Three-dimensional investigation of cycling-induced microstructural changes in lithium-ion battery cathodes using focused ion beam/scanning electron microscopy

For vehicle electrification, one of the biggest issues for lithium ion batteries is cycle life. Within this context, the mechanisms at the source of capacity degradation during cycling are not yet to be fully understood. In this work, we use state-of-the-art FIB-SEM serial sectioning and imaging techniques to determine the effect of cycling on lithium-ion battery cathodes. The three-dimensional (3D) microstructural study was performed on both pristine and cycled LiNixMnyCo1−x−yO2 (NMC) and Li(Li0.2Ni0.13Mn0.54Co0.13)O2 (HE-NMC) cathodes. The spatial distribution of active material, carbon-doped binder and pore spaces were successfully reconstructed by appropriate image processing. Comparisons of NMC and HE-NMC cathodes after different number of cycles showed only minor increases in the number of smaller active particles, possibly negligible, considering the intrinsic microstructure variation within the cathodes. However, the connectivity between carbon-doped binder additives and active particles in NMC and HE-NMC cathodes, assessed using a “neighbor counting” method, showed an appreciable decrease after cycling which indicates a detachment of carbon-doped binder from active particles. This significant cycling-induced detachment effect between the two phases (e.g., ∼22% for HE-NMC) could indicate a loss in electrical connectivity, which may partially explain the capacity fade in the cells.

[1]  Steen B. Schougaard,et al.  Effective Transport Properties of Porous Electrochemical Materials — A Homogenization Approach , 2014 .

[2]  Prashant N. Kumta,et al.  Interfacial Properties of the a-Si ∕ Cu :Active–Inactive Thin-Film Anode System for Lithium-Ion Batteries , 2006 .

[3]  P. Novák,et al.  A review of the features and analyses of the solid electrolyte interphase in Li-ion batteries , 2010 .

[4]  A. Sastry,et al.  Particle Compression and Conductivity in Li-Ion Anodes with Graphite Additives , 2004 .

[5]  Jun Wang,et al.  Tortuosity characterization of 3D microstructure at nano-scale for energy storage and conversion materials , 2014 .

[6]  Ying Shirley Meng,et al.  In-situ neutron diffraction study of the xLi2MnO3·(1 − x)LiMO2 (x = 0, 0.5; M = Ni, Mn, Co) layered oxide compounds during electrochemical cycling , 2013 .

[7]  J. Dahn,et al.  Electrochemical and In Situ X‐Ray Diffraction Studies of Lithium Intercalation in Li x CoO2 , 1992 .

[8]  Moses Ender,et al.  Three-dimensional reconstruction of a composite cathode for lithium-ion cells , 2011 .

[9]  K. Amine,et al.  Nanoscale Phase Separation, Cation Ordering, and Surface Chemistry in Pristine Li1.2Ni0.2Mn0.6O2 for Li-Ion Batteries , 2013 .

[10]  Moses Ender,et al.  Quantitative Characterization of LiFePO4 Cathodes Reconstructed by FIB/SEM Tomography , 2012 .

[11]  J. Colin,et al.  First evidence of manganese-nickel segregation and densification upon cycling in Li-rich layered oxides for lithium batteries. , 2013, Nano letters.

[12]  K. Smith,et al.  Evidence for Anisotropic Mechanical Behavior and Nanoscale Chemical Heterogeneity in Cycled LiCoO2 , 2014 .

[13]  Miaofang Chi,et al.  Identifying surface structural changes in layered Li-excess nickel manganese oxides in high voltage lithium ion batteries: A joint experimental and theoretical study , 2011 .

[14]  Stephen J. Harris,et al.  Measurement of three-dimensional microstructure in a LiCoO2 positive electrode , 2011 .

[15]  Nigel P. Brandon,et al.  Characterization of the 3-dimensional microstructure of a graphite negative electrode from a Li-ion battery , 2010 .

[16]  Y. Koyama,et al.  Defect Chemistry in Layered LiMO2 (M = Co, Ni, Mn, and Li1/3Mn2/3) by First-Principles Calculations , 2012 .

[17]  D. Stephenson,et al.  Modeling 3D Microstructure and Ion Transport in Porous Li-Ion Battery Electrodes , 2011 .

[18]  M. Winter,et al.  Investigation of thermal aging and hydrolysis mechanisms in commercial lithium ion battery electrolyte , 2013 .

