THE EFFECTS OF NATURAL WEATHERING ON THE PROPERTIES OF HEAT-TREATED ALDER WOOD

The objective of this study was to investigate the effect of natural weathering in ground contact on biological resistance, modulus of rupture, and color stability of heat-treated alder wood. Chemical composition of weathered wood was also studied by FTIR-ATR spectra. Wood stakes were heated at 150, 180, and 200°C for periods of 2, 6, and 10 hours, and the stakes were subsequently exposed to natural weathering and decay in a field area located in the north of Turkey for 3 years. The decay index of heat-treated stakes was lower than that of the controls. The weight loss prevention ratio had an increasing tendency with increasing treatment temperature and length of time. Depending on the treatment parameters, heat treatment reduced the modulus of rupture by up to 50%; however decay caused by soil micro-organisms gave rise to a greater loss of modulus of rupture than heat. Weathering processes caused remarkable color changes in the samples. FTIR-ATR spectra showed significant deformations and degradations in wood components, especially in the hemicelluloses of heat-treated samples. Degradation of hemicelluloses increased with an increase in heat temperature and exposure time.

[1]  R. Alén,et al.  Thermochemical behavior of Norway spruce (Picea abies) at 180–225 °C , 2002, Wood Science and Technology.

[2]  M. Nuopponen.  FT-IR and UV Raman spectroscopic studies on thermal modification of Scots pine wood and its extractable compounds , 2005 .

[3]  G. Janin,et al.  La Mesure de Couleur: Une Méthode d’Etude et d’Optimisation des Transformations Chimiques du Bois Thermolysé , 1991 .

[4]  F. Ximenes,et al.  Protection of wood using oxy-aluminum compounds , 2006 .

[5]  A. Pizzi,et al.  Heat-treated timber: potentially toxic byproducts presence and extent of wood cell wall degradation , 2000, Holz als Roh- und Werkstoff.

[6]  M. Boonstra,et al.  A two-stage thermal modification of wood , 2008 .

[7]  Ali Temiz,et al.  Effect of accelerated weathering on surface chemistry of modified wood , 2007 .

[8]  A. Murata,et al.  Changes in the properties of light-irradiated wood with heat treatment: Part 3. Monitoring by DRIFT spectroscopy , 2004, Holz als Roh- und Werkstoff.

[9]  S. Poncsák,et al.  EFFECT OF THERMAL TREATMENT ON THE CHEMICAL COMPOSITION AND MECHANICAL PROPERTIES OF BIRCH AND ASPEN , 2008 .

[10]  Philip H. Mitchell,et al.  Irreversible property changes of small loblolly pine specimens heated in air, nitrogen, or oxygen , 1988 .

[11]  Hanne Wikberg,et al.  Advanced solid state NMR spectroscopic techniques in the study of thermally modified wood , 2005 .

[12]  S. Hiziroglu,et al.  Surface characteristics of spruce veneers and shear strength of plywood as a function of log temperature in peeling process , 2006 .

[13]  L. Matuana,et al.  Accelerated ultraviolet weathering of PVC/wood‐flour composites , 2002 .

[14]  F. Opoku.  An investigation into the suitability of selected lesser utilised Ghanaian hardwoods for use as outdoor furniture and decking , 2007 .

[15]  Helena Pereira,et al.  PINE WOOD MODIFICATION BY HEAT TREATMENT IN AIR , 2008 .

[16]  William C. Feist,et al.  Outdoor wood weathering and protection. , 1990 .

[17]  T. Okano,et al.  Bending strength and toughness of heat-treated wood , 2000, Journal of Wood Science.

[18]  Jasna S. Stevanic,et al.  Analysis of thermally treated wood samples using dynamic FT-IR-spectroscopy , 2008 .

[19]  A. Rapp,et al.  Durability of thermally modified timber from industrial-scale processes in different use classes: Results from laboratory and field tests , 2007 .

[20]  T. Vuorinen,et al.  Heat‐treated softwood exposed to weathering , 2004 .

[21]  B. Sundqvist.  Color response of Scots pine (Pinus sylvestris), Norway spruce (Picea abies) and birch (Betula pubescens) subjected to heat treatment in capillary phase , 2002, Holz als Roh- und Werkstoff.

[22]  Sibel Yildiz,et al.  The effects of thermal modification on crystalline structure of cellulose in soft and hardwood , 2007 .