Reactive pulsed magnetron sputtering process for alumina films

The pulsed magnetron sputtering (PMS) process is now among the leading techniques for the deposition of oxide films. In particular, the use of pulsed dc power has transformed the deposition of dielectric materials, such as alumina. The periodic target voltage reversals during the PMS process effectively discharge poisoned regions on the target. This significantly reduces the occurrence of arc events at the target and stabilizes the deposition process. Many researchers have now shown that pulsed dc reactive magnetron sputtering can be routinely used to produce fully dense, defect-free oxide films. Despite the success of the PMS process, few detailed studies have been carried out on the role played by parameters such as pulse frequency, duty cycle, and reverse voltage in the deposition process. In this study, therefore, alumina films were deposited by reactive pulsed dc magnetron sputtering. Operating conditions were systematically varied and the deposition process monitored throughout. The aim was to inves...

[1]  P. Kelly,et al.  Magnetron sputtering: a review of recent developments and applications , 2000 .

[2]  J. Hölsä,et al.  Properties of zirconium oxide thin films deposited by pulsed reactive magnetron sputtering , 1999 .

[3]  J. Hölsä,et al.  Deposition of aluminium oxide thin films by reactive magnetron sputtering , 1999 .

[4]  A. Belkind,et al.  Using pulsed direct current power for reactive sputtering of Al2O3 , 1999 .

[5]  P. Kelly,et al.  Control of the structure and properties of aluminum oxide coatings deposited by pulsed magnetron sputtering , 1999 .

[6]  W. Sproul.  High-rate reactive DC magnetron sputtering of oxide and nitride superlattice coatings , 1998 .

[7]  J. Szczyrbowski,et al.  Mid frequency sputtering with TwinMag®-a survey of recent results , 1998 .

[8]  A. Belkind,et al.  Pulse duration effects in pulse-power reactive sputtering of Al2O3 , 1998 .

[9]  J. Sellers.  Asymmetric bipolar pulsed DC: the enabling technology for reactive PVD , 1998 .

[10]  Joachim Dr Szczyrbowski,et al.  Mid frequency sputtering — a novel tool for large area coating , 1997 .

[11]  J. Tong,et al.  The deposition of aluminium oxide coatings by reactive unbalanced magnetron sputtering , 1996 .

[12]  P. Yashar,et al.  High-rate reactive d.c. magnetron sputtering of ZrOx coatings , 1996 .

[13]  B. Stauder,et al.  Chemical and structural analysis of aluminium-oxygen coatings obtained by d.c. magnetron reactive sputtering: some features of the process , 1995 .

[14]  M. E. Graham,et al.  Reactive direct current magnetron sputtering of aluminum oxide coatings , 1995 .

[15]  Klaus Goedicke,et al.  Pulsed magnetron sputter technology , 1993 .

[16]  D. Glocker.  Influence of the plasma on substrate heating during low‐frequency reactive sputtering of AIN , 1993 .

[17]  U. Heisig,et al.  Aspects and results of long-term stable deposition of Al2O3 with high rate pulsed reactive magnetron sputtering , 1993 .

[18]  Michael Dr Scherer,et al.  Reactive alternating current magnetron sputtering of dielectric layers , 1992 .