论文信息 - Influence of shot peening on the fatigue life of laser hardened 17-4PH steel

Influence of shot peening on the fatigue life of laser hardened 17-4PH steel

In order to improve the fatigue life of 17-4PH steel after laser hardening treatment, shot peening and dual shot peening treatments were performed on laser hardened 17-4PH steel in this paper. Characteristic changes of the roughness, hardness and residual stress distribution in three typical areas were discussed in order to gain a better understanding about the shot peening influence on laser hardened material state. Results showed that initial residual stresses had no influence on the finial residual stress distribution in shot peening influence region after shot peening treatment. The fatigue life of laser hardened 17-4PH steel increased dramatically after shot peening treatment.

[1] K. Lo,et al. Improvement of cavitation erosion resistance of AISI 316 stainless steel by laser surface alloying using fine WC powder , 2003 .

[2] Raouf Fathallah,et al. Fatigue strength improvement of 5083 H11 Al-alloy T-welded joints by shot peening: experimental characterization and predictive approach , 2005 .

[3] Jun Wang,et al. The microstructure evolution of type 17-4PH stainless steel during long-term aging at 350 °C , 2006 .

[4] Sheng-Hui Wang,et al. Compressive residual stress introduced by shot peening , 1998 .

[5] F. Appel,et al. Effect of shot peening on fatigue performance of a lamellar titanium aluminide alloy , 2006 .

[6] Y. Al-Obaid. The effect of shot peening on stress corrosion cracking behaviour of 2205-duplex stainless steel , 1995 .

[7] Michael F. Ashby,et al. The transformation hardening of steel surfaces by laser beams—I. Hypo-eutectoid steels , 1984 .

[8] M. Ashby,et al. Laser transformation hardening of steel—II. Hypereutectoid steels , 1986 .

[9] S. Kou,et al. A Fundamental Study of Laser Transformation Hardening , 1983 .

[10] Tatjana Miokovic,et al. Analyse des Umwandlungsverhaltens bei ein- und mehrfacher Kurzzeithärtung bzw. Laserstrahlhärtung des Stahls 42CrMo4 , 2005 .

[11] Andrea Carpinteri,et al. Fatigue growth of a surface crack in a welded T-joint , 2005 .