Effect of operating temperature on degradation of solder joints in crystalline silicon photovoltaic modules for improved reliability in hot climates

Abstract Accelerated degradation of solder joint interconnections in crystalline silicon photovoltaic (c-Si PV) modules drives the high failure rate of the system operating in elevated temperatures. The phenomenon challenges the thermo-mechanical reliability of the system for hot climatic operations. This study investigates the degradation of solder interconnections in c-Si PV modules for cell temperature rise from 25 °C STC in steps of 1 °C to 120 °C. The degradation is measured using accumulated creep strain energy density ( W acc ) . Generated W acc magnitudes are utilised to predict the fatigue life of the module for ambient temperatures ranging from European to hot climates. The ANSYS mechanical package coupled with the IEC 61,215 standard accelerated thermal cycle (ATC) profile is employed in the simulation. The Garofalo creep model is used to model the degradation response of solder while other module component materials are simulated with appropriate material models. Solder degradation is found to increase with every 1 °C cell temperature rise from the STC. Three distinct degradation rates in Pa/°C are observed. Region 1, 25 to 42 °C, is characterised by degradation rate increasing quadratically from 1.53 to 10.03 Pa/°C. The degradation rate in region 2 ,43 to 63 °C, is critical with highest constant magnitude of 12.06 Pa/°C. Region 3, 64 to 120 °C, demonstrates lowest degradation rate of logarithmic nature with magnitude 5.47 at the beginning of the region and 2.25 Pa/°C at the end of the region. The module fatigue life, L (in years) is found to decay according to the power function L = 721.48 T - 1.343 . The model predicts module life in London and hot climate to be 18.5 and 9 years, respectively. The findings inform on the degradation of c-Si PV module solder interconnections in different operating ambient temperatures and advise on its operational reliability for improved thermo-mechanical design for hot climatic operations.

[1]  K. Agroui,et al.  Determination of thermal properties of crosslinked EVA encapsulant material in outdoor exposure by TSC and DSC methods , 2014 .

[2]  E. Skoplaki,et al.  ON THE TEMPERATURE DEPENDENCE OF PHOTOVOLTAIC MODULE ELECTRICAL PERFORMANCE: A REVIEW OF EFFICIENCY/ POWER CORRELATIONS , 2009 .

[3]  S. Kurtz,et al.  Outdoor PV degradation comparison , 2010, 2010 35th IEEE Photovoltaic Specialists Conference.

[4]  Jae-Seong Jeong,et al.  Field failure mechanism study of solder interconnection for crystalline silicon photovoltaic module , 2012, Microelectron. Reliab..

[5]  O. S. Sastry,et al.  Effect of irradiance, temperature exposure and an Arrhenius approach to estimating weathering acceleration factor of Glass, EVA and Tedlar in a composite climate of India , 2017 .

[6]  Marco Paggi,et al.  A multi-physics and multi-scale numerical approach to microcracking and power-loss in photovoltaic modules , 2013, 1303.7452.

[7]  M. Paggi,et al.  A reaction-diffusion formulation to simulate EVA polymer degradation in environmental and accelerated ageing conditions , 2017 .

[8]  Thomas Reindl,et al.  Performance Degradation of Various PV Module Technologies in Tropical Singapore , 2014, IEEE Journal of Photovoltaics.

[9]  D. L. King,et al.  Analysis of factors influencing the annual energy production of photovoltaic systems , 2002, Conference Record of the Twenty-Ninth IEEE Photovoltaic Specialists Conference, 2002..

[10]  Dallemand Jean-Francois,et al.  Renewable energies in Africa : current knowledge , 2011 .

[11]  H.M.S. Hussein,et al.  Performance evaluation of photovoltaic modules at different tilt angles and orientations , 2004 .

[12]  Bharath Seshadri,et al.  Temperature Dependent Photovoltaic (PV) Efficiency and Its Effect on PV Production in the World – A Review☆ , 2013 .

[13]  Ahmer Syed,et al.  Predicting solder joint reliability for thermal, power, and bend cycle within 25% accuracy , 2001, 2001 Proceedings. 51st Electronic Components and Technology Conference (Cat. No.01CH37220).

