Sandwich Structured Composites for Aeronautics: Methods of Manufacturing Affecting Some Mechanical Properties

Sandwich panels are composites which consist of two thin laminate outer skins and lightweight (e.g., honeycomb) thick core structure. Owing to the core structure, such composites are distinguished by stiffness. Despite the thickness of the core, sandwich composites are light and have a relatively high flexural strength. These composites have a spatial structure, which affects good thermal insulator properties. Sandwich panels are used in aeronautics, road vehicles, ships, and civil engineering. The mechanical properties of these composites are directly dependent on the properties of sandwich components and method of manufacturing. The paper presents some aspects of technology and its influence on mechanical properties of sandwich structure polymer composites. The sandwiches described in the paper were made by three different methods: hand lay-up, press method, and autoclave use. The samples of sandwiches were tested for failure caused by impact load. Sandwiches prepared in the same way were used for structural analysis of adhesive layer between panels and core. The results of research showed that the method of manufacturing, more precisely the pressure while forming sandwich panels, influences some mechanical properties of sandwich structured polymer composites such as flexural strength, impact strength, and compressive strength.

[1]  Krishna Shankar,et al.  Insight into the shear behaviour of composite sandwich panels with foam core , 2013 .

[2]  Giovanni Belingardi,et al.  Material characterization of a composite–foam sandwich for the front structure of a high speed train , 2003 .

[3]  Francesco Aymerich,et al.  Damage prediction in composite sandwich panels subjected to low-velocity impact , 2013 .

[4]  A. Vassilopoulos,et al.  Shear mechanical characterization of balsa wood as core material of composite sandwich panels , 2013 .

[5]  Wpływ metody wytwarzania na właściwości laminatów poliestrowo/ szklanych do budowy małych jednostek pływających , 2011 .

[6]  A. Juengert,et al.  Damage Detection in Wind Turbine Blades using two Different Acoustic Techniques , 2008 .

[7]  Alberto Corigliano,et al.  Experimental characterization and numerical simulations of a syntactic foam/glass fibre composite sandwich , 2000 .

[8]  S. Ochelski,et al.  Kompozytowe konstrukcje pochłaniające energię uderzenia , 2007 .

[9]  Forrest J. Masters,et al.  Mechanical resistance properties of FRP/polyol–isocyanate foam sandwich panels , 2013 .

[10]  F. C. Campbell.  Manufacturing technology for aerospace structural materials , 2006 .

[11]  F. C. Campbell.  Structural Composite Materials , 2010 .

[12]  Michael F. Ashby,et al.  Cellular Solids: Cork , 1997 .

[13]  P. Qiao,et al.  Impact analysis of fiber reinforced polymer honeycomb composite sandwich beams , 2007 .

[14]  G. Odegard,et al.  Facesheet delamination of composite sandwich materials at cryogenic temperatures , 2006 .

[15]  M. B. Ioannidis,et al.  A new hybrid concept for sandwich structures , 2008 .

[16]  Uday K. Vaidya,et al.  Thermoplastic sandwich structure design and manufacturing for the body panel of mass transit vehicle , 2007 .

[17]  K. Imielińska,et al.  Badania pękania udarowego w konstrukcjach przekładkowych poliestrowo-szklanych z rdzeniem z pianki PVC , 2007 .

[18]  A. Manalo.  Behaviour of fibre composite sandwich structures under short and asymmetrical beam shear tests , 2013 .

[19]  A. Mouritz,et al.  Fire Properties of Polymer Composite Materials , 2006 .

[20]  F. Avilés,et al.  Mechanical degradation of foam-cored sandwich materials exposed to high moisture , 2010 .

[21]  R. Wool,et al.  All natural composite sandwich beams for structural applications , 2004 .