelectric heterostructures. , 1994, Physical review. B, Condensed matter.

[32]  A. Roytburd Elastic domains and polydomain phases in solids , 1993 .

[33]  R. Fournelle,et al.  A high temperature lattice parameter and dilatometer study of the defect structure of nonstoichiometric cerium dioxide , 1993 .

[34]  M. Wuttig,et al.  Non-local elasticity of polydomain phases , 1992 .

[35]  J. Bravman,et al.  Thickness dependence of the twin density in YBa2Cu3O7−δ thin films sputtered onto MgO substrates , 1991 .

[36]  I. Riess,et al.  Nonstoichiometric phases in cerium oxide , 1988 .

[37]  J. Cahn,et al.  The Interactions of Composition and Stress in Crystalline Solids. , 1984, Journal of research of the National Bureau of Standards.

[38]  C. Catlow,et al.  Dopant ion radius and ionic conductivity in cerium dioxide , 1983 .

[39]  D. Park,et al.  Oxygen-ion conductivity and defect interactions in yttria-doped ceria , 1981 .

[40]  A. L. Roitburd,et al.  Equilibrium structure of epitaxial layers , 1976 .

[41]  A. Tschöpe Interface Defect Chemistry and Effective Conductivity in Polycrystalline Cerium Oxide , 2005 .

[42]  S. Ushioda,et al.  Periodic domain structure and opalescence in barium titanate at the tetragonal to orthorhombic phase transition , 1980 .