[19]  Hun‐Gi Jung,et al.  Improved Co-substituted, LiNi0.5−xCo2xMn1.5−xO4 lithium ion battery cathode materials , 2012 .

[20]  Nigel P. Brandon,et al.  Lithiation‐Induced Dilation Mapping in a Lithium‐Ion Battery Electrode by 3D X‐Ray Microscopy and Digital Volume Correlation , 2014 .

[21]  G. G. Stokes.  "J." , 1890, The New Yale Book of Quotations.

[22]  K. Sun,et al.  Three dimensional studies of particle failure in silicon based composite electrodes for lithium ion batteries , 2014 .

[23]  Marco Stampanoni,et al.  Visualization and Quantification of Electrochemical and Mechanical Degradation in Li Ion Batteries , 2013, Science.

[24]  James McBreen,et al.  In situ X-ray diffraction and X-ray absorption studies of high-rate lithium-ion batteries , 2001 .

[25]  P. Shearing,et al.  Three-dimensional high resolution X-ray imaging and quantification of lithium ion battery mesocarbon microbead anodes , 2014 .

[26]  Stephen J. Harris,et al.  In Situ Observation of Strains during Lithiation of a Graphite Electrode , 2010 .

[27]  Kristina Edström,et al.  Recent findings and prospects in the field of pure metals as negative electrodes for Li-ion batteries , 2007 .

[28]  Tsutomu Ohzuku,et al.  Novel lithium insertion material of LiCo1/3Ni1/3Mn1/3O2 for advanced lithium-ion batteries , 2003 .

[29]  Y. K. Chen-Wiegart,et al.  Three-dimensional morphological measurements of LiCoO2 and LiCoO2/Li(Ni1/3Mn1/3Co1/3)O2 lithium-ion battery cathodes , 2013 .

[30]  Nigel P. Brandon,et al.  Local Tortuosity Inhomogeneities in a Lithium Battery Composite Electrode , 2011 .

[31]  D. Wheeler,et al.  A Combination of X‐Ray Tomography and Carbon Binder Modeling: Reconstructing the Three Phases of LiCoO2 Li‐Ion Battery Cathodes , 2014 .

[32]  Robert J. Flatt,et al.  FIB-Nanotomography of Particulate Systems—Part I: Particle Shape and Topology of Interfaces , 2006 .

[33]  Tao Sun,et al.  Unveiling the Roles of Binder in the Mechanical Integrity of Electrodes for Lithium-Ion Batteries , 2013 .

[34]  Leilei Yin,et al.  Simulation of heat generation in a reconstructed LiCoO2 cathode during galvanostatic discharge , 2013 .

[35]  Tsutomu Ohzuku,et al.  Crystal and electronic structures of superstructural Li1−x[Co1/3Ni1/3Mn1/3]O2 (0≤x≤1) , 2003 .

[36]  Ji‐Guang Zhang,et al.  Corrosion/fragmentation of layered composite cathode and related capacity/voltage fading during cycling process. , 2013, Nano letters.

[37]  Ilias Belharouak,et al.  Li(Ni1/3Co1/3Mn1/3)O2 as a suitable cathode for high power applications , 2003 .

[38]  Feng Lin,et al.  Surface reconstruction and chemical evolution of stoichiometric layered cathode materials for lithium-ion batteries , 2014, Nature Communications.

[39]  Daniel P. Abraham,et al.  Surface changes on LiNi0.8Co0.2O2 particles during testing of high-power lithium-ion cells , 2002 .

[40]  L. Christophorou.  Science , 2018, Emerging Dynamics: Science, Energy, Society and Values.

[41]  Ying Shirley Meng,et al.  Phase Transitions and High-Voltage Electrochemical Behavior of LiCoO2 Thin Films Grown by Pulsed Laser Deposition , 2007 .

[42]  B. Scrosati,et al.  A new, high energy Sn-C/Li[Li(0.2)Ni(0.4)/3Co(0.4)/3Mn(1.6/3)]O2 lithium-ion battery. , 2014, ACS applied materials & interfaces.

[43]  Y. K. Chen-Wiegart,et al.  3D analysis of a LiCoO2–Li(Ni1/3Mn1/3Co1/3)O2 Li-ion battery positive electrode using x-ray nano-tomography , 2013 .

[44]  Daniel P. Abraham,et al.  Layered Li(Ni0.5−xMn0.5−xM2x′)O2 (M′=Co, Al, Ti; x=0, 0.025) cathode materials for Li-ion rechargeable batteries , 2002 .