The study of nanoscratch and nanomachining on hard multilayer thin films using atomic force microscope.

In this study, nanoscratching and nanomachining were conducted using an atomic force microscope (AFM) equipped with a doped diamond-coated probe (DDESP-10; VEECO) to evaluate the fabrication of nanopatterns on hard, Cr₂N/Cu multilayer thin films. The influence of normal force, scratch speed, and repeated scratches on the properties of hard multilayer thin films was also investigated. The nanoscratch experiments led researchers to establish a probe preparation and selection criteria (PPS criteria) to enhance the stability and accuracy of machining hard materials. Experimental results indicate that the depth of grooves produced by nanoscratching increased with an increase in normal force, while an increase in the number of scratches in a single location increased the groove depth but decreased friction. Therelationships among normal force and groove depth more closely resembled a logarithmic form than other mathematical models, as did the relationship between repeated scratching and its effect on groove depth and friction. The influence of scratch speed on friction was divided into two ranges. Between 0.1 and 2 µm/s, friction decreased logarithmically with an increase in scratch speed; however, when the speed exceeded 2 µm/s, the friction appeared stable. In this study, multilayered coatings were successfully machined, demonstrating considerable promise for the fabrication of nanopatterns in multilayered coatings at the nanoscale.

[1]  M. Konagai,et al.  Improvement in Aspect Ratio of P-GaAs Oxide Fabricated by Atomic Force Microscope (AFM)-Based Nanolithography Using Pulsed Voltage , 2001 .

[2]  Li-Chun Chang,et al.  Characteristics of Cr2N/Cu multilayered thin films with different bilayer thickness , 2009 .

[3]  D. Sarid.  Scanning Force Microscopy: With Applications To Electric, Magnetic, And Atomic Forces , 1991 .

[4]  E. Martínez,et al.  Wear behavior of nanometric CrN/Cr multilayers , 2003 .

[5]  Andrea Notargiacomo,et al.  Nanofabrication by scanning probe microscope lithography: A review , 2005 .

[6]  Jen-Ching Huang,et al.  The influence of the bias type, doping condition and pattern geometry on AFM tip‐induced local oxidation , 2010 .

[7]  Song Xu,et al.  Nanofabrication of self-assembled monolayers using scanning probe lithography. , 2000, Accounts of chemical research.

[8]  U. Kunze,et al.  PLOWING ON THE SUB-50 NM SCALE : NANOLITHOGRAPHY USING SCANNING FORCE MICROSCOPY , 1999 .

[9]  Scratching properties of nickel-iron thin film and silicon using atomic force microscopy , 2009 .

[10]  Chunli Bai,et al.  Investigation of Nanoscale Frictional Contact by Friction Force Microscopy , 2001 .

[11]  Sen-Yue Yang,et al.  Fabricating Nanostructures by Atomic Force Microscopy , 2009 .

[12]  Bharat Bhushan,et al.  Nano- to microscale wear and mechanical characterization using scanning probe microscopy , 2001 .

[13]  Jyh-Wei Lee,et al.  Nano-scratching and nano-machining in different environments on Cr2N/Cu multilayer thin films , 2011 .

[14]  J. Celis,et al.  Comparative study between macrotribology and nanotribology , 1998 .

[15]  J. Shirakashi,et al.  Scratch properties of nickel thin films using atomic force microscopy , 2010 .

[16]  N. Amer,et al.  Simultaneous measurement of lateral and normal forces with an optical‐beam‐deflection atomic force microscope , 1990 .

[17]  P. Schmuki,et al.  AFM SCRATCHING AND METAL DEPOSITION THROUGH INSULATING LAYERS ON SILICON , 2005 .