[14]  M. Paggi,et al.  A 3D coupled thermo-visco-elastic shear-lag formulation for the prediction of residual stresses in photovoltaic modules after lamination , 2016 .

[15]  Weiwen Peng,et al.  Thermal Cycling Life Prediction of Sn-3.0Ag-0.5Cu Solder Joint Using Type-I Censored Data , 2014, TheScientificWorldJournal.

[16]  A. Syed.  Accumulated creep strain and energy density based thermal fatigue life prediction models for SnAgCu solder joints , 2004, 2004 Proceedings. 54th Electronic Components and Technology Conference (IEEE Cat. No.04CH37546).

[17]  Ndy Ekere,et al.  A review of interconnection technologies for improved crystalline silicon solar cell photovoltaic module assembly , 2015 .

[18]  George Makrides,et al.  Review of photovoltaic degradation rate methodologies , 2014 .

[19]  Michael G. Pecht,et al.  Creep fatigue models of solder joints: A critical review , 2016, Microelectron. Reliab..

[20]  Fu Guo,et al.  Damage behavior of SnAgCu/Cu solder joints subjected to thermomechanical cycling , 2013 .

[21]  Kei Obinata.  Geometrical Optimization of Arrangement of Solar Cells in Photovoltaic Modules , 2011 .

[22]  H. Reichl,et al.  Fatigue life models for SnAgCu and SnPb solder joints evaluated by experiments and simulation , 2003, 53rd Electronic Components and Technology Conference, 2003. Proceedings..

[23]  Dirk Jordan,et al.  Photovoltaic failure and degradation modes , 2017 .

[24]  David Moser,et al.  Monitoring of Photovoltaic Systems: Good Practices and Systematic Analysis , 2013 .

[25]  E. Skoplaki,et al.  Operating temperature of photovoltaic modules: A survey of pertinent correlations , 2009 .

[26]  H. Beyer,et al.  Mapping the performance of PV modules, effects of module type and data averaging , 2010 .

[27]  Emeka H. Amalu,et al.  A review of photovoltaic module technologies for increased performance in tropical climate , 2017 .

[28]  M. Paggi,et al.  A geometrical multi-scale numerical method for coupled hygro-thermo-mechanical problems in photovoltaic laminates , 2016, Computational Mechanics.

[29]  Nduka Nnamdi (Ndy) Ekere,et al.  Damage of lead-free solder joints in flip chip assemblies subjected to high-temperature thermal cycling , 2012 .

[30]  M. Paggi,et al.  Thermomechanical deformations in photovoltaic laminates , 2011 .

[31]  Daniel Philipp,et al.  Why Do PV Modules Fail , 2012 .

[32]  Nick Bosco.  Reliability Concerns Associated with PV Technologies , 2010 .

[33]  S. Tanpichai,et al.  Enhancement of thermal, mechanical and barrier properties of EVA solar cell encapsulating films by reinforcing with esterified cellulose nanofibres , 2015 .

[34]  Yoshiharu Mutoh,et al.  Fatigue crack-growth behavior of Sn-Ag-Cu and Sn-Ag-Cu-Bi lead-free solders , 2002 .

[35]  H. Walter,et al.  Constitutive behaviour of lead-free solders vs. lead-containing solders-experiments on bulk specimens and flip-chip joints , 2001, 2001 Proceedings. 51st Electronic Components and Technology Conference (Cat. No.01CH37220).

[36]  G. Petrone,et al.  Quantification of photovoltaic module degradation using model based indicators , 2017, Math. Comput. Simul..

[37]  B. Henke,et al.  PV module defect detection by combination of mechanical and electrical analysis methods , 2010, 2010 35th IEEE Photovoltaic Specialists Conference.

[38]  NON-LINEAR MECHANICAL PROPERTIES OF ETHYLENE-VINYL ACETATE (EVA) AND ITS RELEVANCE TO THERMOMECHANICS OF PHOTOVOLTAIC MODULES , 2010 .

