Plasticity of high purity iron single crystals (I) 1. work hardening

High purity iron single crystals were deformed in tension in the temperature range 4.2 to 473 K. Work-hardening characteristics were determined and the plastic behaviour in dependence on temperature, strain rate and crystal orientation isz discussed. The transition temperature between low-temperature and intermediate-temperature deformation regimes was found to be ≅ 250 K, the critical temperature estimated from the temperature dependence of the critical resolved shear stress is ≅ 380 K. A hump on the temperature dependence of the critical resolved shear stress was observed in the vicinity of 250 K. These observations are qualitatively explained by special mobilities of dislocations in b.c.c. lattice. Hochreine Eisen-Einkristalle wurden im Temperaturbereich 4,2 bis 473 K zugverformt. Die Verfestigungscharakteristika wurden bestimmt, und das plastische Verhalten in Abhangigkeit von Temperatur, Verformungsrate und Kristallorientierung wird diskutiert. Die Ubergangstemperatur zwischen Tieftemperatur- und Zwischentemperaturregime wurde zu etwa 250 K gefunden; die kritische Temperatur, abgeschatzt aus der Temperaturabhangigkeit der kritischen bezogenen Schubspannung, betragt ca. 380 K. Ein Buckel in der Temperaturabhangigkeit der kritischen bezogenen Schubspannung wurde in der Umgebung von 250 K beobachtet. Dies ist durch spezielle Beweglichkeiten der Versetzungen im krz-Gitter erklarbar.