Effects of Matrix Porosity on the Mechanical Properties of a Porous‐Matrix, All‐Oxide Ceramic Composite

The effects of matrix porosity on the mechanical properties of an all-oxide ceramic composite are investigated. The porosity is varied through impregnation and pyrolysis of a ceramic precursor solution. Mechanical tests are performed to assess the role of the matrix in both matrix-dominated and fiber-dominated loading configurations. The results demonstrate a loss in damage tolerance and tensile strength along the fiber direction as the porosity is reduced. Concomitantly, some improvements in interlaminar strength are obtained. The latter improvements are found to be difficult to quantify over the entire porosity range using the standard short beam shear method, a consequence of the increased propensity for tensile fracture as the porosity is reduced. Measurements of interlaminar shear strength based on the double-notched shear specimen are broadly consistent with the limited values obtained by the short beam shear method, although the former exhibit large variability. In addition, effects of precursor segregation during drying on through-thickness gradients in matrix properties and their role in composite performance are identified and discussed. An analysis based on the mechanics of crack deflection and penetration at an interphase boundary is presented and used to draw insights regarding the role of matrix properties in enabling damage tolerance in porous-matrix composites. Deficiencies in the understanding of the mechanisms that enable damage tolerance in this class of composites are discussed.