Thickness Dependency of Thin-Film Samaria-Doped Ceria for Oxygen Sensing

High-temperature oxygen sensors are widely used for exhaust gas monitoring in automobiles. This particular study explores the use of thin-film single crystalline samaria-doped ceria as the oxygen sensing material. Desired signal-to-noise ratio can be achieved in a material system with high conductance. From previous studies, it is established that 6 atomic percent samarium doping is the optimum concentration for thin-film samaria-doped ceria (SDC) to achieve high ionic conductivity. In this study, the conductance of the 6 atomic percent samaria-doped ceria (SDC) thin film is measured as a function of the sensing film thickness. Hysteresis and dynamic response of this sensing platform are tested for a range of oxygen pressures from 0.001 to 100 torr for temperatures above 673 K. An attempt has been made to understand the physics behind the thickness-dependent conductance of this sensing platform by developing a hypothetical operating model and through COMSOL simulations. This study can be used to identify the parameters required to construct a fast, reliable, and compact high-temperature oxygen sensor.

[1]  J. Giber,et al.  Auger and SIMS study of segregation and corrosion behaviour of some semiconducting oxide gas-sensor materials , 1994 .

[2]  M. C. Bhatnagar,et al.  Improvement of the oxygen gas sensitivity in doped TiO2 thick films , 1999 .

[3]  W. Shin,et al.  Fast response of resistive-type oxygen gas sensors based on nano-sized ceria powder , 2003 .

[4]  M. Engelhard,et al.  Conductivity of Oriented Samaria-Doped Ceria Thin Films Grown by Oxygen-plasma-assisted Molecular Beam Epitaxy , 2008 .

[5]  Joseph R. Stetter,et al.  Kinetics of indium oxide-based thin film gas sensor response: The role of “redox” and adsorption/desorption processes in gas sensing effects , 2007 .

[6]  Nguyen Q. Minh,et al.  Chapter 4 – Electrolyte , 1995 .

[7]  Ichiro Matsubara,et al.  Evaluation of response characteristics of resistive oxygen sensors based on porous cerium oxide thick film using pressure modulation method , 2006 .

[8]  O. Toft Sørensen,et al.  Oxygen sensors based on semiconducting metal oxides: an overview , 2000 .

[9]  M. Engelhard,et al.  Influence of samaria doping on the resistance of ceria thin films and its implications to the planar oxygen sensing devices , 2009 .

[10]  Min-Hsiung Hon,et al.  The effects of thickness and operation temperature on ZnO:Al thin film CO gas sensor , 2002 .

[11]  Ellen Ivers-Tiffée,et al.  Principles of solid state oxygen sensors for lean combustion gas control , 2001 .

[12]  Prabir K. Dutta,et al.  Oxygen sensors: Materials, methods, designs and applications , 2003 .

[13]  Harry L. Tuller,et al.  Ionic conduction in nanocrystalline materials , 2000 .

[14]  H.-J. Beie,et al.  Oxygen gas sensors based on CeO2 thick and thin films , 1991 .

[15]  J. Lando,et al.  Gas-sensing mechanism of phthalocyanine Langmuir-Blodgett films , 1994 .

[16]  J. Hsieh,et al.  Response characteristics of lead phthalocyanine gas sensor: effects of film thickness and crystal morphology , 1998 .

[17]  Ralf Moos,et al.  Materials for temperature independent resistive oxygen sensors for combustion exhaust gas control , 2000 .

[18]  Ichiro Matsubara,et al.  On the platinum sensitization of nanosized cerium dioxide oxygen sensors , 2003 .

[19]  Uwe Lampe,et al.  Thin-film gas sensors based on semiconducting metal oxides , 1995 .

[20]  Ichiro Matsubara,et al.  Response properties of resistive oxygen sensors using Ce1−xZrxO2 (x = 0.05, 0.10) thick films in propane combustion gas , 2008 .