Cutting tool wear in the machining of hardened steels: Part I: alumina/TiC cutting tool wear

Abstract A study was undertaken to investigate the mechanisms of alumina/TiC cutting tool wear in the finish turning of hardened steels with particular cognisance of the work material inclusion content. A six-fold variation in tool life was observed when machining different heats of BS 817M40 steel (similar to AISI 4340) of 52 HRC. In machining steels containing Ca-bearing mixed oxide inclusions, a reaction between the alumina phase of the tool and oxide inclusionary deposits is the dominant wear mechanism. In machining steels containing very low levels of Ca or steels with a very low inclusion content, tool wear appears to be largely based on superficial plastic deformation of the tool surface. The rate of tool wear appears to be determined by the hard inclusion content or alloy carbide content of the work material. Impingement of hard particles against the tool surface are thought to result in the generation of transient localised stresses which exceed the average contact pressures and, thus, either facilitate the operation of additional slip systems or overcome the increases in the critical resolved shear stresses on active slip systems due to prior strain. The influence of saw-tooth chip formation on cutting tool wear is also considered.

[1]  Toshiyuki Obikawa,et al.  Wear characteristic of alumina coated and alumina ceramic tools , 1997 .

[2]  S. Kato,et al.  Stress Distribution at the Interface Between Tool and Chip in Machining , 1972 .

[3]  M. Mikus,et al.  The formation of protective layers when machining steel with ceramic cutting tools , 1987 .

[4]  Sakari Ruppi,et al.  Microstructural changes in CVD κ-Al2O3 coated cutting tools during turning operations , 1999 .

[5]  Gerry Byrne,et al.  Cutting tool wear in the machining of hardened steels , 2001 .

[6]  Yuji Katsumura,et al.  Effects of TiC Content and Grain Size on Cutting Performance of Al2O3-TiC Ceramic Tools , 1993 .

[7]  D. Hasselman,et al.  Evidence for dislocation‐controlled crater wear of polycrystalline aluminum oxide cutting tools , 1973 .

[8]  M. Lahres,et al.  Quantitative measurement of temperatures on diamond-coated tools during machining , 1995 .

[9]  G. Brandt,et al.  Flank and crater wear mechanisms of alumina-based cutting tools when machining steel , 1986 .

[10]  Arthur H. Heuer,et al.  Slip and Twinning in Sapphire (α‐Al2O3) , 1994 .

[11]  H. Tönshoff,et al.  Wear mechanisms of ceramic cutting tools , 1988 .

[12]  Christopher J. Evans,et al.  White Layers and Thermal Modeling of Hard Turned Surfaces , 1997, Manufacturing Science and Engineering: Volume 2.

[13]  Hans Kurt Tönshoff,et al.  Cutting of Hardened Steel , 2000 .

[14]  Takashi Ueda,et al.  Temperature Measurement of CBN Tool in Turning of High Hardness Steel , 1999 .

[15]  Y. Yamane,et al.  The formation of a protective oxide layer in machining resulphurized free-cutting steels and cast irons , 1990 .

[16]  Soon Chong Johnson Lim,et al.  Transitions in wear mechanisms of alumina cutting tools , 1996 .

[17]  G. Brandt,et al.  An electron microprobe and cathodoluminescence study of chemical reactions between tool and workpiece when turning steel with alumina-based ceramics , 1987 .

[18]  G. Byrne,et al.  The mechanisms of chip formation in machining hardened steels , 2002 .

[19]  S. Subramanian,et al.  Micromechanisms of tool wear in machining free cutting steels , 1996 .

[20]  Fukuo Hashimoto,et al.  Surface Integrity Generated by Precision Hard Turning , 1999 .

[21]  N. Narutaki,et al.  Wear Characteristics of Ceramic Tools , 1973 .