Deposition of superconducting Y‐Ba‐Cu‐O films at 400 °C without post‐annealing

Superconducting thin films of Y1Ba2Cu3O7−x were fabricated using the process of plasma‐assisted laser deposition. The substrate temperature was as low as 400 °C and high‐temperature post‐annealing in an O2 atmosphere was not necessary. The as‐deposited films have a Tc of ∼85 K, and are oriented mostly with the c axis perpendicular to the substrate surface. The measured Jc at 80 K was 105 A/cm2.

[1] T. Lu,et al. Nonconformal Al via filling and planarization by partially ionized beam deposition for multilevel interconnection , 1987, IEEE Electron Device Letters.

[2] H. C. Li,et al. In situ preparation of Y‐Ba‐Cu‐O superconducting thin films by magnetron sputtering , 1988 .

[3] D. K. Lathrop,et al. Production of YBa2Cu3O7−y superconducting thin films in situ by high‐pressure reactive evaporation and rapid thermal annealing , 1987 .

[4] T. Venkatesan,et al. Preparation of Y‐Ba‐Cu oxide superconductor thin films using pulsed laser evaporation from high Tc bulk material , 1987 .

[5] Hoi Sing Kwok,et al. Growth of highly oriented CdS thin films by laser-evaporation deposition , 1988 .

[6] O. W. Holland,et al. Formation of thin superconducting films by the laser processing method , 1987 .

[7] H. Kwok,et al. Spin‐forbidden radiative decay of the a 4Πu state of O+2 , 1987 .

[8] M. Beasley,et al. Critical current densities and transport in superconducting YBa2Cu3O7−δ films made by electron beam coevaporation , 1987 .

[9] G. G. Peterson,et al. Superconducting thin films of Y‐Ba‐Cu‐O produced by neodymium:yttrium aluminum garnet laser ablation , 1988 .

[10] M. Scheuermann,et al. Magnetron sputtering and laser patterning of high transition temperature Cu oxide films , 1987 .