The electrical resistivity of ordered Fe3–xPt1+x alloys containing 20, 22, 24, 26, 28, and 30 at % Pt is studied with increasing and decreasing temperatures between 4 and 1200 K. Special attention is given to anomalies due to phase transitions, such as α-γ transition, Martensitic transition, magnetic phase transition, order-disorder transition, etc. A new phase is found to exist at low temperatures (T < 240 K) for alloys with 26, 28, and 30 at % Pt. Both, α-γ transition and the transition to the new phase exhibit hysteresis in the electrical resistivity curves. The Curie temperature and order-disorder temperature is determined from the maxima of dϱ/dT versus T curve. The complete phase diagram is also shown.
Der elektrische Widerstand von geordneten Fe3–xPt1+x- Legierungen mit 20, 22, 24, 26, 28 und 30 At % Pt wird bei steigenden und fallenden Temperaturen im Bereich von 4 bis 1200 K untersucht. Besonders beobachtet werden die Anomalien, die durch Phasenubergange wie α-γ-ubergang, Martensit-ubergang, magnetischer Phasenubergang, Ordnungs-Fehlordnungs-ubergang usw. hervorgerufen werden. Es wird gefunden, das fur Legierungen mit 26, 28 und 30 At % Pt bei niedrigen Temperaturen (T < 240 K) eine neue Phase existiert. Sowohl der α-γ-ubergang als auch der ubergang in die neue Phase zeigen eine Hysterese der Verlaufe des elektrischen Widerstands. Die Curie-Temperatur und die Ordnungs-Fehlordnungstemperatur werden aus den Maxima des dϱ/dT uber T-Verlaufs bestimmt. Ein vollstandiges Phasendiagramm wird ebenfalls angegeben.
[1]
Y. Yao,et al.
Electrical Resistivity and Magnetization Studies of Some Commercial Steels
,
1986,
November 16.
[2]
S. B. Woods,et al.
The electrical resistance of some lithium-magnesium alloys near the martensitic transformation
,
1985
.
[3]
Y. Nakamura,et al.
Magnetic and magnetovolume properties of Fe-Pt alloys around γ-α phase boundary
,
1983
.
[4]
Y. Yao,et al.
Electrical resistivity of Fe-Rich FePd alloys between 77 and 1250 K
,
1981
.
[5]
O. Caporaletti,et al.
Direct comparison of the magnetic properties of ordered and disordered Fe3−xPt1+x alloys at low temperatures
,
1979
.
[6]
C. M. Wayman,et al.
The effect of austenite ordering on the transformation temperature, transformation hysteresis, and thermoelastic behavior in Fe- Pt alloys
,
1978
.
[7]
M. Seehra,et al.
Order-disorder and α − γ transitions in FeCo
,
1976
.
[8]
D. Geldart,et al.
Theory of spin-fluctuation resistivity near the critical point of ferromagnets
,
1975
.
[9]
M. Salamon,et al.
Specific Heat and Resistivity Near the Order-Disorder Transition in β-Brass
,
1971
.