Chronic neural stimulation with thin-film, iridium oxide electrodes

Experiments were conducted to assess the effect of chronic stimulation on the electrical properties of the electrode-tissue system, as measured using electrochemical impedance spectroscopy (EIS) and cyclic voltammetry (CV). Silicon, micromachined probes with multiple iridium oxide stimulating electrodes (400-1600 micron 2) were implanted in guinea pig cortex. A 10-17 day post-operative recovery period was followed by five days of monopolar stimulation, two hours/electrode each day using biphasic, constant current stimulation (5-100 microA, 100 microseconds/phase). EIS and CV data were taken before and after stimulation. The post-stimulation impedance [at mid-range frequencies (100 Hz-100 kHz)] consistently and significantly decreased relative to prestimulation levels. Impedance magnitude increased permanently at low frequencies (< 100 Hz), correlating to a change in the charge storage capacity (the area under a cyclic voltammagram). Impedance magnitude significantly increased during the recovery period, though this increase could be mostly reversed by applying small currents. A mathematical model of the electrode-tissue system impedance was used to analyze in vivo behavior. The data and modeling results shows that applying charge to the electrode can consistently reduce the impedance of the electrode-tissue system. Analysis of explanted probes suggests that the interaction between the tissue and electrode is dependent on whether chronic pulses were applied. It is hypothesized that the interface between the tissue and metal is altered by current pulsing, resulting in a temporary impedance shift.

[1]  D. McCreery,et al.  Neuronal activity evoked by chronically implanted intracortical microelectrodes , 1986, Experimental Neurology.

[2]  B. Aurian‐Blajeni,et al.  The numerical inversion of the Laplace transform applied to impedance spectroscopy , 1992 .

[3]  J. Ross Macdonald,et al.  Note on the parameterization of the constant-phase admittance element , 1984 .

[4]  B. Conway Transition from “Supercapacitor” to “Battery” Behavior in Electrochemical Energy Storage , 1991 .

[5]  S. B. Brummer,et al.  Electrical stimulation of the nervous system: The principle of safe charge injection with noble metal electrodes , 1975 .

[6]  L A Bullara,et al.  Effects of electrical stimulation of brain. , 1977, Brain, behavior and evolution.

[7]  W. Kenan,et al.  Impedance Spectroscopy: Emphasizing Solid Materials and Systems , 1987 .

[8]  D.B. McCreery,et al.  Charge density and charge per phase as cofactors in neural injury induced by electrical stimulation , 1990, IEEE Transactions on Biomedical Engineering.

[9]  X. Beebe,et al.  Charge injection limits of activated iridium oxide electrodes with 0.2 ms pulses in bicarbonate buffered saline (neurological stimulation application) , 1988, IEEE Transactions on Biomedical Engineering.

[10]  S. Glarum,et al.  The A‐C Response of Iridium Oxide Films , 1980 .

[11]  Allen J. Bard,et al.  Electroanalytical Chemistry: A Series of Advances , 1974 .

[12]  D. McCreery,et al.  Histopathologic evaluation of prolonged intracortical electrical stimulation , 1986, Experimental Neurology.

[13]  D.J. Anderson,et al.  Batch fabricated thin-film electrodes for stimulation of the central auditory system , 1989, IEEE Transactions on Biomedical Engineering.

[14]  S. B. Brummer,et al.  Activated Ir: An Electrode Suitable for Reversible Charge Injection in Saline Solution , 1983 .

[15]  T. L. Rose,et al.  Impedance of hydrated iridium oxide electrodes , 1989 .

[16]  F. Hambrecht,et al.  CRITERIA FOR SELECTING ELECTRODES FOR ELECTRICAL STIMULATION: THEORETICAL AND PRACTICAL CONSIDERATIONS , 1983, Annals of the New York Academy of Sciences.

[17]  K. Wise,et al.  A 16-channel CMOS neural stimulating array , 1992, 1992 IEEE International Solid-State Circuits Conference Digest of Technical Papers.

[18]  William F. Agnew,et al.  Electrical Characteristics of Chronically Implanted Platinum-Irdium Electrodes , 1987, IEEE Transactions on Biomedical Engineering.

[19]  P. Pickup,et al.  A MODEL FOR ANODIC HYDROUS OXIDE GROWTH AT IRIDIUM , 1987 .

[20]  D. Robinson,et al.  The electrical properties of metal microelectrodes , 1968 .

[21]  U. M. Twardoch,et al.  Integrity of ultramicro-stimulation electrodes determined from electrochemical measurements , 1994 .

[22]  B. Conway,et al.  Transition from 'supercapacitor' to 'battery' behavior in electrochemical energy storage , 1990, Proceedings of the 34th International Power Sources Symposium.

[23]  B. Lengeler,et al.  Valency and Structure of Iridium in Anodic Iridium Oxide Films , 1993 .

[24]  John R. Scully,et al.  Basic Aspects of Electrochemical Impedance Application for the Life Prediction of Organic Coatings on Metals , 1990 .

[25]  W. Scheider Theory of the frequency dispersion of electrode polarization. Topology of networks with fractional power frequency dependence , 1975 .

[26]  M. Petty,et al.  IMPEDANCE SPECTROSCOPY OF BIOMEMBRANE LANGMUIR-BLODGETT FILMS , 1994 .