[39]  M. Nagaraju Naik,et al.  Degradation analysis of 28 year field exposed mono-c-Si photovoltaic modules of a direct coupled solar water pumping system in western Himalayan region of India , 2015 .

[40]  Alberto Giuseppe Sapora,et al.  An Accurate Thermoviscoelastic Rheological Model for Ethylene Vinyl Acetate Based on Fractional Calculus , 2015 .

[41]  Paresh Limaye,et al.  Hermal cycling reliability of snagcu and snpb solder joints: a comparison for several ic-packages , 2004, 5th International Conference on Thermal and Mechanical Simulation and Experiments in Microelectronics and Microsystems, 2004. EuroSimE 2004. Proceedings of the.

[42]  M. Paggi,et al.  Fatigue crack growth in Silicon solar cells and hysteretic behaviour of busbars , 2018, Solar Energy Materials and Solar Cells.

[43]  Dirk C. Jordan,et al.  Photovoltaic Degradation Rates—an Analytical Review , 2012 .

[44]  F. Chenlo,et al.  Early degradation of silicon PV modules and guaranty conditions , 2011 .

[45]  Archana Sinha,et al.  Nondestructive characterization of encapsulant discoloration effects in crystalline-silicon PV modules , 2016 .

[46]  Ibidun O. Adelekan,et al.  Air temperature, relative humidity, climate regionalization and thermal comfort of Nigeria , 2014 .

[47]  P. Lall,et al.  The effects of aging on the cyclic stress-strain behavior and hysteresis loop evolution of lead free solders , 2011, 2011 IEEE 61st Electronic Components and Technology Conference (ECTC).

[48]  M. Paggi,et al.  Fatigue degradation and electric recovery in Silicon solar cells embedded in photovoltaic modules , 2014, Scientific Reports.

[49]  Mei-Ling Wu,et al.  Failure of lead-free solder joint under thermal cycling , 2011, 2011 6th International Microsystems, Packaging, Assembly and Circuits Technology Conference (IMPACT).

[50]  Abdessamad Kobi,et al.  Degradations of silicon photovoltaic modules: A literature review , 2013 .

[51]  Jan K. Spelt,et al.  Effect of geometry on the fracture behavior of lead-free solder joints , 2011 .

[52]  Abdessamad Kobi,et al.  Degradation evaluation of crystalline-silicon photovoltaic modules after a few operation years in a tropical environment , 2014 .

[53]  Marco Paggi,et al.  A thermo-visco-elastic shear-lag model for the prediction of residual stresses in photovoltaic modules after lamination , 2016 .

[54]  Holm Altenbach,et al.  Thermomechanics of PV Modules Including the Viscoelasticity of EVA , 2011 .

[55]  Marko Topič,et al.  Outdoor testing of PV module temperature and performance under different mounting and operational conditions , 2011 .

[56]  D. Das,et al.  Thermal Cycling Reliability of Lead-Free Solders (SAC305 and Sn3.5Ag) for High-Temperature Applications , 2011, IEEE Transactions on Device and Materials Reliability.

[57]  Emeka H. Amalu,et al.  A study of SnAgCu solder paste transfer efficiency and effects of optimal reflow profile on solder deposits , 2011 .

[58]  Gregory A. Keoleian,et al.  Parameters affecting the life cycle performance of PV technologies and systems , 2007 .

[59]  Emeka H. Amalu,et al.  Prediction of damage and fatigue life of high-temperature flip chip assembly interconnections at operations , 2012, Microelectron. Reliab..

[60]  E. Skoplaki,et al.  A simple correlation for the operating temperature of photovoltaic modules of arbitrary mounting , 2008 .

[61]  Y. Mulugetta,et al.  Power generation scenarios for Nigeria: An environmental and cost assessment , 2011 .

[62]  S. Bordas,et al.  Lifetime prediction for solder joints with the extended finite element method , 2011, 2011 12th Intl. Conf. on Thermal, Mechanical & Multi-Physics Simulation and Experiments in Microelectronics and Microsystems.