A new catalyst system for the polymerization of epoxides

Various epoxides such as ethylene oxide, propylene oxide, epichlorohydrin, isobutylene oxide, 2-chloromethyl propylene oxide, styrene oxide, and phenylglycidyl ether, can be polymerized to high molecular weight, crystalline polymers with catalyst systems of AlEt3/transition-metal chelate compound. Poly(propylene oxide) having an intrinsic viscosity up to 11 was obtained by AlEt3/bis(dimethylglyoximo)nickel(II). Crystalline poly(epichlorohydrin), poly(styrene oxide), poly(phenylglycidyl ether) with high molecular weights were formed. The last polymer is insoluble in common solvents at room temperature and can be converted to a strong fiber and a tough film. In addition, the polymerization mechanism by a coordinate propagation process is discussed. Verschiedene Epoxyde, wie Athylenoxyd, Propylenoxyd, Epichlorhydrin, Isobutylenoxyd, 2-Chlormethylpropylenoxyd, Styroloxyd und Phenylglycidylather konnen mit katalytischen Systemen aus AlEt3 und Chelaten von Ubergangsmetallen zu kristallinen Produkten mit hohem Molekulargewicht polymerisiert werden. Polypropylenoxyd mit [η]-Werten bis zu 11 wurde mit AlEt3/bis(Dimethylglyoximo)-nicke(II) erhalten. Kristallines Polyepichlorhydrin, Polystyroloxyd und Polyphenylglycidylather mit hohen Molekulargewichten wurden gebildet. Das letzte Polymere ist bei Zimmertemperatur in den ublichen Losungsmitteln unloslich und kann zu einer starken Faser oder zu einem zahen Film geformt werden. Weiterhin wird der Mechanismus der Polymerisation als koordinativer Wachstumsvorgang diskutiert.